PolyOne Syncure™ System S110FV Polyethylene, Crosslinked (XLPE)

Category Polymer , Thermoplastic , Polyethylene (PE)
Manufacturer PolyOne Corporation
Trade Name Syncure™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Syncure™ System S110FV Polyethylene, Crosslinked (XLPE).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Syncure™ systems are two part moisture crosslinkable compounds, is a UL bulletinized high strength, highly flame retardant insulation compound. Available in a RoHS complaint version.NOTE: The above represents Typical Properties measured on 14 AWG with 30 mil wall. STORAGE AND HANDLING: Use within 48 hours once package is open to avoid self-curing and scrap.Information provided by PolyOne
Physical Properties Metric English Comments
Specific Gravity 1.29 g/cc
1.29 g/cc
ASTM D792
Deformation 3.0 %

@Temperature 131 °C,
Time 3600 sec
3.0 %

@Temperature 268 °F,
Time 1.00 hour
500 g; UL 1581
Mechanical Properties Metric English Comments
Hardness, Shore D 50
50
10 sec; ASTM D2240
54
54
ASTM D2240
Tensile Strength, Yield 17.2 MPa
2490 psi
Type IV, 510 mm/min; ASTM D638
Elongation at Break 400 %
400 %
Type IV, 510 mm/min; ASTM D638
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 90.0 °C
194 °F
UL Temperature Rating
Oxygen Index 27 %

@Thickness 1.91 mm
27 %

@Thickness 0.0752 in
ASTM D2863
Electrical Properties Metric English Comments
Dielectric Constant 2.54

@Frequency 1.00e+6 Hz
2.54

@Frequency 1.00e+6 Hz
ASTM D150
Dielectric Strength 39.0 kV/mm
991 kV/in
ASTM D149
Dissipation Factor 0.0028

@Frequency 1.00e+6 Hz
0.0028

@Frequency 1.00e+6 Hz
ASTM D150
Descriptive Properties Value Comments
Agency Ratings UL 44
UL VW-1
Appearance Natural Color
Catalyst Masterbatch 50%
V-0044G RoHS
Features Flame Retardant
Oil Resistant
Flame Test Pass
UL 1581; Vertical
Forms Pellets
Gel Content 60%
ASTM D2765; Crosslinked PE, Method B (NonReferee Test)
Generic Material XLPE
Generic Name Polyethylene, Crosslinked (XLPE)
Grafted Base Resin 50%
S-1060A
Processing Method Extrusion Coating
Regional Availability North America
Retention of Tensile Elongation 94%
121°C, 1.91 mm; 336 hr, UL Standard
Retention of Tensile Strength 100%
121°C, 1.91 mm; 336 hr, UL Standard
Uses Insulation
Wire & Cable Applications