MarkeTech Ceraflex 8Y Thin Zirconia Ceramic Oxygen Ion Conductor, Yttria Stabilized

Category Ceramic , Oxide , Zirconium Oxide
Manufacturer MarkeTech
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF MarkeTech Ceraflex 8Y Thin Zirconia Ceramic Oxygen Ion Conductor, Yttria Stabilized.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data provided by the supplier, MarkeTech International.8 mole% Y2O3 (13.8 wt%). CERAFLEX is a sintered and fully dense zirconia ceramic material that is formed into extremely thin sheets, that are both flexible and highly resilient. The high strength of CERAFLEX makes it easier to handle than other ceramic materials of the same thickness. CERAFLEX is available as strips, sheets, or custom parts. It is either partially or fully stabilized with yttria.The fully stabilized material is an oxygen ion conductor and used to build solid oxide fuel cells and oxygen sensors. A new cesium stabilized material (CERAFLEX:Cs) with much better electrical conductivity is now available.Properties and availability: Flatness 50 µm/in. Surface roughness 0.1 µm. Bending strength 40 kgf. Standard thicknesses 0.100 & 0.200 mm (up to 0.5 mm). Maximum size 200 x 200 mm.
Physical Properties Metric English Comments
Density 5.85 g/cc
0.211 lb/in³
Thermal Properties Metric English Comments
CTE, linear 9.50 µm/m-°C

@Temperature 20.0 °C
5.28 µin/in-°F

@Temperature 68.0 °F
Thermal Conductivity 2.80 W/m-K
19.4 BTU-in/hr-ft²-°F
Electrical Properties Metric English Comments
Electrical Resistivity 5.00 ohm-cm

@Temperature 1000 °C
5.00 ohm-cm

@Temperature 1830 °F
10.0 ohm-cm

@Temperature 900 °C
10.0 ohm-cm

@Temperature 1650 °F
20.0 ohm-cm

@Temperature 800 °C
20.0 ohm-cm

@Temperature 1470 °F
30.0 ohm-cm

@Temperature 700 °C
30.0 ohm-cm

@Temperature 1290 °F
120 ohm-cm

@Temperature 600 °C
120 ohm-cm

@Temperature 1110 °F