Jackon JACKOCELL® S3312 Expanded Polystyrene Packaging and Shape Molding

Category Polymer , Thermoplastic , Polystyrene (PS) , Expanded Polystyrene (EPS)
Manufacturer Jackon GmbH
Trade Name JACKOCELL®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Jackon JACKOCELL® S3312 Expanded Polystyrene Packaging and Shape Molding.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
100% Polystyrene.Pre-expansionA substantial reduced pentane emission has been made possible with Jackocell® S3312 - which will lead the industry into the future. High stability of pre-expanded beads in pre-expansion, transportation and silo storage reduces opportunity losses through typical lower average density during regular production. This combination of good properties is clearly a result of high technology in combination with extensive product development.Shape MouldingWith S3312, low density and low pentane mouldings have finally been combined. The unique designs of polystyrene chains adds numerous advantages to Jackocell® S3312 in shape moulding. Fast moulding cycles, good fusion, and easy to reach good surface. The additional broad moulding window further reduces waste material and maintains a high quality to the extent that it can be recognized long term on productivity and financial earnings.
Physical Properties Metric English Comments
Density 0.0170 g/cc
0.000614 lb/in³
1.5 minute residence time
0.0180 g/cc
0.000650 lb/in³
1 minute residence time
0.0220 g/cc
0.000795 lb/in³
2.5 minute residence time
0.0300 g/cc
0.00108 lb/in³
0.6 minute residence time
Bead Size 0.600 - 1.00 mm
0.0236 - 0.0394 in
Mechanical Properties Metric English Comments
Flexural Strength 0.335 MPa
48.6 psi
16 hour silo aging time
0.345 MPa
50.0 psi
32 hour silo aging time
0.350 MPa
50.8 psi
48 hour silo aging time
0.350 MPa
50.8 psi
64 hours silo aging time
Compressive Strength 1.25 MPa
181 psi
30 g/l
1.27 MPa
184 psi
50 g/l
1.30 MPa
189 psi
90 g/l
1.32 MPa
191 psi
70 g/l
Chemical Properties Metric English Comments
Blowing Agent Content <= 5.2 %
<= 5.2 %
Pentane
Descriptive Properties Value Comments
Coefficient of Variation (%), max 15
Moulding Cycle Time (sec) 124
6 hour silo aging time, 20 kg/m^3
71
64 hours silo aging time, 20 kg/m^3
78
48 hour silo aging time, 20 kg/m^3
90
32 hour silo aging time, 20 kg/m^3