SABIC Innovative Plastics ULTEM 9075 PEI (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name ULTEM
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics ULTEM 9075 PEI (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
High flow Polyetherimide blend. Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke, and flame evolution.
Physical Properties Metric English Comments
Density 1.32 g/cc
0.0477 lb/in³
ISO 1183
Moisture Absorption 0.700 %
0.700 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 1.25 %
1.25 %
ISO 62
Linear Mold Shrinkage, Flow 0.0060 - 0.0080 cm/cm
0.0060 - 0.0080 in/in
on Tensile Bar; SABIC Method
Melt Index of Compound 15 g/10 min

@Load 5.00 kg,
Temperature 340 °C
 15 g/10 min

@Load 11.0 lb,
Temperature 644 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Hardness, H358/30 127 MPa
18400 psi
ISO 2039-1
Tensile Strength at Break 75.0 MPa
10900 psi
50 mm/min; ISO 527
Tensile Strength, Yield 90.0 MPa
13100 psi
50 mm/min; ISO 527
Elongation at Break 25 %
25 %
50 mm/min; ISO 527
Elongation at Yield 6.0 %
6.0 %
50 mm/min; ISO 527
Tensile Modulus 3.20 GPa
464 ksi
1 mm/min; ISO 527
Flexural Strength 120 MPa
17400 psi
2 mm/min; ISO 178
Flexural Yield Strength 130 MPa
18900 psi
2 mm/min; ISO 178
Flexural Modulus 3.20 GPa
464 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 7.00 kJ/m²
3.33 ft-lb/in²
80*10*4; ISO 180/1A
5.00 kJ/m²

@Temperature -30.0 °C
 2.38 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
Charpy Impact, Notched 0.700 J/cm²
3.33 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
0.600 J/cm²

@Temperature -30.0 °C
 2.86 ft-lb/in²

@Temperature -22.0 °F
 Edgew 80*10*4 sp=62mm; ISO 179/1eA
Taber Abrasion, mg/1000 Cycles 15
15
CS-17, 1 kg; SABIC Method
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 50.0 µm/m-°C

@Temperature 23.0 - 150 °C
 27.8 µin/in-°F

@Temperature 73.4 - 302 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 50.0 µm/m-°C

@Temperature 23.0 - 150 °C
 27.8 µin/in-°F

@Temperature 73.4 - 302 °F
 ISO 11359-2
Thermal Conductivity 0.260 W/m-K
1.80 BTU-in/hr-ft²-°F
ISO 8302
Deflection Temperature at 0.46 MPa (66 psi) 200 °C
392 °F
Edgew 120*10*4 sp=100mm; ISO 75/Be
Deflection Temperature at 1.8 MPa (264 psi) 185 °C
365 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
Vicat Softening Point 200 °C
392 °F
Rate B/50; ISO 306
200 °C
392 °F
Rate B/120; ISO 306
210 °C
410 °F
Rate A/50; ISO 306
Flammability, UL94 V-0

@Thickness 1.60 mm
 V-0

@Thickness 0.0630 in
 UL 94 by SABIC-IP
Glow Wire Test 960 °C

@Thickness 3.20 mm
 1760 °F

@Thickness 0.126 in
 IEC 60695-2-12
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C PASSES
IEC 60695-10-2
OSU total heat release (2 minute test) 0kW-min/m^2
FAR 25.853
OSU peak heat release rate (5 minute test) 16kW/m^2
FAR 25.853