ExxonMobil Optema® TC-110 Cast Ethylene Methyl Acrylate

Category Polymer , Thermoplastic , Ethylene Methyl Acrylate , Ethylene-Methyl Acrylate Copolymer, Compounding Grade
Manufacturer Exxon Chemical
Trade Name Optema®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Optema® TC-110 Cast Ethylene Methyl Acrylate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: Optema TC 110 is an ethylene methyl acrylate copolymer specifically formulated to offer extrusion and property performance for blown and cast film applications. It can produce film under 1.0 mil thickness.Availability: Latin America, North America and South America Additive: Antiblock: NoSlip: No Thermal Stabilizer: YesApplications: Disposable GlovesHospital DrapesUpholstery FilmData provided by the manufacturer, Exxon Chemical.
Physical Properties Metric English Comments
Density 0.942 g/cc
0.0340 lb/in³
Exxon Method
Methyl Acrylate Content 21.5 %
21.5 %
Exxon Method
Melt Flow 2.00 g/10 min

@Load 2.16 kg,
Temperature 190 °C
2.00 g/10 min

@Load 4.76 lb,
Temperature 374 °F
Exxon Method
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 360 %
360 %
ASTM D882
Film Elongation at Break, TD 810 %
810 %
ASTM D882
Elmendorf Tear Strength MD 20 g
20 g
ASTM D1922
Elmendorf Tear Strength TD 360 g
360 g
ASTM D1922
Dart Drop Test 220 g
0.485 lb
ASTM D1709A
Film Tensile Strength at Break, MD 23.4 MPa
3400 psi
ASTM D882
Film Tensile Strength at Break, TD 17.2 MPa
2500 psi
ASTM D882
1% Secant Modulus, MD 51.0 MPa
7400 psi
ASTM D882
1% Secant Modulus, TD 44.1 MPa
6400 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 80.0 °C
176 °F
Exxon Method
Vicat Softening Point 52.8 °C
127 °F
Peak Melting Temperature; ASTM D1525
Optical Properties Metric English Comments
Haze 18 %
18 %
ASTM D1003
Gloss 34 %
34 %
45°; ASTM D2457