UBE UBEPOL BR150B Synthetic Rubber (Compound)
| Category | Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | UBE |
| Trade Name | UBEPOL |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | UBE UBEPOL BR150B Synthetic Rubber (Compound).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: UBEPOL BR is UBE's line of polybutadiene rubber products.Information provided by UBE.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Mooney Viscosity | 49.5 @Temperature 100 °C |
49.5 @Temperature 212 °F |
ML1+4; ASTM D1646 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 0.720 MPa | 104 psi | |
| Elongation at Break | 1110 % | 1110 % | |
| Modulus of Elasticity | 0.000390 GPa | 0.0566 ksi | 600% Modulus |
| 50% Modulus | 0.000220 GPa | 0.0319 ksi | |
| 300% Modulus | 0.000280 GPa | 0.0406 ksi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage | 53 % | 53 % | Mill Shrinkage |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Extrusion Rate | 66.7 g/min | 66.7 g/min | |
| Cure Time | 10.6 min | 0.177 hour | t10 |
| 12.8 min | 0.213 hour | t90 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Die Swell | 4.87 g/min |
Users viewing this material also viewed the following:
- Old Hickory M-33 Kentucky Ball Clay
- KKPC Kuhmo HI 410T Transparent HIPS
- Solvay TECHNYL® AR 218 V25 Nylon 66, 25% glass fiber, DRY
- Teknor Apex Telcar® TL-2545A Thermoplastic Elastomer
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 40 PHR Non-Black, Mistron Vapor
- DuPont Teijin Films Mylar® LB Polyester Film, 92 Gauge (23 µm)
- Fainplast Compounds HAX HF 108 Halogen Free PVC
- Azdel SuperLite® SL552000-100 PP Resin Matrix / 55% Glass Fiber (6 mm Molded Thickness)
- Bulk Molding Compounds BMC 404 Thermoset Polyester, Low Shrink, High Strength, Electrical Grade
- Adell BW-17 Nylon 6, 35% Glass Reinforced; Superior Finish
Copyright © lookpolymers.com All Rights Reserved