Formosa Plastics Formolene® HB5202A Blow Molding HDPE

Category Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Blow Molding Grade
Manufacturer Formosa Plastics Corporation, USA
Trade Name Formolene®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Formosa Plastics Formolene® HB5202A Blow Molding HDPE.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
High Density Polyethylene Hexene Copolymer for Blow Molding – With Antistat Formolene® HB5202A is designed for applications requiring excellent stiffness and stress crack resistance propertiesApplications: Containers - Bleach and Detergents and ChemicalsPhysical properties reported herein were determined on compression molded specimens prepared in accordance with Procedure C of ASTM D1928.Information provided by Formosa Plastics Corporation, USA
Physical Properties Metric English Comments
Density 0.952 g/cc
0.0344 lb/in³
ASTM D1505
Environmental Stress Crack Resistance 50 hour
50 hour
Condition B, F<sub>50</sub>; ASTM D1693
ESCR 100% Igepal® 50 hour
50 hour
Condition A, F<sub>50</sub>; ASTM D1693
Melt Flow 0.35 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.35 g/10 min

@Load 4.76 lb,
Temperature 374 °F
Condition E; ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 26.9 MPa
3900 psi
2" (50mm) per min, Type IV; ASTM D638
Elongation at Break >= 600 %
>= 600 %
2" (50mm) per min, Type IV; ASTM D638
Flexural Modulus 1.31 GPa
190 ksi
ASTM D790
Thermal Properties Metric English Comments
Brittleness Temperature <= -118 °C
<= -180 °F
ASTM D746