Polymer Property : Modulus of Elasticity = 1310 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Modulus of Elasticity	9.00 GPa	1310 ksi
Poco Graphite AXZ-5Q Industrial Grade Graphite POCO’s specialty graphite materials are used in a wide range of highly technical and industrial applications. Each grade has characteristics and properties that allow the user to match the ideal gr..
Modulus of Elasticity	9.00 GPa	1310 ksi	ASTM D638
Owens Corning Glass Fiber Reinforced Polyester (PET), 30 wt.% glass Thermoplastic Polyesters are resistant to most organic solvents, weak acids and alkalis. They are not recommended with strong acids and alkalis or for prolonged use in hot water. Data provided by t..
Modulus of Elasticity	9.00 - 11.0 GPa	1310 - 1600 ksi	Injection; ISO 527
Raschig Group 2557 AMC Polyester Glass fiber reinforced polyester molding compound. Very good mechanical strength, very good electrical properties and dimensional stability, exceptional processability with short cycle time and low ..
Modulus of Elasticity	9.00 - 10.0 GPa	1310 - 1450 ksi	Injection; ISO 527
Raschig Group AMPLA® 2000 melamine-modified polyester Halogen-free, organically and inorganically filled melamine-modified Polyester molding compound. Low post-shrinkage, very good electrical values, high heat resistance, very good sliding behavior, ve..
Modulus of Elasticity	9.00 - 11.0 GPa	1310 - 1600 ksi	Compression and Injection; ISO 527
Raschig Group RALUPOL® 4385 UP Glass-fiber reinforced polyester molding compound. Low mold shrinkage and post-shrinkage, very high arc resistance, very high mechanical values. This product meets the allowed upper limits for heavy..
Modulus of Elasticity	9.00 - 11.0 GPa	1310 - 1600 ksi	Injection and Compression; ISO 527
Raschig Group SURAPLAST 54 UPA Glass fiber reinforced polyester molding compound. Minimal mold shrinkage and post-shrinkage, very good arc resistance, very good mechanical strength. This product meets the allowed upper limits for..
Modulus of Elasticity	9.00 - 11.0 GPa	1310 - 1600 ksi	Average value: 10.1 GPa Grade Count:6
Overview of materials for Phenolic, Novolac, Mineral/Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Novolac, Mineral/Fiber Filled". Each property range of values reported is minimum and maximum ..
Modulus of Elasticity	9.00 - 18.6 GPa	1310 - 2700 ksi	Average value: 14.0 GPa Grade Count:26
Overview of materials for Nylon 66, 20% Carbon Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 20% Carbon Fiber Filled". Specific grades with carbon fiber content between 15% and 24% are in..
Modulus of Elasticity	9.00 GPa	1310 ksi
Lehmann & Voss LUVOCOMÂ® 1105-8432 PEEK, unreinforced Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Electrically conductive, suitable for continuous discharging of statically generated elect..
Modulus of Elasticity	9.00 GPa	1310 ksi
Lehmann & Voss LUVOCOMÂ® 1105-8534 PEEK, with mineral filler Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Reduced moment of inertia compared with metal parts.Chemical and hydrolysis resistance par..
Modulus of Elasticity	9.00 GPa	1310 ksi
Lehmann & Voss LUVOCOMÂ® 1-7789/EG Polyamide 66, with carbon fiber, lubricant modified, heat stabilized Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts.Reduced moment of inertia compared with metal parts.Antistatic.High dimensi..
Modulus of Elasticity	9.00 GPa	1310 ksi
Lehmann & Voss LUVOCOMÂ® 1850-7431 PBT, with carbon fiber and glass spheres Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts.Low warpage.Low waterabsorbtion, for dimensional stable precision parts.Par..
Modulus of Elasticity	9.00 GPa	1310 ksi
Lehmann & Voss LUVOCOMÂ® 20-8332 Polyphthalamide, with glass fiber and PTFE Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts.Low influence from moisture and temperature to measures and electrical prop..
Modulus of Elasticity	9.00 GPa	1310 ksi
Lehmann & Voss LUVOCOMÂ® 3-7234-1 Polyamide 6, with carbon fiber, electrically conducting Applications: Automotive industry, textile machinery, apparatus- and precision engineering.Strong, stiff parts.dynamic stressAntistatic.Handles, levers, rollers, body parts.Information provided by L..
Modulus of Elasticity	9.00 GPa	1310 ksi
Lehmann & Voss LUVOCOMÂ® 50/CF/7/GF/20/TF/10/BK Polycarbonate, with carbon fiber, glass fiber and PTFE Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.High-strength and high-stiff parts; low coefficient of expansi..
Modulus of Elasticity	9.00 GPa	1310 ksi
Lehmann & Voss LUVOCOMÂ® 50-7154/V0 Polycarbonate, with carbon fiber, low-warpage Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.Strong, stiff parts.Reduced moment of inertia compared with me..
Modulus of Elasticity	9.00 GPa	1310 ksi	25mm flat samples, compression moulded; ISO 527-4
Menzolit MenzolitÂ® BMC 2310 Unsaturated Polyester UP BMC 2310 is a chemically resistant grade reinforced with special fibres. Being completely glass-free (no glass fibre reinforcement) it is specifically recommended for the manufacture of high voltage..
Modulus of Elasticity	9.00 GPa	1310 ksi	25mm flat samples, compression moulded; ISO 527-4
Menzolit MenzolitÂ® SMC 0430 Unsaturated Polyester UP SMC 0430 is a low emission Class-A SMC for on-line painted exterior body applications on passenger cars. These compounds mould to parts with excellent surface quality for on-line painted body panel..
Modulus of Elasticity	9.00 GPa	1310 ksi
Lehmann & Voss LUVOCOMÂ® 1105-0948/YL2 PEEK, with glass fiber Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Strong, stiff parts; impact resistance.Dynamic stressed parts at high movement velocity.Ch..
Modulus of Elasticity	9.00 GPa	1310 ksi	ISO 527-2
Tisan TISLAMID® 6 30% Glass Fiber Reinforced Nylon 6 TISLAMID has a wide area of application in electric/electronic, automotive, durable goods and telecommunications industries. It demonstrates characteristics such as Excellent chemical resistanceElec..
Modulus of Elasticity	9.00 GPa	1310 ksi	ISO 527-2
Tisan TISLAMID® 66 30% Glass Fiber Reinforced Nylon 66 TISLAMID has a wide area of application in electric/electronic, automotive, durable goods and telecommunications industries. It demonstrates characteristics such as Excellent chemical resistanceElec..
Modulus of Elasticity	9.00 GPa @Thickness >=1.50 mm	1310 ksi @Thickness >=0.0591 in	24hr/23°C/50% RH; ISO 178; IEC/EN 60893-2 5.2
Elektro-Isola G-Etronax PM GPO 3 Polyester, Glass Mat, Red, Sheets Description: Good electrical properties such as high breakdown voltage in air and oil and highest arc resistance and tracking resistance. Self-extinguishing. Low smoke emission, halogen-free.Applica..
Modulus of Elasticity	9.00 GPa	1310 ksi	ISO 527
BASF Ultramid® KR 4355 G5 25% Glass Filled PA6/6T (Conditioned) Description: 25% glass-fiber reinforced product for injection-molding; high toughness, strength and stiffness, low water absorption, high melting point (295°C [563°F]). The mechanical properties r..
Modulus of Elasticity	9.00 GPa	1310 ksi	ISO 527-1/-2
BASF Ultramid® KR 4355 G5 25% Glass Filled PA6/6T (Dry) Description: 25% glass-fiber reinforced product for injection-molding; high toughness, strength and stiffness, low water absorption, high melting point (295°C [563°F]). The mechanical properties r..
Modulus of Elasticity	9.00 GPa	1310 ksi	ISO 527-1/-2
BASF Ultramid® KR 4355 G5 BK 00564 25% Glass Filled PA6/6T (Dry) Description: 25% glass-fiber reinforced product for injection-molding; high toughness, strength and stiffness, low water absorption, high melting point (295°C [563°F]). The mechanical properties r..
Modulus of Elasticity	9.00 GPa @Temperature 80.0 °C	1310 ksi @Temperature 176 °F	ISO 527
BASF Ultramid® KR 4355 G7 35% Glass Filled PA6/6T (Dry) Description: 35% glass-fiber reinforced product for injection-molding; high toughness, strength and stiffness, low water absorption, high melting point (295°C [563°F]). The mechanical properties r..
Modulus of Elasticity	9.00 GPa	1310 ksi	ISO 527-1/-2
BASF Ultramid® KR 4357 G6 BK 00564 30% Glass Filled PA6/6T (Conditioned) Description: 30% glass-fiber reinforced, impact-modified product for injection-molding; high toughness, strength and stiffness, low water absorption, high melting point (295°C [563°F]). The mechan..
Modulus of Elasticity	9.00 - 11.0 GPa	1310 - 1600 ksi	Injection; ISO 527
Raschig Group 5567 DAP Diallyl Phthalate (DAP), Cast, Mineral Filler Glass-fiber reinforced diallyl phthalate molding compound free from halogens. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exc..