PolyOne Novablend™ 6602 Polyvinyl Chloride, Rigid (PVC, Rigid)

Category	Polymer , Thermoplastic , Vinyl (PVC) , PVC, Rigid Grade
Manufacturer	PolyOne Corporation
Trade Name	Novablend™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PolyOne Novablend™ 6602 Polyvinyl Chloride, Rigid (PVC, Rigid).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Novablend 6602 is a rigid, opaque PVC for molding compounds. This product has high impact, excellent indoor/outdoor weathering, high flow, and good processing characteristics.Applications includes: Electrical,Business machines,Telecommunications, Multi Purpose.Information provided by PolyOne

Physical Properties	Metric	English	Comments
Specific Gravity	1.35 g/cc	1.35 g/cc	ASTM D792
Linear Mold Shrinkage, Flow	0.0020 - 0.0050 cm/cm	0.0020 - 0.0050 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	81	81	15 sec; ASTM D2240
Tensile Strength	45.5 MPa	6600 psi	ASTM D638
Elongation at Break	32 %	32 %	ASTM D638
Tensile Modulus	2.45 GPa	355 ksi	Type I; ASTM D638
Flexural Strength	70.3 MPa	10200 psi	ASTM D790
Flexural Modulus	2.52 GPa	365 ksi	ASTM D790
Izod Impact, Notched	6.40 J/cm @Thickness 3.18 mm, Temperature 23.0 °C	12.0 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F	Injection Molded; ASTM D256A

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	67.2 °C @Thickness 3.18 mm	153 °F @Thickness 0.125 in	Unannealed; ASTM D648
	70.6 °C @Thickness 3.18 mm	159 °F @Thickness 0.125 in	Annealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	57.0 °C @Thickness 3.18 mm	135 °F @Thickness 0.125 in	Unannealed; ASTM D648
	68.3 °C @Thickness 3.18 mm	155 °F @Thickness 0.125 in	Annealed; ASTM D648
UL RTI, Electrical	105 °C @Temperature 105 °C	221 °F @Temperature 221 °F	UL 746
UL RTI, Mechanical with Impact	105 °C @Temperature 105 °C	221 °F @Temperature 221 °F	elong; UL 746
UL RTI, Mechanical without Impact	105 °C @Temperature 105 °C	221 °F @Temperature 221 °F	UL 746
Flammability, UL94	5VA @Thickness 1.80 mm	5VA @Thickness 0.0709 in	All, Also UL 94 V-O @ 0.059 in thick.; UL 94

Processing Properties	Metric	English	Comments
Melt Temperature	199 - 204 °C	390 - 399 °F

Descriptive Properties	Value	Comments
Forms	Pellets
Generic Material	PVC, Rigid
Generic Name	Polyvinyl Chloride, Rigid (PVC, Rigid)
Outdoor Suitability	f1	UL 746C
Regional Availability	North America
Uses	Outdoor Applications