- Polymer Property : Melt Flow = 20 g/10 min
Polymer Property : Melt Flow = 20 g/10 min Product List
Physical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 190 °C |
20 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Polimeri Europa Riblene® MR 30 Low Density Polyethylene - Injection Molding Riblene MR 30 is a high fluidity low density polyethylene resin (LDPE) characterized by a high flowability and a medium rigidity.Parts made with Riblene MR 30 are characterized by good mechanical an.. |
|||
| Melt Flow | 20 - 40 g/10 min @Load 11.6 kg, Temperature 250 °C |
20 - 40 g/10 min @Load 25.6 lb, Temperature 482 °F |
ASTM D1238 |
| Polymer Resources PPX-FR2-[color]-EN Modified-PPO, V-1 Flame Retardant, Extrusion Grade Modified-Polyphenylene Oxide, V-1 Flame Retardant, 210F HDT, Extrusion GradeFeatures: • Bromine Free • Chlorine FreeProcess: ExtrusionNotes: All physical, mechanical and thermal testing conducte.. |
|||
| Melt Flow | 20 - 30 g/10 min @Load 11.6 kg, Temperature 250 °C |
20 - 30 g/10 min @Load 25.6 lb, Temperature 482 °F |
ASTM D1238 |
| Polymer Resources PPX-GP4 Modified-PPO, General Purpose Modified-Polyphenylene Oxide, General Purpose, 210F HDTProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Informati.. |
|||
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 190 °C |
20 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Eastman Voridian D4053-A Polyethylene
(discontinued **) Voridian polyethylene D4053-A is a low density formulation used for injection molding. It is an outstanding material for molding lids and other container closures because it processes easily on aut.. |
|||
| Melt Flow | 20 g/10 min | 20 g/10 min | 230/2.16 (typical); ASTM D1238 |
| Fiberfil® PP-61/V2 Polypropylene Copolymer, Flame Retardant, UL94 V2 Information provided by FIBERFIL Engineered Plastics |
|||
| Melt Flow | 20 g/10 min @Load 10.0 kg, Temperature 220 °C |
20 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| LG Chemical LI911 ASA Description: Good Weatherability, High FlowApplication: Air-conditioner grill, Sawing Machine Cover, Electric/Electronic ApplicationsCAS: 26299-47-8Information provided by LG Chemical |
|||
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 230 °C |
20 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Inno-Comp INNOPOL® CS 2-2000 TO Polypropylene Block-Copolymer Based Compound INNOPOL® CS 2-2000 TO is a polypropylene block-copolymer based compound. This grade is available in natural and custom colored form.INNOPOL® CS 2-2000 TO is developed for producing injection m.. |
|||
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 230 °C |
20 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| LG Chemical LUPOL TE5007B PP+Rubber, High Impact Description: Injection Molding, PP+Rubber, Low Density, High Impact, Good WeatherabilityApplication: Automotive Exterior (Bumper Fascia , Rear Bumper Step)Information provided by LG Chemical |
|||
| Melt Flow | 20 g/10 min @Load 5.00 kg, Temperature 275 °C |
20 g/10 min @Load 11.0 lb, Temperature 527 °F |
ISO 1133 |
| Gromax BFG50-AH00B2 Nylon 6 50% Glass Filled (Dry) Information provided by Gromax Enterprises Corp. |
|||
| Melt Flow | 20 g/10 min @Load 5.00 kg, Temperature 280 °C |
20 g/10 min @Load 11.0 lb, Temperature 536 °F |
ASTM D1238 |
| SABIC Innovative Plastics NORYL GTX GTX973 PPE+PA (Europe-Africa-Middle East) NORYL GTX973 is a material especially designed for electrostatic painting and powder coating applications. The material combines high heat resistance with impact and conductivity in a unique way. |
|||
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 190 °C |
20 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| A. Schulman POLYBATCH™ Green 3012E Concentrate Based In Polyethylene DescriptionPOLYBATCH® 3012E is a green color concentrate based in polyethylene. This concentrate was designed to provide color in polyolefin film and molding applications. POLYBATCH® 3012E is he.. |
|||
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 190 °C |
20 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| A. Schulman POLYBATCH™ 60186U Almond Concentrate Based in LLDPE DescriptionPOLYBATCH® Almond 60186U is an almond color concentrate containing an optimized blend of color and UV stabilizer based in LLDPE. POLYBATCH® 60186U is heavy metal free and is typically.. |
|||
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 190 °C |
20 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| A. Schulman POLYBATCH™ Red 5557 Concentrate Based In Polyethylene DescriptionPOLYBATCH® 5557 is a red color concentrate based in polyethylene. This concentrate was designed to provide color in polyolefin film and molding applications. POLYBATCH® 5557 is heavy .. |
|||
| Melt Flow | 20 g/10 min | 20 g/10 min | ASTM D1238 |
| Tipco Tipcofil® AG 200 - 10% Glass Fiber Reinforced Nylon-6 Compound, with High Heat Stability 10% Glass Reinforced Nylon-6 CompoundApplications: General PurposeProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries Ltd.,
India. |
|||
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 190 °C |
20 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| A. Schulman POLYBATCH™ Lattice Grey 80354U/4 Concentrate Based In LLDPE DescriptionPOLYBATCH® 80354U/4 is a grey color concentrate containing an optimized blend of color and UV stabilizer based in LDPE. This concentrate was designed to provide color and UV stability i.. |
|||
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 190 °C |
20 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| A. Schulman POLYBATCH™ Blue 4500 Concentrate Based In Polyethylene DescriptionPOLYBATCH® 4500 is a blue color concentrate based in polyethylene. This masterbatch was designed to provide color in polyolefin film and molding applications. POLYBATCH® 4500 is typic.. |
|||
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 190 °C |
20 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| A. Schulman POLYBATCH™ CE-505-E Concentrate Based In Polyethylene DescriptionPOLYBATCH® CE-505-E is a 5% erucamide slip concentrate based in polyethylene. This concentrate is designed to reduce film COF in LDPE, LLDPE, and mPE cast and blown films. POLYBATCH® .. |
|||
| Melt Flow | 20 - 30 g/10 min @Temperature 230 °C |
20 - 30 g/10 min @Temperature 446 °F |
Condition L; ASTM D1238 |
| A. Schulman POLYFORT™ PP 2175HU-31 High Flow Copolymer Polypropylene DescriptionPolyfort® PP 2175HU-31 is a high flow copolymer polypropylene.Information provided by A. Schulman. |
|||
| Melt Flow | 20 - 40 g/10 min @Load 21.6 kg, Temperature 190 °C |
20 - 40 g/10 min @Load 47.6 lb, Temperature 374 °F |
|
| Lubrizol ESTANE® GP92AT Ether Based Thermoplastic Polyurethane Type: Estane® GP 92AT is an aromatic polyether-based thermoplastic polyurethane (TPU).Appearance: Translucent spherical pelletsUses: Injection molding partsAvailable in EuropeInformation provided b.. |
|||
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 190 °C |
20 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| A. Schulman POLYBATCH™ Treated Pine 60181U/4 Concentrate Based In LLDPE DescriptionPOLYBATCH® 60181U/4 is a treated pine color concentrate containing an optimized blend of color and UV stabilizer based in LLDPE. This concentrate was designed to provide color and UV s.. |
|||
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 190 °C |
20 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| A. Schulman POLYBATCH™ Orange 1770E Concentrate Based In Polyethylene DescriptionPOLYBATCH® 1770E is an orange color concentrate based in polyethylene. This concentrate was designed to provide color in polyolefin film and molding applications. POLYBATCH® 1770E is .. |
|||
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 230 °C |
20 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D 1238 |
| Cossa Polimeri ESTAPROP 1006 V2 H Flame Retardant Polypropylene PP copolymerFlame retardant class V2, PBDE and antimony trioxide free, no blooming, low smoke emission, good physical and mechanical characteristicsInformation provided by Cossa Polimeri S.r.l. |
|||
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 190 °C |
20 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D 1238 |
| Chevron Phillips Marlex® 9018 HDPE Injection Molding Resin Resin Type: Linear Copolymer, ASTM D 4976 Classification: PE 232, A 53600Characteristics: Good Flow, Good Impact Strength, Good Stiffness, Good ESCR, Good Shrinkage ResistanceApplications:Housewares.. |
|||
| Melt Flow | 20 g/10 min @Load 1.20 kg, Temperature 300 °C |
20 g/10 min @Load 2.65 lb, Temperature 572 °F |
ISO 1133 |
| Covestro Makrolon® 2400 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• General purpose• Low.. |
|||
| Melt Flow | 20 g/10 min @Load 1.20 kg, Temperature 300 °C |
20 g/10 min @Load 2.65 lb, Temperature 572 °F |
ISO 1133 |
| Covestro Makrolon® 2407 MAS070 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• General purpose• Low.. |
|||
| Melt Flow | 20 g/10 min @Load 5.00 kg, Temperature 230 °C |
20 g/10 min @Load 11.0 lb, Temperature 446 °F |
ISO 1133 |
| Eurostar Starflam M10009AP PP, Flame Retardant, Injection Molding Starflam M10009AP is an Unfilled Flame Retardant high fluidity Polypropylene (Homo) Injection Molding ResinInformation provided by Eurostar. |
|||
| Melt Flow | 20 g/10 min | 20 g/10 min | ISO 1133 |
| Addiplast Addilene J 522 K20 Polypropylene Copolymer High densityInformation provided by Addiplast. |
|||
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 190 °C |
20 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| A. Schulman POLYBATCH™ Tan LL60139/2 Concentrate Based In LLDPE DescriptionPOLYBATCH® LL60139/2 is a tan color concentrate based in LLDPE. This concentrate was designed to provide opacity and color in blow molding applications. POLYBATCH® LL60139/2 is typic.. |
|||
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 190 °C |
20 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| A. Schulman POLYBATCH™ Yellow 2214E Concentrate Based In Polyethylene DescriptionPOLYBATCH® 2214E is a yellow color concentrate based in polyethylene. This concentrate was designed to provide color in polyolefin film and molding applications. POLYBATCH® 2214E is h.. |
|||
| Melt Flow | 20 g/10 min @Load 3.80 kg, Temperature 250 °C |
20 g/10 min @Load 8.38 lb, Temperature 482 °F |
ASTM D1238 |
| Samyang Triloy® S460G15 Polymer Alloy, Reinforced Excellent impact, formability and weather resistance.220 is a reinforced grade.Applications: LCD Panel Frame - for dimensional stabilityInformation provided by Samyang. |
|||