Mapal Plastics Maplon PAPER MATCH Polypropylene Sheet

Category Polymer , Film , Thermoplastic , Polypropylene (PP) , Polypropylene, Sheet/Thermoforming Grade
Manufacturer Mapal Plastics
Trade Name Maplon
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Mapal Plastics Maplon PAPER MATCH Polypropylene Sheet.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Paper match is a multi layer graphic sheet. The core layer is a high rigidity PP. The skin layers are high field polyolefine. The surface bonds easily to inks and have some absorbing capacity.Main advantages are: High durability, Water and chemical resistance, High heat resistance, Unlimited flex life of integral hinge, Easy processing with conventional paper converting equipment.
Physical Properties Metric English Comments
Specific Gravity 1.04 g/cc
1.04 g/cc
Thickness 400 microns
15.7 mil
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 28.0 MPa

@Temperature 23.0 °C
4060 psi

@Temperature 73.4 °F
ASTM D638
Film Tensile Strength at Yield, TD 26.0 MPa

@Temperature 23.0 °C
3770 psi

@Temperature 73.4 °F
ASTM D638
Film Elongation at Break, MD >= 100 %

@Temperature 23.0 °C
>= 100 %

@Temperature 73.4 °F
ASTM D638
Film Elongation at Break, TD >= 100 %

@Temperature 23.0 °C
>= 100 %

@Temperature 73.4 °F
ASTM D638
Film Elongation at Yield, MD 14 %

@Temperature 23.0 °C
14 %

@Temperature 73.4 °F
ASTM D638
Film Elongation at Yield, TD 9.4 %

@Temperature 23.0 °C
9.4 %

@Temperature 73.4 °F
ASTM D638
Modulus of Elasticity 0.800 GPa

@Temperature 23.0 °C
116 ksi

@Temperature 73.4 °F
MD/TD; ASTM D638
Tear Strength <= 230 kN/m
<= 1310 pli
Mapal internal
Thermal Properties Metric English Comments
Vicat Softening Point 145 °C
293 °F
ASTM D1525
Heat Distortion Temperature 110 °C
230 °F
ASTM 648
Descriptive Properties Value Comments
Yield (g/m²) 416