PEAK Werkstoff DISPAL S263 Aluminum Alloy, AlSi25Cu3Fe3Ni3MgCoTi, Condition F

Category Metal , Nonferrous Metal , Aluminum Alloy
Manufacturer PEAK Werkstoff
Trade Name DISPAL
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PEAK Werkstoff DISPAL S263 Aluminum Alloy, AlSi25Cu3Fe3Ni3MgCoTi, Condition F.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Excellent properties:abrasive stabilityhigh stiffness (E-modulus)resistance even at high temperaturesgood grindabilityPEAK DISPAL materials allow the manufacturing of pistons for highest operational demands.Information provided by PEAK Werkstoff GmbH
Physical Properties Metric English Comments
Density 2.622 - 2.898 g/cc
0.09473 - 0.1047 lb/in³
Mechanical Properties Metric English Comments
Hardness, Vickers >= 140
>= 140
HV30
Tensile Strength at Break >= 268 MPa

@Temperature 200 °C
 >= 38900 psi

@Temperature 392 °F
>= 362 MPa

@Temperature 20.0 °C
 >= 52500 psi

@Temperature 68.0 °F
Tensile Strength, Yield >= 183 MPa

@Temperature 200 °C
 >= 26500 psi

@Temperature 392 °F
>= 223 MPa

@Temperature 20.0 °C
 >= 32300 psi

@Temperature 68.0 °F
Elongation at Break >= 1.2 %

@Temperature 20.0 °C
 >= 1.2 %

@Temperature 68.0 °F
>= 1.9 %

@Temperature 200 °C
 >= 1.9 %

@Temperature 392 °F
Modulus of Elasticity >= 80.0 GPa

@Temperature 200 °C
 >= 11600 ksi

@Temperature 392 °F
>= 92.0 GPa

@Temperature 20.0 °C
 >= 13300 ksi

@Temperature 68.0 °F
Poissons Ratio 0.286

@Temperature 20.0 °C
 0.286

@Temperature 68.0 °F
0.289

@Temperature 100 °C
 0.289

@Temperature 212 °F
0.29

@Temperature 150 °C
 0.29

@Temperature 302 °F
0.291

@Temperature 200 °C
 0.291

@Temperature 392 °F
0.294

@Temperature 250 °C
 0.294

@Temperature 482 °F
0.294

@Temperature 300 °C
 0.294

@Temperature 572 °F
Fatigue Strength 101.5 MPa

@Temperature 150 °C
 14720 psi

@Temperature 302 °F
 P50% rotary bending values for 5X10<sup>7</sup> cycles
Shear Modulus 35.0 GPa

@Temperature 300 °C
 5080 ksi

@Temperature 572 °F
36.0 GPa

@Temperature 250 °C
 5220 ksi

@Temperature 482 °F
37.0 GPa

@Temperature 200 °C
 5370 ksi

@Temperature 392 °F
38.0 GPa

@Temperature 150 °C
 5510 ksi

@Temperature 302 °F
38.0 GPa

@Temperature 100 °C
 5510 ksi

@Temperature 212 °F
40.0 GPa

@Temperature 20.0 °C
 5800 ksi

@Temperature 68.0 °F
Thermal Properties Metric English Comments
CTE, linear 15.3 - 16.3 µm/m-°C

@Temperature 20.0 - 100 °C
 8.50 - 9.06 µin/in-°F

@Temperature 68.0 - 212 °F
16.1 - 17.1 µm/m-°C

@Temperature 20.0 - 200 °C
 8.94 - 9.50 µin/in-°F

@Temperature 68.0 - 392 °F
17.0 - 18.0 µm/m-°C

@Temperature 20.0 - 300 °C
 9.44 - 10.0 µin/in-°F

@Temperature 68.0 - 572 °F
Specific Heat Capacity 0.840 - 0.880 J/g-°C
0.201 - 0.210 BTU/lb-°F
Thermal Conductivity 95.30 W/m-K

@Temperature 400 °C
 661.4 BTU-in/hr-ft²-°F

@Temperature 752 °F
99.20 W/m-K

@Temperature 200 °C
 688.4 BTU-in/hr-ft²-°F

@Temperature 392 °F
99.20 W/m-K

@Temperature 300 °C
 688.4 BTU-in/hr-ft²-°F

@Temperature 572 °F
99.60 W/m-K

@Temperature 100 °C
 691.2 BTU-in/hr-ft²-°F

@Temperature 212 °F
101.2 W/m-K

@Temperature 30.0 °C
 702.3 BTU-in/hr-ft²-°F

@Temperature 86.0 °F
Melting Point 528 - 784 °C
982 - 1440 °F
Solidus 528.1 - 534.1 °C
982.6 - 993.4 °F
Liquidus 784.2 - 790.2 °C
1444 - 1454 °F
Component Elements Properties Metric English Comments
Aluminum, Al 63 %
63 %
As Balance
Cobalt, Co 1.0 %
1.0 %
Copper, Cu 3.0 %
3.0 %
Iron, Fe 3.0 %
3.0 %
Magnesium, Mg 1.0 %
1.0 %
Nickel, Ni 3.0 %
3.0 %
Silicon, Si 25 %
25 %
Titanium, Ti 1.0 %
1.0 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.00000910 - 0.0000100 ohm-cm
0.00000910 - 0.0000100 ohm-cm