Solvay Engineered Polymers SEQUEL® E3000 HMS TPO  (discontinued **)

Category Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Olefinic Elastomer (TPO) , Polyolefin
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Engineered Polymers SEQUEL® E3000 HMS TPO  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: SEQUEL® E3000HMS thermoplastic olefinic elastomer (TPO) is designed for exterior and interior applications that require stiffness and durability. This extrusion-grade material is specially formulated to exhibit high melt-strength performance. This material can be supplied with or without UV stabilizers. Applications: Sheet extrusion and thermoforming Information provided by Solvay Engineered Polymers.LyondellBasell acquired Solvay Engineered Polymers in 2008. This grade is not part of the current LyondellBasell product line.
Physical Properties Metric English Comments
Specific Gravity 1.07 g/cc
1.07 g/cc
ASTM D792
Linear Mold Shrinkage 0.0080 - 0.010 cm/cm
0.0080 - 0.010 in/in
ASTM D955
Melt Flow 1.1 g/10 min

@Load 2.16 kg,
Temperature 230 °C
1.1 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 23.0 MPa
3340 psi
ASTM D638
Elongation at Break 300 %
300 %
ASTM D638
Flexural Modulus 2.069 GPa
300.1 ksi
I.B., TAN, 0.5 in/min; ASTM D790
Izod Impact, Notched 9.98 J/cm
18.7 ft-lb/in
NB; ASTM D256
1.60 J/cm

@Temperature -30.0 °C
3.00 ft-lb/in

@Temperature -22.0 °F
PB; ASTM D256
Gardner Impact >= 36.2 J

@Temperature -30.0 °C
>= 26.7 ft-lb

@Temperature -22.0 °F
ASTM D5420-96
>= 36.2 J

@Temperature 23.0 °C
>= 26.7 ft-lb

@Temperature 73.4 °F
ASTM D5420-96
Thermal Properties Metric English Comments
CTE, linear 50.2 µm/m-°C

@Temperature 20.0 °C
27.9 µin/in-°F

@Temperature 68.0 °F
modified; ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 105 °C
221 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 57.8 °C
136 °F
ASTM D648