Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength, Yield 31.0 - 42.7 MPa
4500 - 6200 psi
Average value: 37.3 MPa Grade Count:22
Overview of materials for Acrylonitrile Butadiene Styrene (ABS), Sheet
This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), Sheet". Each property range of values reported is minimum and max..
Tensile Strength, Yield 31.0 MPa
4500 psi
LyondellBasell Lupolen® 6031 M HDPE, Injection Molding Grade
Easy flow, injection molding grade for fruit crates, tote boxes and bottle crates, cartridges, protective headgear, buckets, dishes, cartridges for adhesive film canisters, aerosol lids, child seats..
Tensile Strength, Yield 31.0 MPa

@Temperature 22.0 °C
4500 psi

@Temperature 71.6 °F
25mm flat samples, compression moulded; ISO 527-4
Menzolit Menzolit® BMC 2500 Unsaturated Polyester UP
BMC 2500 is a special BMC for high voltage isolating applications. The glass content is set to a level that combines good mouldability with good strength and stiffness properties. The fire retardanc..
Tensile Strength, Yield 31.0 MPa
4500 psi
2 in/min (50 mm/min); ASTM D-638
Ineos A60-70-162 HDPE
Ineos A60-70-162 is a high density polyethylene homopolymer, developed specifically for blow molding food containers on reciprocating screw-type equipment. It exhibits excellent processing character..
Tensile Strength, Yield 31.0 MPa
4500 psi
50 mm/min; ISO 527-1,-2
Inno-Comp INNOPOL® CS 1-4140 BAP 40% Talc-Filled Polypropylene Homopolymer
INNOPOL® CS 1-4140 B AP is a 40% talc-filled polypropylene homopolymer compound /PP-H TD40 (ISO 1043)/.INNOPOL® CS 1-4140 B AP is recommended especially for producing products, where high stif..
Tensile Strength, Yield 31.0 MPa
4500 psi
50 mm/min; ISO 527-1,-2
Inno-Comp INNOPOL® CS 1-5120 BLH 20% Talc-Filled Polypropylene Homopolymer
INNOPOL® CS 1-5120 BLH is a 20% talc-filled polypropylene homopolymer compound /PP-H TD20 (ISO 1043)/.INNOPOL® CS 1-5120 BLH is recommended especially for producing products, where high stiffn..
Tensile Strength, Yield 31.0 MPa

@Temperature 22.0 °C
4500 psi

@Temperature 71.6 °F
25mm flat samples, compression moulded; ISO 527-4
Menzolit Menzolit® BMC 2300 Unsaturated Polyester UP
BMC 2300 is a special BMC with exceptional high fire retardancy. The glass content is set to a level that provides sufficient mouldability with high strength and stiffness properties. Fire retardanc..
Tensile Strength, Yield 31.0 MPa
4500 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP ML004 PP
LNP* LUBRICOMP* ML004 is a product based on Polypropylene containing 20% PTFE. Added features of this grade include: Wear Resistant.
Tensile Strength, Yield 31.0 MPa
4500 psi
50 mm/min; ISO 527
SABIC Innovative Plastics Xenoy® EXXY0113 PBT (Europe-Africa-Middle East)
Blow Moldable Impact modified XENOYThis data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Tensile Strength, Yield 31.0 MPa
4500 psi
ASTM D638
SABIC Innovative Plastics LNP STAT-LOY A3000T ABS (Asia Pacific)
LNP* Stat-loy* A3000T is a compound based on Acrylonitrile Butadiene Styrene resin containing Anti-Static. Added features of this material include: Antistat.
Tensile Strength, Yield 31.0 MPa
4500 psi
ASTM D638
Shuman 510 Black Polypropylene Homopolymer
Excellent chemical resistance, excellent processabilityData provided by the manufacturer.
Tensile Strength, Yield 31.0 MPa
4500 psi
ASTM D638
Techmer ES HiFill® TPU 0266 A
Availability: North AmericaForms: PelletsFeatures: High Density and High Specific GravityInformation provided by TP Composites, Inc.
Tensile Strength, Yield 31.0 MPa
4500 psi
ASTM D638
Techmer ES Plastiblend® ABS 8010
Availability: North AmericaForms: PelletsProcessing Method: Extrusion Blow Molding and Sheet ExtrusionInformation provided by TP Composites, Inc.
Tensile Strength, Yield 31.0 MPa
4500 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP WH0270F PBT
LNP* Thermocomp* WH0270F is a dense compound based on PBT.
Tensile Strength, Yield 31.0 MPa
4500 psi
ASTM D638
A. Schulman POLYFORT™ FXP 1943 CaC03 and Glass Fiber Hybrid Copolymer Polypropylene
DescriptionPolyfort® FXP 1943 is a 20% CAC03 and glass fiber hybrid copolymer polypropylene product. Information provided by A. Schulman.
Tensile Strength, Yield 31.0 MPa
4500 psi
ASTM D638
A. Schulman POLYFORT™ FPP 892E Extrusion and Blow Molding Grade Homopolymer Polypropylene
DescriptionPolyfort® FPP 892E is an extrusion and blow molding grade 20% mineral-filled homopolymer polypropylene.Information provided by A. Schulman.
Tensile Strength, Yield 31.0 MPa
4500 psi
50 cm/min; ASTM D638
Washington Penn PPH2TF-2B Polypropylene, 20% Talc Filled
Injection Molding Grade. Heat Stabilized. Meets Ford ESH-M4D293-B Spec.Applications: AC Blower wheels, parts and appliances.Data provided by Washington Penn Plastic Co., Inc.
Tensile Strength, Yield 31.0 MPa
4500 psi
ISO 527-2
Tisan TISOPLEN® 30% Talc Filled Heat Stabilized Homopolymer Polypropylene
TISOPLEN has a wide area of application in furniture, durable goods, household appliances, electrics/electronics, and telecommunication industries. General specifications include Low densityLow mois..
Tensile Strength, Yield 31.0 MPa
4500 psi
ISO 572-2
Total Lumicene® MR110MC2 Metallocene Random Copolymer Polypropylene, Injection Molding
Lumicene® MR110MC2 is a metallocene random copolymer with a melt flow index of 110 g/10 min for injection molding. This Lumicene® MR110MC2 high fluidity differs from standard random copolymers by ..
Tensile Strength, Yield 31.0 MPa
4500 psi
ASTM D638
A. Schulman PP 3479-01 Polypropylene Random Copolymer
DescriptionPolypropylene PP 3479-01 is a polypropylene random copolymer produced utilizing unique catalyst and processing technology. It was designed for injection molding and stretch blow molding ..
Tensile Strength, Yield 31.0 MPa
4500 psi
ASTM D638
A. Schulman POLYFORT™ FXP 1943 CaC03 and Glass Fiber Hybrid Copolymer Polypropylene
DescriptionPolyfort® FXP 1943 is a 20% CAC03 and glass fiber hybrid copolymer polypropylene product. Information provided by A. Schulman.
Tensile Strength, Yield 31.0 MPa
4500 psi
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 45 PHR Mistron Vapor Filler
MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje..
Tensile Strength, Yield 31.0 MPa
4500 psi
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with Benzoflex T-150 Plasticizer
MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje..
Tensile Strength, Yield 31.0 MPa
4500 psi
2 in/min, Type IV bar; ASTM D638
Chevron Phillips Marlex® K608 HDPE Extrusion Molding Resin
Resin Type: Ethylene HomopolymerCharacteristics: Good ESCRExceptional RigidityExcellent melt strengthGood whiteness in unpigmented partsApplications: Table topsNursery containersDunnage traysLarge t..
Tensile Strength, Yield 31.0 MPa

@Temperature 23.0 °C
4500 psi

@Temperature 73.4 °F
DAM; ISO 527
DuPont Performance Polymers Zytel® ST811HS NC010 Nylon 6  (Unverified Data**)
Zytel® ST811HS is a flexible, heat stabilized Super Tough polyamide 6 resin developed for extrusion and injection molding applications such as cable and rope jacketing, hose inner cores and fastene..
Tensile Strength, Yield 31.0 MPa
4500 psi
BASF Procom® X25H 650 Polypropylene
Electrical and domestic appliances, housings where high gloss is required.Data was collected by ISO methods and provided by BASF.
Tensile Strength, Yield 31.0 MPa
4500 psi
ASTM D638
Asahi Kasei Thermofil P-20TC-5103 20% Talc Reinforced, Lubricated, Heat Stabilized
Information provided by Asahi Thermofil
Tensile Strength, Yield 31.0 MPa
4500 psi
TSE Industries Millathane® CM Millable Polyether Urethane Rubber, 0.75 PHR Sulfur
MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje..
Tensile Strength, Yield 31.0 MPa
4500 psi
2" per min, Type IV; ASTM D638
Amco PRIMATOP HDPE 006964EG Pipe Extrusion Polyethylene
HDPE 006964 features high quality for critical food packaging requirements and excellent stiffness. Applications include milk, water, and juice packaging.Former A-Top Polymers product; part of Amco ..
Tensile Strength, Yield 31.0 - 40.8 MPa
4500 - 5920 psi
Average value: 34.7 MPa Grade Count:8
Overview of materials for ABS/PVC Alloy
This property data is a summary of similar materials in the MatWeb database for the category "ABS/PVC Alloy". Each property range of values reported is minimum and maximum values of appropriate MatW..