Huntsman Rexell® L3102 Blown Film Extrusion LLDPE  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Huntsman Rexell® L3102 Blown Film Extrusion LLDPE  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Linear-low density copolymer, cast film extrusion, FDA compliant.Features: Good impact and puncture resistance with excellent optics and sealability.Applications: Laminated and coextruded films for sealability in food packaging.FDA Notes: Conforms to FDA regulation 21 CFR 177.1520 (c)3.2.aFilm properties based on 1.0 guage (25 µm) thickness; blow-up ratio 2:1.Information provided by Huntsman Corporation
Physical Properties Metric English Comments
Density 0.919 g/cc
0.0332 lb/in³
ASTM D1505
Thickness 25.4 microns
1.00 mil
Melt Flow 2.2 g/10 min
2.2 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 380 %
380 %
ASTM D882
Film Elongation at Break, TD >= 700 %
>= 700 %
ASTM D882
Secant Modulus, MD 0.124 GPa
18.0 ksi
ASTM D882
Secant Modulus, TD 0.145 GPa
21.0 ksi
ASTM D882
Elmendorf Tear Strength MD 480 g
480 g
ASTM D1922
Elmendorf Tear Strength TD 740 g
740 g
ASTM D1922
Elmendorf Tear Strength, MD 18.9 g/micron
480 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 29.1 g/micron
740 g/mil
ASTM D1922
Dart Drop 4.88 g/micron
124 g/mil
ASTM D1709
Dart Drop Test 124 g
0.273 lb
ASTM D1709
Film Tensile Strength at Break, MD 42.0 MPa
6090 psi
ASTM D882
Film Tensile Strength at Break, TD >= 18.0 MPa
>= 2610 psi
ASTM D882
Optical Properties Metric English Comments
Haze 0.70 %
0.70 %
ASTM D1003
Gloss 95 %
95 %
at 45°; ASTM D523
Processing Properties Metric English Comments
Melt Temperature 260 - 290 °C
500 - 554 °F