Formosa Plastics Formolene® FORMAX® L71709E2 Film (Hexene Grade) LLDPE  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE)/Hexene, Film Grade
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Formosa Plastics Formolene® FORMAX® L71709E2 Film (Hexene Grade) LLDPE  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
High Strength Linear Low Density Polyethylene for Film Extrusion Formolene FORMAX® L7 is a high strength linear low density hexene copolymer polyethylene made using a gas-phase process. Film mechanical properties are significantly improved compared to competitive super hexene LLDPE film resins. FormoleneFORMAX® L7 is formulated with slip and antiblock for use in high performance film applications offering excellent extrusion processing and outstanding impact strength and tear resistance. Films exhibit good optical properties Formolene FORMAX® L7 meets all requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520, covering safe use of polyolefin articles intended for direct food contact.Applications: Industrial packaging, Industrial liners, Coextrusion, Can liners and Consumer trash bagsInformation provided by Formosa Plastics Corporation, USA
Physical Properties Metric English Comments
Density 0.917 g/cc
0.0331 lb/in³
ASTM D1505
Thickness 25.0 microns
0.984 mil
Melt Flow 0.90 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.90 g/10 min

@Load 4.76 lb,
Temperature 374 °F
Condition E; ASTM D1238
Antiblock Level 7000 ppm
7000 ppm
Slip Level 1500 ppm
1500 ppm
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 11.41 MPa
1655 psi
ASTM D882
Film Tensile Strength at Yield, TD 11.27 MPa
1635 psi
ASTM D882
Film Elongation at Break, MD 700 %
700 %
ASTM D882
Film Elongation at Break, TD 870 %
870 %
ASTM D882
Elmendorf Tear Strength MD 375 g
375 g
ASTM D1922
Elmendorf Tear Strength TD 705 g
705 g
ASTM D1922
Dart Drop Test 405 g
0.893 lb
ASTM D1709
Film Tensile Strength at Break, MD 39.2 MPa
5680 psi
ASTM D882
Film Tensile Strength at Break, TD 29.6 MPa
4290 psi
ASTM D882
Processing Properties Metric English Comments
Blow-up Ratio (BUR) 2.5