Eurostar Starflam PZ0052E PA6, 25% Glass Filled, Injection Molded

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled
Manufacturer Eurostar Engineering Plastics
Trade Name Starflam
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Eurostar Starflam PZ0052E PA6, 25% Glass Filled, Injection Molded.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PZ0052E is a Halogen Free and Red Phosphorous Free, Flame Retardant, Glass Reinforced, Polyamide 6 Injection Molding (also known as PF1005Z222 or PA625GFUZ22)Information provided by Polymer Technology & Services, the North American exclusive supplier.
Physical Properties Metric English Comments
Density 1.38 g/cc
0.0499 lb/in³
ASTM D792
Moisture Absorption 1.05 %

@Temperature 23.0 °C
1.05 %

@Temperature 73.4 °F
50% RH; ASMT D570
Linear Mold Shrinkage, Flow 0.0040 - 0.0060 cm/cm

@Time 86400 sec
0.0040 - 0.0060 in/in

@Time 24.0 hour
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 82.0 MPa
11900 psi
ISO 527
103 MPa
14900 psi
ASTM D638
Elongation at Break 2.3 %
2.3 %
ASTM D638
2.5 %
2.5 %
ISO 527
Tensile Modulus 6.10 GPa
885 ksi
1 mm/min; ISO 527
7.44 GPa
1080 ksi
50 mm/min; ASTM D638
Flexural Strength 120 MPa
17400 psi
ISO 178
144 MPa
20900 psi
ASTM D790
Flexural Modulus 5.20 GPa
754 ksi
ISO 178
7.10 GPa
1030 ksi
ASTM D790
Izod Impact, Notched 0.530 J/cm
0.993 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 3.00 kJ/m²
1.43 ft-lb/in²
80x10x4; ISO 180/1A
Izod Impact, Unnotched (ISO) 25.0 kJ/m²
11.9 ft-lb/in²
80x10x4; ISO 180/1U
Impact Test 8.00 J
5.90 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
8.00 J
5.90 ft-lb
Multiaxial; ISO 6603
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 32.4 µm/m-°C

@Temperature -40.0 - 40.0 °C
18.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E831
Deflection Temperature at 0.46 MPa (66 psi) 215 °C

@Thickness 3.20 mm
419 °F

@Thickness 0.126 in
unannealed; ASMT D648
Deflection Temperature at 1.8 MPa (264 psi) 137 °C
279 °F
Flatw 80x10x4, sp=64 mm; ISO 75/Af
204 °C

@Thickness 3.20 mm
399 °F

@Thickness 0.126 in
unannealed; ASMT D648
UL RTI, Electrical 125 °C

@Thickness 0.750 mm
257 °F

@Thickness 0.0295 in
125 °C

@Thickness 1.50 mm
257 °F

@Thickness 0.0591 in
125 °C

@Thickness 3.00 mm
257 °F

@Thickness 0.118 in
UL RTI, Mechanical with Impact 125 °C

@Thickness 0.750 mm
257 °F

@Thickness 0.0295 in
125 °C

@Thickness 1.50 mm
257 °F

@Thickness 0.0591 in
125 °C

@Thickness 3.00 mm
257 °F

@Thickness 0.118 in
UL RTI, Mechanical without Impact 130 °C

@Thickness 0.750 mm
266 °F

@Thickness 0.0295 in
130 °C

@Thickness 1.50 mm
266 °F

@Thickness 0.0591 in
140 °C

@Thickness 3.00 mm
284 °F

@Thickness 0.118 in
Flammability, UL94 V-2

@Thickness 0.750 mm
V-2

@Thickness 0.0295 in
IEC 60695-11-10
V-2

@Thickness 1.50 mm
V-2

@Thickness 0.0591 in
IEC 60695-11-10
V-2

@Thickness 3.00 mm
V-2

@Thickness 0.118 in
IEC 60695-11-10
Oxygen Index >= 20 %
>= 20 %
ISO 4589
Glow Wire Test 960 °C

@Thickness 1.60 mm
1760 °F

@Thickness 0.0630 in
IEC 60695-2-12
Electrical Properties Metric English Comments
Comparative Tracking Index 400 - 600 V
400 - 600 V
PLC 1
Hot Wire Ignition, HWI 30 - 60 sec

@Thickness 0.750 mm
30 - 60 sec

@Thickness 0.0295 in
PLC 2
30 - 60 sec

@Thickness 1.50 mm
30 - 60 sec

@Thickness 0.0591 in
PLC 2
30 - 60 sec

@Thickness 3.00 mm
30 - 60 sec

@Thickness 0.118 in
PLC 2
High Amp Arc Ignition, HAI >= 120 arcs

@Thickness 0.750 mm
>= 120 arcs

@Thickness 0.0295 in
PLC 0
>= 120 arcs

@Thickness 1.50 mm
>= 120 arcs

@Thickness 0.0591 in
PLC 0
>= 120 arcs

@Thickness 3.00 mm
>= 120 arcs

@Thickness 0.118 in
PLC 0
Processing Properties Metric English Comments
Rear Barrel Temperature 240 - 250 °C
464 - 482 °F
Zone 1
Middle Barrel Temperature 250 - 260 °C
482 - 500 °F
Zone 2
Front Barrel Temperature 250 - 270 °C
482 - 518 °F
Zone 3
Melt Temperature 250 - 270 °C
482 - 518 °F
Mold Temperature 50.0 - 90.0 °C
122 - 194 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 4.00 hour
4.00 hour
Moisture Content 0.20 %
0.20 %
Descriptive Properties Value Comments
UL f1 f1