Lehmann & Voss LUVOCOM® 1105-8432 PEEK, unreinforced
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1105-8432 PEEK, unreinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Electrically conductive, suitable for continuous discharging of statically generated electricity.Chemical and hydrolysis resistance parts, non flammable.Isotropic shrinkage characteristics.High dimensionally stable precision parts, high continuous use temperature.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 2.41 g/cc | 2.41 g/cc | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h |
| Linear Mold Shrinkage | 0.011 - 0.018 cm/cm | 0.011 - 0.018 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 95.0 MPa | 13800 psi | |
| Elongation at Yield | 1.5 % | 1.5 % | |
| 1.9 % | 1.9 % | flexural | |
| Modulus of Elasticity | 9.00 GPa | 1310 ksi | |
| Flexural Strength | 140 MPa | 20300 psi | |
| Flexural Modulus | 7.50 GPa | 1090 ksi | |
| Charpy Impact Unnotched | 2.50 J/cm² | 11.9 ft-lb/in² | flatwise; ISO 179 1fU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 250 °C | 482 °F | |
| 270 °C | 518 °F | short term | |
| Flammability, UL94 | V-0 | V-0 | not recognized by UL |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | >= 1000 ohm | >= 1000 ohm | |
| Insulation Resistance | >= 1000 ohm | >= 1000 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 390 °C | 734 °F | mass temp |
| Nozzle Temperature | 360 - 380 °C | 680 - 716 °F | |
| Zone 1 | 360 - 370 °C | 680 - 698 °F | |
| Zone 2 | 380 - 390 °C | 716 - 734 °F | |
| Zone 3 | 390 - 400 °C | 734 - 752 °F | |
| Mold Temperature | 170 - 200 °C | 338 - 392 °F | |
| Drying Temperature | 120 °C @Time 21600 - 28800 sec |
248 °F @Time 6.00 - 8.00 hour |
or |
| 150 °C @Time 10800 - 21600 sec |
302 °F @Time 3.00 - 6.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color (black) |
Users viewing this material also viewed the following:
- PolyOne Nymax™ GF 600 A 44 Black 13 Polyamide 6 (Nylon 6)
- Lehmann & Voss LUVOCOM® 3/CF/10/BK Polyamide 6, with carbon fiber
- Huntsman HY 955 Polyamide
- Latrobe Lescalloy® D6AC VAC-ARC High Strength Alloy Steel
- Shinkong Synthetic Fibers Shinite® F102G30 PET, 30% Glass Filled, Fire Retardant, Halogen Free
- A. Schulman POLYBLAK™ 3209 Superior Black Color Concentrate, 40% Carbon Black Based In Polypropylene
- Barlog Plastics KEBAFORM C 270 LS black POM Copolymer unreinforced, laser markable
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 60 PHR Carbon Black, N-330 (HAF)
- Polykemi AB POLYfill PPH T5040 FC Polypropylene Homopolymer, Mineral Reinforced
Copyright © lookpolymers.com All Rights Reserved