Vyncolit X659 Glass, Mineral and Graphite Filled Novolac Phenolic

Category Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic , Phenolic, Novolac, Mineral/Glass Filled , Phenolic, Novolac, Mineral/Graphite Filled
Manufacturer Vyncolit N.V., Sumitomo Bakelite
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Vyncolit X659 Glass, Mineral and Graphite Filled Novolac Phenolic.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Novolac resin based, glass fiber, mineral and graphite filled. Grade with superior stiffness, high dimensional stability and excellent tribological properties. Good chemical resistance against several fuels at elevated temperatures. Used for fuel pump housings.Information provided by Sumitomo Bak North America, Inc.
Physical Properties Metric English Comments
Bulk Density 1.00 g/cc
0.0361 lb/in³
ISO 60
Density 2.06 g/cc
0.0744 lb/in³
ISO 1183
Water Absorption 0.040 %
0.040 %
ISO 62
Linear Mold Shrinkage 0.0020 cm/cm
0.0020 in/in
ISO 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 89.0 MPa
12900 psi
ISO 527-1
Elongation at Break 0.35 %
0.35 %
ISO 527-1
Tensile Modulus 29.0 GPa
4210 ksi
ISO 527-1
Flexural Strength 163 MPa
23600 psi
ISO 178
Flexural Modulus 26.0 GPa
3770 ksi
ISO 178
Compressive Strength 269 MPa
39000 psi
ISO 604
Charpy Impact Unnotched 0.960 J/cm²
4.57 ft-lb/in²
ISO 179-1
Charpy Impact, Notched 0.260 J/cm²
1.24 ft-lb/in²
ISO 179-1
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 14.0 µm/m-°C
7.78 µin/in-°F
TMA
CTE, linear, Transverse to Flow 30.0 µm/m-°C
16.7 µin/in-°F
TMA
Deflection Temperature at 1.8 MPa (264 psi) >= 222 °C
>= 432 °F
ISO 75 Af
Shrinkage 0.010 %
0.010 %
Post Shrinkage; ISO 2577
Descriptive Properties Value Comments
Color Black
Molding Method Compression
Injection
Transfer