Honeywell ACLAR® 33C (2.00 mil) Copolymer Film  (discontinued **)

Category Polymer , Film , Thermoplastic , Fluoropolymer
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Honeywell ACLAR® 33C (2.00 mil) Copolymer Film  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: ACLAR® 33C is a copolymer film consisting primarily of chlorotrifluoroethylene (CTFE). 33C is used for military and industrial packaging applications.Information provided by Honeywell.
Physical Properties Metric English Comments
Specific Gravity 2.12 g/cc
2.12 g/cc
ASTM D1505
Density 2.10 g/cc
0.0760 lb/in³
Yield Density
Water Vapor Transmission 0.140 g/m²/day
0.00902 g/100 in²/day
100°F (37.8°C) / 100%RH; ASTM F1249
Thickness 50.8 microns
2.00 mil
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 125 - 200 %
125 - 200 %
ASTM D882
Film Elongation at Break, TD 100 - 200 %
100 - 200 %
ASTM D882
Secant Modulus, MD 1.379 - 1.551 GPa
200.0 - 225.0 ksi
ASTM D882
Secant Modulus, TD 1.31 - 1.517 GPa
190 - 220.0 ksi
ASTM D882
Tear Strength Test 375 - 475
375 - 475
graves tear TD, grams/mil; ASTM D1004
400 - 500
400 - 500
graves tear MD, grams/mil; ASTM D1004
Film Tensile Strength at Break, MD 47.6 - 66.9 MPa
6900 - 9700 psi
ASTM D882
Film Tensile Strength at Break, TD 26.9 - 39.3 MPa
3900 - 5700 psi
ASTM D882
Thermal Properties Metric English Comments
Thermal Conductivity 0.197 W/m-K
1.36 BTU-in/hr-ft²-°F
Melting Point 206 °C
403 °F
crystalline melting point; ASTM D4591
Oxygen Index 100 %
100 %
ASTM D2863
Shrinkage, MD <= 2.5 %
<= 2.5 %
300°F / 149°C - 10 min.; ASTM D1204
Shrinkage, TD <= 2.5 %
<= 2.5 %
300°F / 149°C - 10 min.; ASTM D1204
Optical Properties Metric English Comments
Haze <= 1.0 %
<= 1.0 %
ASTM D1003
Descriptive Properties Value Comments
Flammability non flammable