Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 90.0 MPa | 13100 psi | STN EN ISO 527-2 |
Plastcom SLOVAMID 66 GF 10 GB 20 Polyamide 66, 10% Glass Fiber, 20% Glass Beads FeaturesPA 66 chemically reinforced with 10% glass fiber and with the content of 20% glass beads. Improved anisotropy of shrinkage. The relation of the anisotropy to the mechanical properties can .. |
|||
Tensile Strength at Break | 90.0 MPa | 13100 psi | 50 mm/min; ASTM D638 |
Ovation Polymers RIGITRON 20415 GF PBT, 15% Glass Reinforced PBT - Glass reinforced (15 %), high tensile strength, stiffness and HDT. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All samples are prepared acco.. |
|||
Tensile Strength at Break | 90.0 MPa | 13100 psi | ISO 527 |
Nilit FRIANYL A63 HH Nylon 6.6 for injection molding Nylon 6.6 for injection molding, heat and hydrolysis stabilizedInformation provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Tensile Strength at Break | 90.0 MPa | 13100 psi | 10mm/min; ASTM D638 |
Kingfa JH710 G15 Flame Retardant & 15% Glass Fiber Reinforced PC Features:Environmental friendly flame retardantUL V-0 @ 1.6mmHigh mechanical strengthGood size stability, good surfaceSuitable for exact moldingApplications:CD-ROM, DVDPrinter, photocopier cabinetSc.. |
|||
Tensile Strength at Break | 90.0 MPa | 13100 psi | Conditioned; ISO 527-1/-2 |
Lanxess Durethan® AKV 15 H2.0 901510 Nylon 66, 15% Glass Fiber PA 66, injection molding grade, 15% glass fibers, good heat-ageing resistance |
|||
Tensile Strength at Break | 90.0 MPa | 13100 psi | ISO 527 Type 1A |
Solvay TECHNYL® A 548B2 V15 PA66, 15% glass fiber, DRY Description: TECHNYL® A 548B2 V15 is a polyamide 6.6, reinforced with 15% of glass fiber, heat stabilized, impact modified, for blow molding. This product is available in black color.Benefits: Th.. |
|||
Tensile Strength at Break | 90.0 MPa | 13100 psi | ISO 527 Type 1A |
Solvay TECHNYL® C 246 V 30 PA6, 30% glass fiber, Conditioned Description: Polyamide PA6, reinforced with 30 % of glass fiber, high impact strength, for injection molding.Available in: Asia Pacific and North AmericaProduct Applications: Having good mechanical .. |
|||
Tensile Strength at Break | 90.0 MPa | 13100 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Ultem 2412EPR PEI (Asia Pacific) 40% Milled glass filled, high flow Polyetherimide (Tg 217C) with internal mold release and enhanced electroplatability. ECO Conforming, UL94 V0 listing.This data was supplied by SABIC-IP for the As.. |
|||
Tensile Strength at Break | 90.0 MPa | 13100 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Xenoy® 1760T PBT+PC (Europe-Africa-Middle East) XENOY 1760T is developed as a easy flow material, for applications such as doorhandles and mirror housings. It is a 11% glass reinforced material with excellent strength and dimensional stability.Th.. |
|||
Tensile Strength at Break | 90.0 MPa | 13100 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP DX06313 PC (Asia Pacific) Polycarbonate base, 30% glass fiber reinforced, impact modified material. Thinwall housing, mobile phone. Some light color grades may have lower impact data than nature and black grade. |
|||
Tensile Strength at Break | 90.0 MPa | 13100 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP EX06430H PEI LNP* THERMOCOMP* EX06430H is a compound based on Polyetherimide resin containing Proprietary Filler(s). Added feature of this grade is: Healthcare. |
|||
Tensile Strength at Break | 90.0 MPa | 13100 psi | ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP RF002 PA 66 LNP THERMOCOMP* RF002 is a compound based on Nylon 66 resin containing 10% Glass Fiber. |
|||
Tensile Strength at Break | 90.0 MPa | 13100 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP WF0049XP PBT (Europe-Africa-Middle East) LNP* Thermocomp* WF0049XP is a compound based on Polybutylene Terephalate resin containing Glass Fiber, Flame Retardant. Added features of this material include: Flame Retardant. |
|||
Tensile Strength at Break | 90.0 MPa | 13100 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL GFN1720 PPE+HIPS (Asia Pacific) Noryl* GFN1720 is a 20% glass fiber reinforced, injection moldable grade. This modified polyphenylene ether resin is designed to deliver a balance of heat, strength and electrical properties. Noryl .. |
|||
Tensile Strength at Break | 90.0 MPa | 13100 psi | ISO 527-2 |
Tisan TISLAMID® 6 20% Glass Fiber Reinforced, Flame Retardant (V0). Halogen Free Heat Stabilized Nylon 6 TISLAMID has a wide area of application in electric/electronic, automotive, durable goods and telecommunications industries. It demonstrates characteristics such as Excellent chemical resistanceElec.. |
|||
Tensile Strength at Break | 90.0 MPa | 13100 psi | ISO 527-93 |
Wellman Wellamid® FRGF1827-BK1 10% Glass Fiber Reinforced Flame Retardant Nylon 66 Description: Glass Fiber Reinforced Flame Retardant Nylon 66Information provided by Wellman. |
|||
Tensile Strength at Break | 90.0 MPa | 13100 psi | DIN EN ISO 527 |
Wolf Kunststoff ZEDEX® ZX-324V2T A3F PEEK, PTFE Modified Reduced friction; High wear resistance; High elasticity; Stress resistantApplications: Shipbuilding; Chemical Engineering; Automotive Technology; Machine ToolsInformation provided by Zedex |
|||
Tensile Strength at Break | 90.0 MPa | 13100 psi | ASTM D 638 |
Cossa Polimeri ESTAPROP H 0560 HFC Polypropylene, 30% Glass Filled PP homopolymer 30% chemically coupled glass fiber reinforcedGood stiffness, excellent impact strengthInformation provided by Cossa Polimeri S.r.l. |
|||
Tensile Strength at Break | 90.0 MPa | 13100 psi | conditioned; ISO 527-1/-2 |
EMS-Grivory Grivory® TSGZ-30 PA666-GF30 Product description: Grilon TSGZ-30 is a heat stabilized, normal viscosity, and impact modified PA66 + PA6 injection molding grade with 30% glass fibers. Grilon TSGZ-30 has the following important p.. |
|||
Tensile Strength at Break | 90.0 MPa | 13100 psi | ISO 527 |
Eurotec® Tecomid® NA40 MR30 NL PA 6.6 30% mineral reinforced Excellent stiffness/toughness balanceHigh mechanical strengthVery good thermal stabilityExcellent flammability characteristicsGood electrical propertiesHigh wear resistance and low frictionVery good.. |
|||
Tensile Strength at Break | 90.0 MPa @Temperature 140 - 150 °C, Time 7.20e+7 sec |
13100 psi @Temperature 284 - 302 °F, Time 20000 hour |
5 [mm/min], 50% Loss of Tensile Strength; ICE 216 |
Akro-Plastic Akroloy® PA GF 30 (2718) PA 6.6 & PA6I/6T Conditioned, 30% Glass Filled One of the most characteristic properties of polyamide (PA 6.6) is the absorption of moisture. This essentially leads to increased toughness and elongation at break, to name the most important param.. |
|||
Tensile Strength at Break | 90.0 MPa @Temperature 80.0 °C |
13100 psi @Temperature 176 °F |
ASTM Test |
BASF Ultramid® 8233G HS BK-102 33% Glass Filled PA6 (Dry) Ultramid 8233G HS BK-102 is a heat stabilized, weather resistant, 33% glass fiber reinforced PA6 injection molding compound offering excellent strength, stiffness, high temperature performance and d.. |
|||
Tensile Strength at Break | 90.0 MPa | 13100 psi | 0.2 in/min; ASTM Test |
BASF Ultramid® 8260 40% Mineral Filled PA6 (Dry) Ultramid 8260 is a 40% mineral reinforced PA6 injection molding compound. It possesses high stiffness, dimensional stability and heat resistance combined with excellent processability including low.. |
|||
Tensile Strength at Break | 90.0 MPa | 13100 psi | Conditioned; ISO R 527 |
Addiplast Addinyl PMD 20090 Nylon 6, 40% Glass Filled Glass fiber reinforced, high resistance to frictionInformation provided by Addiplast. |
|||
Tensile Strength at Break | 90.0 MPa | 13100 psi | 5 mm/min; ISO 527 |
CP-Polymer-Technik Wellamid® 6600/58 GV 30 HWCP 30% Glass Fiber Nylon 66, Impact Modified Until -40°C, Heat Stabilized, Conditioned Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
Tensile Strength at Break | 90.0 MPa | 13100 psi | 5 mm/min; ISO 527 |
Eurostar Staramide BG3ST43 PA6, 15% Glass Fiber Filled, Impact Modified, Injection Molded BG3ST43 is an Impact Modified and Glass Fiber Reinforced, Polyamide 6 Injection Molding ResinInformation provided by Polymer Technology & Services, the North American exclusive supplier. |
|||
Tensile Strength at Break | 90.0 MPa | 13100 psi | ISO 527-1/-2 |
Lanxess Pocan® B 3215 000000 PBT, 10% Glass Fiber PBT, 10% glass fibers, injection molding |