Unitika RUN35-C25 PA6, Dry
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | Unitika |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Unitika RUN35-C25 PA6, Dry.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High modulus and low warpage nylonInformation provided by Unitika Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.66 g/cc | 0.0600 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 1.0 % | 1.0 % | 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm @Thickness 3.20 mm |
0.0010 in/in @Thickness 0.126 in |
|
| Linear Mold Shrinkage, Transverse | 0.0050 cm/cm @Thickness 3.20 mm |
0.0050 in/in @Thickness 0.126 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 164 MPa | 23800 psi | ISO 527-1/-2 |
| Elongation at Break | 1.3 % | 1.3 % | ISO 527-1/-2 |
| Tensile Modulus | 17.5 GPa | 2540 ksi | ISO 527-1/-2 |
| Flexural Strength | 240 MPa | 34800 psi | ISO 178 |
| Flexural Modulus | 15.0 GPa | 2180 ksi | ISO 178 |
| Charpy Impact Unnotched | 3.50 J/cm² | 16.7 ft-lb/in² | ISO 179-1 |
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | ISO 179-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 15.0 µm/m-°C | 8.33 µin/in-°F | ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 194 °C | 381 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 191 °C | 376 °F | ISO 75-1/-2 |