Polymer Property : Flexural Strength = 13100 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most.

Mechanical Properties	Metric	English	Comments
Flexural Strength	90.0 MPa	13100 psi	ISO 178
Nilit FRIANYL B63 K Nylon 6 for injection molding Nylon 6 for injection molding, specially formulated for knobs.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Flexural Strength	<= 90.0 MPa	<= 13100 psi	ISO 178
Polykemi AB SCANMID 6 B32^ E Nylon 6, Modified Information provided by Polykemi AB
Flexural Strength	90.0 - 110 MPa	13100 - 16000 psi	Compression; ISO 178
Raschig Group 5553 DAP Glass-fiber reinforced diallyl phthalate molding compound. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensiona..
Flexural Strength	90.0 - 110 MPa	13100 - 16000 psi	Injection; ISO 178
Raschig Group AMPLA® 2000 melamine-modified polyester Halogen-free, organically and inorganically filled melamine-modified Polyester molding compound. Low post-shrinkage, very good electrical values, high heat resistance, very good sliding behavior, ve..
Flexural Strength	90.0 - 110 MPa	13100 - 16000 psi	Injection; ISO 178
Raschig Group DECAL® 2061 Phenolic Wood flour reinforced phenolic molding compound. Good electrical properties, chemical resistance and mechanical properties. This product meets the allowed upper limits for heavy metals and PCAs and ..
Flexural Strength	90.0 - 120 MPa	13100 - 17400 psi	Compression; ISO 178
Raschig Group MELOPAS® 2010 MF Melamine Organically and inorganically filled Melamine molding compound. Excellent surface hardness, good mechanical strength, good electrical properties. This product meets the allowed upper limits for heav..
Flexural Strength	90.0 MPa	13100 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP FARADEX NX07344 PC+ABS (Asia Pacific) Faradex NX07344 is a compound based on PC+ABS blend resin containing non-brominated and non-chlorinated flame retardant system, Stainless Steel and glass fiber. Added features of this material incl..
Flexural Strength	90.0 MPa	13100 psi	2 mm/min; ISO 178
Hexion Bakelite™ PF 14694 Phenolic Formaldehyde Resin, High Surface Quality  (discontinued **) Phenolic molding compound, mainly organically filled, very soft flow for large molds.Application areas: Housing parts, heat shields, cookware fittings.Information provided by Bak AGBak AG became a p..
Flexural Strength	90.0 MPa	13100 psi
Lehmann & Voss LUVOCOMÂ® 3-8266/BL Polyamide 6, unreinforced Applications: Automotive industry, textile machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Isotropic shrinkage characteristics.Reduce..
Flexural Strength	90.0 MPa	13100 psi	ISO 178
Mitsubishi XantarÂ® MX 2021 Polycarbonate XantarÂ® materials are engineered for performance, consistency and reliability. This makes XantarÂ® resins ideal for interior automotive components, electrical equipment and consumer appliances ..
Flexural Strength	90.0 MPa	13100 psi
Lehmann & Voss LUVOCOMÂ® 1/TF/18/SI/2 Polyamide 66, with PTFE, lubricant modified Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Isotropic shrinkage characteri..
Flexural Strength	90.0 MPa	13100 psi	2 mm/min; ISO 178
Sax Polymers SAXAMID 126H Nylon 6, Injection Molding Grade SAXAMID 126H is a general purpose polyamide 6 injection-molding-grade. Benefits are short cycle times and good release properties. Additionally it has a higher content of heat stabilizer which is p..
Flexural Strength	90.0 MPa	13100 psi
Sumitomo Bakelite DurezÂ® 31906 Phenolic, Injection Grade Durez 31906 Black Phenolic is an asbestos free, medium impact, molding compound. It is designed for applications where additional mechanical strength is required.Information provided by Sumitomo Ba..
Flexural Strength	90.0 MPa	13100 psi	ISO 178-93
Wellman Wellamid® FR22F-NBK3 Flame Retardant Nylon 66 Description: Flame Retardant Nylon 66Information provided by Wellman.
Flexural Strength	90.0 MPa	13100 psi	ASTM D790
Plenco 4548 Phenolic, Granular, Injection Molded PLENCO 04548 is a heat resistant mineral filled phenolic molding compound, offering fast cure rates and hot rigidity. Type ASTM 5948 CFG, and UL recognized under component file E40654. 04548 is avai..
Flexural Strength	90.0 MPa	13100 psi	ASTM D790
Polyram RamTough PZ503 Polycarbonate, Flame Retardant Flame retardant polycarbonate for injection molding applicationsInformation provided by Polyram Ram On Ind.
Flexural Strength	90.0 MPa	13100 psi	ISO 178
Polyram RamTough RZ320G2 Polycarbonate, 10% Glass Fiber, Flame Retardant 10% Glass fiber reinforced, flame retardant polycarbonate for injection molding applications.Information provided by Polyram.
Flexural Strength	90.0 MPa <br>@Diameter >=100 mm	13100 psi <br>@Diameter >=3.94 in	24hr/23°C/50% RH; ISO 178; IEC/EN 61212-2 5.1
Elektro-Isola Etronax MF Phenolic, Cotton Fabric Reinforcement, Brown, Tubes Description: Mechanical applications. Impact-resistant, noise-reducing and wear-resistant material. Well suited as a low-friction material. High wear resistance in aggressive and dust-filled environ..
Flexural Strength	90.0 MPa <br>@Strain 3.50 %	13100 psi <br>@Strain 3.50 %	ISO 178
DuPont Performance Polymers Delrin® 911DP NC010 Acetal (POM)  (Unverified Data**) Nucleated Low Viscosity Acetal Homopolymer Delrin 911DP is a low viscosity acetal homopolymer with improved thermal stability and modifications for more precise molding (reduced warpage less shrinka..
Flexural Strength	90.0 MPa	13100 psi	2 mm/min; ISO 178
Chi Mei Wonderlite® PC-122U Polycarbonate - UV Stabilized UV Stabilized
Flexural Strength	>= 90.0 MPa <br>@Diameter >=100 mm	>= 13100 psi <br>@Diameter >=3.94 in	Perpendicular to laminations; IEC 1212-2 4.1
Hippe PF CC 21 Woven Cotton Cloth Reinforced Phenolic Resin - Round, Rolled Tube Used in mechanical and electrical applications. Fine weave (>30 threads per cm).Information provided by Hippe.
Flexural Strength	>= 90.0 MPa	>= 13100 psi	cold bending
China-Yixing Longly Refractories Seggar Semi-Corundum-Mullite Our company's production of a variety of corundum mullite push slab (moved plate), corundum-mullite seggar, corundum mullite corrugated board and other kinds of the kiln furniture, high refractorine..
Flexural Strength	90.0 MPa	13100 psi	ASTM D790
Beijing Ranger Chem PBT-MFC-G0 FR PBT Modified PBT Characteristics: Unreinforced grades have abundant strength and flexibility, and have strong characteristics against brittleness. UL-certified slow-burning (94HB) and self-extinguishin..
Flexural Strength	90.0 - 120 MPa	13100 - 17400 psi	ISO 178
Bulk Molding Compounds tetra-DUR L 4305 Bulk Molding Compound UL-licensed. Anchor wave-isolation.Typical Applications - Requiring mechanical strength, abrasion resistance, dimensional stability, electrical insulation, electrostatic dissipation (explosion prote..
Flexural Strength	90.0 - 150 MPa	13100 - 21800 psi
Alliance S-32 Samarium Cobalt Magnetic Material
Flexural Strength	90.0 MPa	13100 psi	ASTM D790
Beijing Chemical Industry KAIFA® MN301-M30 Nylon 66 Resin Mineral filled, Good flowInformation provided by Beijing Chemical Industry Research Institute (Group)
Flexural Strength	90.0 MPa	13100 psi	ASTM D790
A. Schulman ComAlloy Hiloy® 212 Polystyrene, Glass Reinforced Data provided by the manufacturer, ComAlloy International Company.20% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
Flexural Strength	90.0 MPa	13100 psi	ISO 178
BLUESTAR BS270 Acetal Copolymer Information provided by Polymer Technology and Services, LLC (PTS).
Flexural Strength	90.0 MPa	13100 psi
Lehmann & Voss LUVOCOM® 1-7497 Polyamide 66, with PTFE, lubricant modified, heat stabilized Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Isotropic shrinkage characteri..
Flexural Strength	90.0 MPa	13100 psi	2 mm/min; ISO 178
Hexion Bakelite™ PF 83 Phenolic Formaldehyde Resin, Special Preparation Cylindrical Pellets  (discontinued **) Phenolic molding compound, organically filled, reinforced with cotton fibers, increased notched impact strength, standardized molding compound.Application areas: Switch covers, rolls, handle casings..