LNP Stat-Kon® PDX-S-90398 Polyamide 12, Stainless Steel Fiber  (discontinued **)

Category Polymer , Thermoplastic , Nylon , Nylon 12
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LNP Stat-Kon® PDX-S-90398 Polyamide 12, Stainless Steel Fiber  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features: Electrically ConductiveForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase.
Physical Properties Metric English Comments
Specific Gravity 1.10 g/cc
1.10 g/cc
Method A; ASTM D792
Water Absorption 0.20 %
0.20 %
at 24 hrs; ASTM D570
Linear Mold Shrinkage 0.011 cm/cm
0.011 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.017 cm/cm
0.017 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 35.9 MPa
5210 psi
ASTM D638
Tensile Strength, Yield 43.4 MPa
6290 psi
ASTM D638
Elongation at Break 120 %
120 %
ASTM D638
Elongation at Yield 5.3 %
5.3 %
ASTM D638
Tensile Modulus 1.91 GPa
277 ksi
ASTM D638
Flexural Strength 62.1 MPa
9010 psi
ASTM D790
Flexural Modulus 1.78 GPa
258 ksi
ASTM D790
Izod Impact, Notched 0.747 J/cm

@Thickness 3.18 mm
1.40 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Unnotched NB

@Thickness 3.18 mm
NB

@Thickness 0.125 in
ASTM D256
Izod Impact, Notched (ISO) 7.60 kJ/m²
3.62 ft-lb/in²
ISO 180
Izod Impact, Unnotched (ISO) 85.0 kJ/m²
40.4 ft-lb/in²
ISO 180
Falling Dart Impact 9.73 J
7.18 ft-lb
ASTM D3763
Impact Test 20.8 J
15.3 ft-lb
Multi-Axial Instrumented Impact Energy; ISO 6603-2
Thermal Properties Metric English Comments
CTE, linear 100 µm/m-°C

@Temperature 20.0 °C
55.6 µin/in-°F

@Temperature 68.0 °F
TMA; ASTM E831
CTE, linear, Transverse to Flow 99.0 µm/m-°C

@Temperature 20.0 °C
55.0 µin/in-°F

@Temperature 68.0 °F
TMA; ASTM E831
Deflection Temperature at 0.46 MPa (66 psi) 114 °C
237 °F
Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 67.7 °C
154 °F
Unannealed; ASTM D648
Electrical Properties Metric English Comments
Surface Resistance 100 - 1.00e+6 ohm
100 - 1.00e+6 ohm
ASTM D4496
Processing Properties Metric English Comments
Melt Temperature 204 °C
399 °F
Mold Temperature 82.2 - 107 °C
180 - 225 °F
Drying Temperature 82.2 °C
180 °F
Dry Time 4 hour
4 hour
Moisture Content 0.20 %
0.20 %
Suggested
Back Pressure 0.172 - 0.345 MPa
24.9 - 50.0 psi