Niagara LaSalle e.t.d.® 150® Cold Finished Steel Bar

Category Metal , Ferrous Metal , Alloy Steel , AISI 4000 Series Steel
Manufacturer Niagara LaSalle
Trade Name e.t.d.®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Niagara LaSalle e.t.d.® 150® Cold Finished Steel Bar.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
e.t.d.® 150® is produced from AISI medium carbon 4100 series alloy steel. The heats to be used for e.t.d. 150® are controlled to contain nitrogen in quantities normally associated with steel produced by the electric furnace process. Only one additive, such as tellurium, selenium, or sulfur is also added to improve machinability. Like Fatigue-Proof®, it is another Niagara LaSalle high strength material made by the elevated temperature drawing process. It eliminates heat treating and secondary operations such as straightening, finish grinding, cleaning, and inspections. e.t.d.® 150® can be roll threaded, knurled and plated. Suitable for induction hardening, e.t.d.® 150® is also electromagnetically tested using eddy currents and pretested for machinability through Niagara LaSalle’s unique testing procedure.Information provided by Niagra LaSalle Corporation
Mechanical Properties Metric English Comments
Hardness, Brinell >= 302
>= 302
Hardness, Rockwell C >= 32
>= 32
Tensile Strength 1030 MPa
150000 psi
Tensile Strength, Yield 896 MPa
130000 psi
0.2% offset
Elongation at Break >= 10 %
>= 10 %
mean
Reduction of Area 37 %
37 %
mean
Component Elements Properties Metric English Comments
Carbon, C >= 0.40 %
>= 0.40 %
Chromium, Cr 0.80 - 1.2 %
0.80 - 1.2 %
Iron, Fe 97.1 - 97.8 %
97.1 - 97.8 %
as balance
Manganese, Mn 0.70 - 1.1 %
0.70 - 1.1 %
Molybdenum, Mo 0.15 - 0.25 %
0.15 - 0.25 %
Silicon, Si 0.15 - 0.35 %
0.15 - 0.35 %