Polimeri Europa Greenflex® FD 53 Ethylene Vinyl Acetate Copolymer - Blown Film Extrusion

Category Polymer , Film , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate Copolymer (EVA), Film Grade
Manufacturer Polimeri Europa (Former EniChem)
Trade Name Greenflex®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polimeri Europa Greenflex® FD 53 Ethylene Vinyl Acetate Copolymer - Blown Film Extrusion.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Greenflex FD 53 is an ethylene vinyl acetate copolymer (EVA), containing antiblocking agent, for blown film extrusion. Films produced with Greenflex FD 53 exhibit good sealing properties, high flexibility and toughness and optimum processability.Main Applications: Greenflex FD 53 is recommended for the production of agricultural films and water proofing membrane having outstanding mechanical performances (flexibility, elasticity and adherence) and dimensional stability.Information provided by Polimeri Europa.
Physical Properties Metric English Comments
Specific Gravity 0.938 g/cc
0.938 g/cc
ISO 1183
Vinyl Acetate Content 17 %
17 %
Internal Method
Thickness 50.0 - 200 microns
1.97 - 7.87 mil
Recommended
Melt Flow 0.47 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.47 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore A 90
90
ISO 868/A
Hardness, Shore D 39
39
ISO 868/A
Film Tensile Strength at Yield, MD 5.00 MPa
725 psi
ISO 527-3
Film Tensile Strength at Yield, TD 4.50 MPa
653 psi
ISO 527-3
Film Elongation at Break, MD 490 %
490 %
ISO 527-3
Film Elongation at Break, TD 630 %
630 %
ISO 527-3
Coefficient of Friction, Dynamic >= 0.50
>= 0.50
ISO 8295
Elmendorf Tear Strength, MD 3.057 g/micron
77.65 g/mil
ISO 6383-2
Elmendorf Tear Strength, TD 5.095 g/micron
129.4 g/mil
ISO 6383-2
Dart Drop Test >= 700 g
>= 1.54 lb
F50; ISO 7765-1
Film Tensile Strength at Break, MD 34.0 MPa
4930 psi
ISO 527-3
Film Tensile Strength at Break, TD 32.0 MPa
4640 psi
ISO 527-3
1% Secant Modulus, MD 55.0 MPa
7980 psi
ISO 527-3
1% Secant Modulus, TD 60.0 MPa
8700 psi
ISO 527-3
Thermal Properties Metric English Comments
Melting Point 88.0 °C
190 °F
Internal Method
Vicat Softening Point 67.0 °C

@Load 1.00 kg
153 °F

@Load 2.20 lb
ISO 306/A
Brittleness Temperature <= -80.0 °C
<= -112 °F
ASTM D746
Optical Properties Metric English Comments
Haze 8.0 %
8.0 %
ISO 14782
Gloss 72 %
72 %
45°; ASTM D2457