Polymer Property : Melt Flow = 2.2 g/10 min Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Melt Flow	2.2 g/10 min	2.2 g/10 min	(Condition L) ASTM D-1238
Multibase Multi-Flex® TPE A 7606 BLK The burn rate is 1.2 in/min (30 mm/min) based on ASTM FM VSS 302. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase.
Melt Flow	2.2 g/10 min	2.2 g/10 min	(Condition L) ASTM D-1238-94a
Multibase Multi-Pro® 0001 Black Polypropylene This product was specially designed for one customer's extrusion application needs. Data is taken from sample material only.Data provided by Multibase.
Melt Flow	2.2 g/10 min @Load 2.16 kg, Temperature 190 °C	2.2 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133
Polimeri Europa Riblene® FL 20 Low Density Polyethylene - Blown Film Extrusion Riblene FL 20 is a low density polyethylene (LDPE) suitable for blown film extrusion. Riblene FL 20 is characterized by a good balance between processability and mechanical properties.Films manufac..
Melt Flow	2.2 g/10 min @Load 2.16 kg, Temperature 250 °C	2.2 g/10 min @Load 4.76 lb, Temperature 482 °F	cm³/10 min
Polimeri Europa KOBLEND HI PD 14 PBT+PC, Impact Grade (discontinued **) Symbol according to ISO 1043/1: PBT+PC-HI Elastomer modified PBT+PC blend, similar to KOBLEND HI 18 with higher shrinkage values. Main application fields: bumpersUnfilled. Suitable for Injection ..
Melt Flow	2.2 g/10 min @Load 2.16 kg, Temperature 250 °C	2.2 g/10 min @Load 4.76 lb, Temperature 482 °F	cm³/10 min
Polimeri Europa KOBLEND HI PD 19 PBT+PC, Impact Grade (discontinued **) Symbol according to ISO 1043/1: PBT+PC-HI Elastomer modified PBT+PC blend with a very good impact behaviour, good stiffness and higher thermal properties than KOBLEND HI 18. Main application field..
Melt Flow	2.2 g/10 min	2.2 g/10 min	Condition E; ASTM D 1238
Chevron Phillips 4610 LDPE High Clarity, Bakery Packaging Film Resin (discontinued **) Resin Type: HomopolymerCharacteristics: Excellent Clarity, Very High Gloss, Medium Slip, No Antiblock, Good Stability at High Drawdown Speeds, Good Printability, Good Heat Seal CharacteristicsApplic..
Melt Flow	2.2 g/10 min @Load 2.16 kg, Temperature 190 °C	2.2 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
NOVA Chemicals Novapol® LF-0225-B LDPE Clarity Film Resin (discontinued **) Features: High optical clarityExcellent processability Applications: Produce and bakery filmLinersTextile packaging filmGeneral packaging requiring high clarity filmInformation provided by Nova Chem..
Melt Flow	2.2 g/10 min	2.2 g/10 min	Exxon Method
ExxonMobil Escorene® LD-129 MDPE Cast Overwrap Film Resin (discontinued **) Data provided by the manufacturer, Exxon Chemical.A homopolymer film resin with good clarity and excellent stiffness. Film made from LD-129 can be used in overwrap applications and in push-through ..
Melt Flow	2.2 g/10 min	2.2 g/10 min	ASTM D1238
LyondellBasell PetrotheneÂ® NA951080 Low Density Polyethylene ApplicationsPETROTHENE NA 951-080 is designed for use as a base resin for compounding material including gas-injected or chemically expanded insulation. NA 951-080 is a natural, low density, medium..
Melt Flow	2.2 g/10 min @Load 2.16 kg, Temperature 190 Â°C	2.2 g/10 min @Load 4.76 lb, Temperature 374 Â°F
Silon Tabond 3021 Adhesive Resin TABOND 3021 is LLDPE based adhesive resin for co-extruded three layer barrier and composite pipe applications.Characteristics: â€¢ Strong adhesion to aminosilane treated glass, Nylon, EVOH, PET, ..
Melt Flow	2.2 g/10 min @Load 5.00 kg, Temperature 200 Â°C	2.2 g/10 min @Load 11.0 lb, Temperature 392 Â°F	ASTM D1238
Samsung Cheil Industries StarexÂ® SD-0150W ABS, Unreinforced WNP GradeInformation provided by Samsung Cheil Industries.
Melt Flow	2.2 g/10 min @Load 5.00 kg, Temperature 200 Â°C	2.2 g/10 min @Load 11.0 lb, Temperature 392 Â°F	ASTM D1238
Samsung Cheil Industries StarexÂ® SD-0150W ABS, Unreinforced WNP GradeInformation provided by Samsung Cheil Industries.
Melt Flow	2.2 g/10 min @Load 5.00 kg, Temperature 200 Â°C	2.2 g/10 min @Load 11.0 lb, Temperature 392 Â°F	ASTM D1238
Supreme Petrochem SH 2114 High Impact Polystyrene Characteristics Very high impact strength Easy processing High heat Processing Extrusion MoldingApplications Toys, shoe heels, cosmetic boxes, pill vials Luggage cases Blending with clear polys..
Melt Flow	2.2 g/10 min @Load 2.16 kg, Temperature 230 °C	2.2 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133
Borealis HB601WG Polypropylene Homopolymer HB601WG is a polypropylene homopolymer intended for injection molding and blow molding. The product is available in natural but other colors can be provided on request. This material has excellent ..
Melt Flow	2.2 g/10 min @Load 2.16 kg, Temperature 190 °C	2.2 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
Borealis LR4201L Polyethylene Insulation Compound, Crosslinkable LR4201L is a natural low-density crosslinkable polyethylene compound. Application: LR4201L is designed as insulation compound for low voltage power cables. Specifications: IEC 60502 ANSI/ICEA S-66..
Melt Flow	2.2 g/10 min @Load 2.16 kg, Temperature 190 °C	2.2 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
Westlake EF606 Low Density Polyethylene Westlake EF606 is a LDPE resin suggested for use in multiwall and general purpose liners, and for use as a blend resin in general purpose packaging applications. It has excellent processability, and..
Melt Flow	2.2 g/10 min @Load 2.16 kg, Temperature 190 °C	2.2 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
Chevron Phillips MarFlex® 5430 Low Density Polyethylene, Cast Film This LDPE is tailored for cast film applications that require:Excellent opticsEasy processingHigh coefficient of frictionTypical cast film applications include:OverwrapCoextruded filmGeneral purpose..
Melt Flow	2.2 g/10 min	2.2 g/10 min	ASTM D1238
ExxonMobil Exact™ 4151 Ethylene-based Plastomer Resin Product Description: Exact 4151 is an ethylene-based hexane plastomer produced using ExxonMobil Chemical’s EXXPOL® Catalyst Technology. Exact 4151 is designed for both monolayer and multilayer coe..
Melt Flow	2.2 g/10 min	2.2 g/10 min	ExxonMobil Method
ExxonMobil EXACT™ 4151 Plastomer for Cast Film Product Description: Exact 4151 is an ethylene-based hexane plastomer produced using ExxonMobil Chemical’s EXXPOL® Catalyst Technology. Exact 4151 is designed for both monolayer multilayer coextru..
Melt Flow	2.2 g/10 min @Load 2.16 kg, Temperature 190 °C	2.2 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133
DuPont Performance Polymers Delrin® 100TL NC010 Acetal (POM) (Unverified Data**) Teflon® Lubricated High Viscosity Acetal Homopolymer with Low Wear and Low FrictionDelrin 100TL NC010 (formerly Delrin 100TL NC000) is a high viscosity acetal homopolymer with 1.5% TeflonInformatio..
Melt Flow	2.2 g/10 min @Load 2.16 kg, Temperature 190 °C	2.2 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238, ISO 1133
DuPont™ Bynel® 41E766 Anhydride Modified LLDPE BYNEL® Series 4100 series resins are anhydride-modified, linear low-density polyethylene (LLDPE) resins. All BYNEL Series 4100 series resins are available in pellet form for use in conventional ext..
Melt Flow	2.2 g/10 min @Load 2.16 kg, Temperature 235 °C	2.2 g/10 min @Load 4.76 lb, Temperature 455 °F
Arkema Group Rilsan® BZM 23 G9 Nylon 11, 23% Glass Fiber Filled (Dry) Designation ISO 1874-PA11,MS,18-040,(G+C)(F+D)(25+05)Rigid grade with glass fiber (23%) and graphite filler for injection molding. Available color: steel black gray. Additive free.Rigidity. Low fric..
Melt Flow	2.2 g/10 min @Load 2.16 kg, Temperature 235 °C	2.2 g/10 min @Load 4.76 lb, Temperature 455 °F
Arkema Group Rilsan® AZM 30 GT8LD Nylon 12, 30% Glass Fiber Filled (Dry) Designation ISO 1874-PA12,MHLS,16-050,(G+C)(F+D)(30+05)Rigid grade with glass fiber (30%) and graphite filler for injection molding. Available color: steel black gray. Reinforced light and heat stab..
Melt Flow	2.2 g/10 min @Load 2.16 kg, Temperature 190 °C	2.2 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM-D1238
Braskem TS9002 LDPE Blown Film Extrusion Polyethylene TS9022 is a low-density polyethylene (LDPE) developed specially for automatic overwrap packaging. This resin has a combination of high optical properties and excellent stiffness. The incorporated ad..
Melt Flow	2.2 g/10 min	2.2 g/10 min	ASTM D1238
Aclo Accucomp ABS ABS803L Medium Impact Grade
Melt Flow	2.2 g/10 min @Load 3.80 kg, Temperature 230 °C	2.2 g/10 min @Load 8.38 lb, Temperature 446 °F	ASTM D-1238
Plaskolite Optix® CP - 80 General Purpose Acrylic Resin OPTIX® general purpose acrylics are available in a variety of performance grades that offer varying melt flow rates, heat resistance, color/opacity and gloss levels.Information provided by Plaskoli..
Melt Flow	2.2 g/10 min	2.2 g/10 min	Exxon Method
ExxonMobil Escorene® LD-316 EVA Film Resin, High Clarity, High Impact (discontinued **) Data provided by the manufacturer, Exxon Chemical.A 1.9% vinyl acetate copolymer, high clarity film resin. Film made from LD-316 offers improved impact strength and heat sealability versus homopoly..
Melt Flow	2.2 g/10 min	2.2 g/10 min	ISO 1133
Total Lacqtene® 1025 FH 24 LDPE blown film (discontinued **) Radical polyethylene made by high pressure tubular process. Slip and antiblock formulated grade for good transparent thin films. Advised temperature profile : 150 to 190°C.Information provided prov..