- Polymer Property : Tensile Strength at Break = 82.0 MPa
Polymer Property : Tensile Strength at Break = 82.0 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 82.0 MPa | 11900 psi | ASTM D638 |
| Niche Polymer PPCG40BK Copolymer PP, 40% Glass Fiber Filled Information provided by Niche Polymer |
|||
| Tensile Strength at Break | <= 82.0 MPa | <= 11900 psi | ISO/R527 |
| Polykemi AB SCANMID 6 B11^ FC Nylon 6 Information provided by Polykemi AB |
|||
| Tensile Strength at Break | 82.0 MPa | 11900 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP FARADEX KX98009 Acetal Copolymer (Europe-Africa-Middle East) LNP* FARADEX* KX98009 is a compound based on Acetal Copolymer resin containing Stainless Steel Fiber, Glass Fiber. Added features include : EMI / RFI Shielding, Electrically Conductive. |
|||
| Tensile Strength at Break | 82.0 MPa | 11900 psi | STN EN ISO 527-2 |
| Plastcom SLOVAMID 6 BT LS Polyamide 6, UV Stabilized FeaturesPA 6 for injection moulding with the content of UV stabilizer predetermines products for external use, eg. seats for sport stadiums, covers of electrical appliances. Delivered in natural an.. |
|||
| Tensile Strength at Break | 82.0 MPa | 11900 psi | ISO 527 |
| SABIC Innovative Plastics LNP LUBRICOMP EL003 PEI LNP LUBRICOMP* EL003 is a compound based on Polyetherimide resin containing 15% PTFE. Added features of this material include: Internally Lubricated. |
|||
| Tensile Strength at Break | 82.0 MPa | 11900 psi | ISO 527 |
| SABIC Innovative Plastics LNP LUBRICOMP EL003 PEI (Asia Pacific) LNP LUBRICOMP* EL003 is a compound based on Polyetherimide resin containing PTFE. Added features of this material include: Internally Lubricated. |
|||
| Tensile Strength at Break | 82.0 MPa | 11900 psi | ISO 527 |
| SABIC Innovative Plastics LNP LUBRICOMP EL003 PEI (Europe-Africa-Middle East) LNP LUBRICOMP* EL003 is a compound based on Polyetherimide resin containing PTFE. Added features of this material include: Internally Lubricated. |
|||
| Tensile Strength at Break | 82.0 MPa | 11900 psi | ASTM D 638 |
| SABIC Innovative Plastics LNP Lubricomp KFL22 Acetal Copolymer LNP* Lubricomp* KFL22 is a compound based on Acetal Copolymer resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP f.. |
|||
| Tensile Strength at Break | 82.0 MPa | 11900 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics ULTEM 1285 PEI (Asia Pacific) Transparent Polyetherimide blend. ECO Conforming. US FDA and EU Food Contact compliant in recognized colors. |
|||
| Tensile Strength at Break | 82.0 MPa | 11900 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics ULTEM 4000 PEI Glass fiber, PTFE, and Graphite filled, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 listing. |
|||
| Tensile Strength at Break | 82.0 MPa | 11900 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics ULTEM 4000 PEI (Asia Pacific) Glass fiber, PTFE, and Graphite filled, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 listing. |
|||
| Tensile Strength at Break | 82.0 MPa | 11900 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics ULTEM DU319 PEI Transparent Polyetherimide blend. ECO Conforming. US FDA and EU Food Contact Compliant in recognized colors. |
|||
| Tensile Strength at Break | 82.0 MPa | 11900 psi | Type I, 5 mm/min; ASTM D 638 |
| SABIC Innovative Plastics Ultem HFATX200 PEI+PCE (Asia Pacific) High flow Polyetherimide blend with internal mold release. ECO Conforming.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Tensile Strength at Break | 82.0 MPa | 11900 psi | Type I, 5 mm/min; ASTM D 638 |
| SABIC Innovative Plastics Ultem HTX1010F PEI (Asia Pacific) Higher impact, Polyetherimide (Tg 217C). ECO Conforming. US FDA Food Contact compliant.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Tensile Strength at Break | 82.0 MPa | 11900 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics Valox® 4012 PBT (Europe-Africa-Middle East) VALOX 4012 is a 10% high strength glass fibre reinforced PBT injection moulding resin with improved mechanical properties. Applications: connectors. |
|||
| Tensile Strength at Break | 82.0 MPa | 11900 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics Valox® 732E PBT + PC + PET 30% glass/mineral reinforced, excellent thermal performance, low shrinkage and warp. Easy flow. |
|||
| Tensile Strength at Break | 82.0 MPa | 11900 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP THERMOCOMP AF006 ABS (Europe-Africa-Middle East) LNP* Thermocomp* AF006 is a compound based on Acrylonitrile Butadiene Styrene resin containing Glass Fiber. |
|||
| Tensile Strength at Break | 82.0 MPa | 11900 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP THERMOCOMP AF006XXZ ABS (Europe-Africa-Middle East) LNP* Thermocomp* AF006XXZ is a compound based on Acrylonitrile Butadiene Styrene resin containing Glass Fiber. |
|||
| Tensile Strength at Break | 82.0 MPa | 11900 psi | ASTM D638 |
| SABIC Innovative Plastics LNP THERMOCOMP DX06411 PC (Asia Pacific) LNP* Thermocomp* DX06411 is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Easy Molding, Mold Release. |
|||
| Tensile Strength at Break | 82.0 MPa | 11900 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP STAT-KON AE002 ABS LNP* STAT-KON* AE002 is a compound based on ABS resin containing 10% Carbon Fiber. Added feature of this material is: Electrically Conductive. |
|||
| Tensile Strength at Break | 82.0 MPa | 11900 psi | ASTM D638 |
| SABIC Innovative Plastics LNP THERMOTUF PX06416 PA 6 LNP* Thermotuf* PX06416 is a compound based on Nylon 6 resin containing Glass Fiber. Added features of this material include: High Impact. |
|||
| Tensile Strength at Break | 82.0 MPa | 11900 psi | 5 mm/min; ISO 527 |
| CP-Polymer-Technik Wellamid® 6000 GS 40 HWCP 40% Glass Sphere Filled Nylon 6, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
| Tensile Strength at Break | 82.0 MPa | 11900 psi | 50%RH; ISO 527-1/-2 |
| DuPont Performance Polymers Minlon® 22C NC010 Nylon 66
(Unverified Data**) 38% Mineral/Glass Reinforced Polyamide 66 Minlon 22C NC010 is a 38% mineral/glass reinforced heat stabilized polyamide 66 resin for injection molding.Information provided by DuPont Performance Polym.. |
|||
| Tensile Strength at Break | 82.0 MPa | 11900 psi | ASTM D 638 |
| Cossa Polimeri ESTASAN SAN 0840 GF Styrene Acrylonitrile SAN with 20% glass fiber reinforcementExcellent dimensional stability, good heat resistanceInformation provided by Cossa Polimeri S.r.l. |
|||
| Tensile Strength at Break | 82.0 MPa | 11900 psi | ISO 527 |
| Eurostar Starflam PZ0052E PA6, 25% Glass Filled, Injection Molded PZ0052E is a Halogen Free and Red Phosphorous Free, Flame Retardant, Glass Reinforced, Polyamide 6 Injection Molding (also known as PF1005Z222 or PA625GFUZ22)Information provided by Polymer Technolo.. |
|||
| Tensile Strength at Break | 82.0 MPa @Temperature 80.0 °C |
11900 psi @Temperature 176 °F |
ASTM Test |
| BASF Petra® 330 FR BK-112 30% Glass Filled PET Petra 330 FR BK-112 is a 30% glass reinforced, flame retardant PET, pigmented black injection molding compound rated UL94 V-0 in a 1/64 inch thickness. The product is designed for injection molding.. |
|||
| Tensile Strength at Break | 82.0 MPa | 11900 psi | ASTM D638 |
| SABIC Innovative Plastics LNP THERMOTUF PX06416 PA 6 (Asia Pacific) LNP* Thermotuf* PX06416 is a compound based on Nylon 6 resin containing Glass Fiber. Added features of this material include: High Impact. |
|||
| Tensile Strength at Break | 82.0 MPa | 11900 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics Valox® K4530 PBT 15% glass reinforced PBT, Hydrolytically stable, High flow, Automotive connectors. |
|||