Polymer Property : Tensile Strength = 1030 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength	1030 MPa	150000 psi
Niagara LaSalle e.t.d.® 150® Cold Finished Steel Bar e.t.d.® 150® is produced from AISI medium carbon 4100 series alloy steel. The heats to be used for e.t.d. 150® are controlled to contain nitrogen in quantities normally associated with steel prod..
Tensile Strength	1030 MPa @Temperature -5.56 Â°C	150000 psi @Temperature 22.0 Â°F	Hardened and tempered to 34 HRC
Schmolz + Bickenbach P-20 High Hard Plastic Mold Steel Description: P-20 High Hard is an improved pre-hardened mold steel that has been specially designed for large plastic molds; Material is forged on a 5000 ton press assuring maximum deformation durin..
Tensile Strength	1030 MPa @Temperature -5.56 Â°C	150000 psi @Temperature 22.0 Â°F	Hardened and tempered to 34 HRC
Schmolz + Bickenbach P-20 Modified Plastic Mold Steel Description: P-20 Modified is an improved pre-hardened mold steel that has been specially designed for large plastic molds; The material is forged on a 5000 ton press assuring maximum deformation du..
Tensile Strength	1030 - 1170 MPa @Thickness >=25.4 mm	150000 - 170000 psi @Thickness >=1.00 in	Turned Bars
Schmolz + Bickenbach UGIMAÂ® 630 Stainless Steel Bar Description: 630 UGIMAÂ® is an improved machining martensitic precipitation hardenable grade produced only by Ugitech. It is identical in every way to standard type 630 (17-4), except with respect..
Tensile Strength	>= 1030 MPa	>= 150000 psi
Eagle Brass 301 Austenitic Stainless Steel, 1/2 Hardened Type 301 is a chromium-nickel stainless steel that provides high strength and good ductility with chromium and nickel contents lowered to increase the work hardening range. This permits higher tens..
Tensile Strength	>= 1030 MPa	>= 150000 psi
Eagle Brass 302 Austenitic Stainless Steel, 1/2 Hardened Types 302 is a widely used variation of the basic 18-8 grade with variations of nickel, chromium and carbon content. It is weakly magnetic when cold rolled.Information provided by Eagle Brass Compa..
Tensile Strength	>= 1030 MPa	>= 150000 psi
Eagle Brass 304 Austenitic Stainless Steel, 1/2 Hardened Types 304 is a widely used variation of the basic 18-8 grade with variations of nickel, chromium and carbon content. It is weakly magnetic when cold rolled.Information provided by Eagle Brass Compa..
Tensile Strength	>= 1030 MPa	>= 150000 psi
Eagle Brass 305 Austenitic Stainless Steel, 1/2 Hardened Type 305 is a chromium nickel stainless steel that can be spun and deep drawn more easily due to an increased nickel content that decreases work hardening. It is nonmagnetic under most conditions. ..
Tensile Strength	>= 1030 MPa	>= 150000 psi
Eagle Brass 316 Austenitic Stainless Steel, 1/2 Hardened The Mo addition increases general corrosion resistance to pitting from chloride ion solutions, and provides increased strength at elevated temperatures. Properties are similar to those of Type 304 ..
Tensile Strength	>= 1030 MPa	>= 150000 psi
Eagle Brass 316L Austenitic Stainless Steel, 1/2 Hardened Type 316L is an extra-low carbon version of Type 316 that minimizes carbide precipitation. Typical uses include exhaust manifolds, furnace parts, heat exchangers, jet engine parts, pharmaceutical a..
Tensile Strength	>= 1030 MPa	>= 150000 psi
Eagle Brass 304L Austenitic Stainless Steel, 1/2 Hardened Type 304L is a very common variation of the basic 18-8 grade with variations of nickel, chromium and carbon content. It is weakly magnetic when cold rolled. Lower carbon 304L minimizes chromium ca..