PolyOne Geon™ FIT E 50 Polyvinyl Chloride Homopolymer (PVC Homopolymer)

Category Polymer , Thermoplastic , Vinyl (PVC)
Manufacturer PolyOne Corporation
Trade Name Geon™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Geon™ FIT E 50 Polyvinyl Chloride Homopolymer (PVC Homopolymer).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Geon® FIT E 50 is a low molecular weight homopolymer resin intended for use as a Formulation Improvement Tool (FIT) in plastisol formulations which enhance the plastisol usage (pot life) and reduce the viscosity aging characteristics. Geon® FIT E 50 resins increase physical properties up to 30% compared to traditional blending resins. It allows the addition of up to 40phr of filler, significantly decreasing the formulation cost. It improves air release properties, provides faster de -aeration time and reduces scrap rates caused by the presence of air bubbles or voids in finished part. This resin reduces the viscosity profile of the plastisol providing an improved 'ease of coating' performance resulting a more uniform plastisol coating and improving line up time. Geon® FIT E 50 is recommeded for solid and foamed plastisol applications for instance coated fabrics and carpet tiles, cast films and coatings, rotational and slush molded parts, dip molded and coated parts, and walk off and foam mats and pads.Note: The value set forth represent typical values and PolyOne Corporation, therefore, makes no representation that the material in any particular shipment will conform to the listed properties. Packaging: This resin is shipped in multi-wall paper bags, net weight 50 lbs, 2500 lbs per pallet. Information shown on the package includes commercial identification number, lot and weight. Geon® ALTC (formulation): 60phr Geon® 121A, 40phr Geon® FIT E 50, 57phr DINP, 3phr ESO, and 2phr Therm-Chek SP 120 LOHF Geon® STP 1203(formulation): 60phr Geon® 178, 40phr Geon® FIT E 50,and 60phr DOPInformation provided by PolyOne
Physical Properties Metric English Comments
Specific Gravity 1.40 g/cc
1.40 g/cc
ASTM D792
Volatiles 0.070 %
0.070 %
Geon® STP 1242; Internal Method
Apparent Bulk Density 0.530 g/cc
0.0191 lb/in³
Geon® STP 1169; Internal Method
Particle Size 30 µm
30 µm
Geon® DFT 1466; Internal Method
<= 52 µm
<= 52 µm
95%; Geon® DFT 1466; Internal Method
<= 74 µm
<= 74 µm
99%; Geon® DFT 1466; Internal Method
Relative Viscosity 1.95 cP
1.95 cP
Correlation, Cyclohexanone 1%; Internal Method
Brookfield Viscosity 2.03 cP
2.03 cP
Initial Viscosity @ 20 rpmGeon® ALTC 22 (with provided formulation); Internal Method
2.1 cP
2.1 cP
Initial Viscosity @ 2 rpmGeon® ALTC 22 (with provided formulation); Internal Method
2.4 cP
2.4 cP
One Day Viscosity @ 2 rpmGeon® ALTC 22 (with provided formulation); Internal Method
2.48 cP
2.48 cP
One Day Viscosity @ 20 rpmGeon® ALTC 22 (with provided formulation); Internal Method
Viscosity Measurement 0.75
0.75
Inherent; ASTM D1243-60-A
Melt Flow 540 g/10 min

@Pressure 0.655 MPa
540 g/10 min

@Pressure 95.0 psi
Severs Efflux; Geon® ALTC 23 (with provided formulation); Internal Method
Optical Properties Metric English Comments
Haze 15 %
15 %
Fused 5 mins @ 350FGeon® ALTC 66 (with provided formulation); Internal Method
Gloss 15 %
15 %
60 Degree, Fused 5 mins @ 350FGeon® ALTC 65 (with provided formulation); Internal Method
Descriptive Properties Value Comments
Forms Powder
Fine, White Powder
Gel Temperature 88 °C
Internal Method; Geon® ALTC 29 (with provided formulation)
Generic Material PVC Homopolymer
Generic Name Polyvinyl Chloride Homopolymer (PVC Homopolymer)
K-Value 60
Internal Method; Correlation, 0.5g/100ml
Polymerization Process Suspension
Regional Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
Residual Vinyl Chloride Monomer < 5 ppm
Internal Method; Geon® STP 1005
Vinyl Dispersion Gauge 95 µm
Internal Method; Geon® STP 1203 (with provided formulation)