- Kotec Carbotex K-30CF10 Polycarbonate, Conductive, 10% Carbon Fiber Reinforced
Kotec Carbotex K-30CF10 Polycarbonate, Conductive, 10% Carbon Fiber Reinforced
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Carbon Fiber Reinforced , Polycarbonate, Conductive |
| Manufacturer | Kotec Corp |
| Trade Name | Carbotex |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kotec Carbotex K-30CF10 Polycarbonate, Conductive, 10% Carbon Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: Conductive, 10% Carbon fiber reinforcedApplications: OA equipment, Communications, Precision parts, Machineries, E & E partsInformation provided by Kotec Corporation
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.24 g/cc | 1.24 g/cc | ASTM D792 |
| Water Absorption | 0.20 % @Temperature 23.0 °C, Time 86400 sec |
0.20 % @Temperature 73.4 °F, Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | ASTM D995 |
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | ASTM D995 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 108 MPa | 15700 psi | ASTM D638 |
| Elongation at Break | 118 % | 118 % | ASTM D638 |
| Flexural Strength | 160 MPa | 23200 psi | ASTM D790 |
| Flexural Modulus | 6.00 GPa | 870 ksi | ASTM D790 |
| Izod Impact, Notched | 1.20 J/cm @Temperature 23.0 °C |
2.25 ft-lb/in @Temperature 73.4 °F |
V-Notched 1/8"; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Heat Distortion Temperature | 147 °C | 297 °F | ASTM D648 |
| Flammability, UL94 | V-2 @Thickness 1.60 mm |
V-2 @Thickness 0.0630 in |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 0.00 % @Thickness 3.00 mm |
0.00 % @Thickness 0.118 in |
ASTM D1003 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1e+05 | 1e+05 | ASTM D257 |
| Arc Resistance | 110 sec | 110 sec | ASTM D495 |
Users viewing this material also viewed the following:
- MV Labs RU460 K2RuCl6 Potassium hexachlororuthenate(IV)
- Latrobe BG42® Stainless Knife Steel (AMS 5749)
- SABIC Innovative Plastics LNP STAT-KON DE003ER PC (Asia Pacific)
- Borealis Borclean™ HC318BF Polypropylene Homopolymer for Capacitor Film
- UBE UBESTA® 3030JLX1 Plasticized Automotive Grade Nylon 12
- A. Schulman PP 1255-01 Polypropylene General Purpose Homopolymer Polypropylene
- Topas Advanced Polymers TOPAS® 9506F-500 Cyclic Olefin Copolymer (COC)
- ExxonMobil LDPE LD 331.08 Low Density Polyethylene Resin
- BASF Styropor® F 315-N Expandable Polystyrene
Copyright © lookpolymers.com All Rights Reserved