Polymer Property : Tensile Strength, Yield = 49.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	49.0 MPa	7110 psi	Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics Cycolac® X17 ABS Automotive: Very high heat resistance with high strength and modulus. UL94 HB rated.This data was supplied by SABIC-IP for the Americas region.
Tensile Strength, Yield	49.0 MPa	7100 psi	ASTM D638
Polymer Resources TP-FV699 PBT, 10% Glass Reinforced Structural Foam Grade, Low Shrinkage Process: Foam MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Foam grades tested with foamed parts with a 10% weight reduction rel..
Tensile Strength, Yield	49.0 - 100 MPa	7100 - 14500 psi	Average value: 76.6 MPa Grade Count:32
Overview of materials for Polybutylene Terephthalate (PBT), 10% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), 10% Glass Fiber Filled".Specific grades with glass content between 5% ..
Tensile Strength, Yield	49.0 MPa @Temperature 150 °C	7110 psi @Temperature 302 °F	ISO 527
Solvay Specialty Polymers Amodel® A-1340 HS Polyphthalamide (PPA) Resin, 40% Mineral/Glass Reinforced, Dry as Molded &a AMODEL® A-1340 HS is a 40% mineral/glass reinforced, heat stabilized polyphthalamide (PPA) which exhibits a high deflection temperature, high flexural modulus, high tensile strength and low warpage..
Tensile Strength, Yield	49.0 MPa	7100 psi	ASTM D638
Total 680 Polystyrene (discontinued **) Polystyrene 680 is a medium impact polystyrene developed for the foam extrusion and laminate markets. This polymers impact qualities in conjunction with its high flexural strength allow 680 to be ex..
Tensile Strength, Yield	49.0 MPa	7110 psi
Ineos ABS Lustran® QE 1455/L2, Injection Grade (discontinued **) Injection molding grade, increased heat resistance, medium gloss, UV-stabilized grade.Applications: Automotive: body parts.Information provided by Bayer.LANXESS was spun-off from Bayer in early 2005..
Tensile Strength, Yield	49.0 MPa @Thickness 3.20 mm	7110 psi @Thickness 0.126 in	50mm/min; ASTM D638
LG Chemical LUMID GP1300AP PA6, Plasticized Feature: Injection Molding, PA6, PlasticizedApplication: Automotive PartsInformation provided by LG Chemical
Tensile Strength, Yield	49.0 MPa @Thickness 3.20 mm	7110 psi @Thickness 0.126 in	50mm/min; ASTM D638
LG Chemical LUMIPLAS LD590T Light diffusion ABS Description: Extrusion, Light diffusion, High ImpactApplication: (LED) Lamp Cover, Signboard Lighting Decoration of Electronic DeviceCAS No. 9010-94-0Information provided by LG Chemical
Tensile Strength, Yield	49.0 MPa @Thickness 3.20 mm	7110 psi @Thickness 0.126 in	50 mm/min; ASTM D638
LG Chemical XR401 ABS, Heat Resistance Feature: Injection Molding, Heat ResistanceApplication: Electric & Electronic Housing (Frame etc) Automotives Interior & Exterior Housing (lamp housing etc)CAS No. 25120-20-1, 9003-56-9, 25747-74-7 ..
Tensile Strength, Yield	49.0 MPa	7110 psi	ASTM D638
SABIC Innovative Plastics LNP LUBRILOY D2000I PC LNP* LUBRILOY* D2000I is a compound based on Polycarbonate resin containing Proprietary Lubricant. Added features of this material include: Wear Resistant, High Impact.
Tensile Strength, Yield	49.0 MPa	7110 psi	50 mm/min; ISO 527
SABIC Innovative Plastics XenoyÂ® IQ1103 PBT+PC Xenoy iQ1103 resin - Environmentally responsible and sustainable low carbon footprint resin. Xenoy iQ1103 is an unreinforced, impact modified alloy of PC (polycarbonate) + Valox iQ PBT (polybuty..
Tensile Strength, Yield	49.0 MPa	7110 psi	50 mm/min; ISO 527
SABIC Innovative Plastics XenoyÂ® IQ1103 PBT+PC (Asia Pacific) Xenoy iQ1103 resin - Environmentally responsible and sustainable low carbon footprint resin. Xenoy iQ1103 is an unreinforced, impact modified alloy of PC (polycarbonate) + Valox iQ PBT (polybuty..
Tensile Strength, Yield	49.0 MPa	7110 psi	50 mm/min; ISO 527
SABIC Innovative Plastics XenoyÂ® IQ1103R PBT+PC (Asia Pacific) Xenoy* Resin iQ1103R - Environmetally responsible, sustainable, and low carbon footprint resin. Xenoy iQ1103R is an unreinforced, impact modified PC + iQ-PBT alloy with excellent low temperature im..
Tensile Strength, Yield	49.0 MPa	7110 psi	50 mm/min; ISO 527
SABIC Innovative Plastics XenoyÂ® IQ1103U PBT+PC Xenoy* Resin iQ1103U - Environmetally responsible, sustainable, and low carbon footprint resin. Xenoy iQ1103U is an unreinforced, UV stable, impact modified PC+ iQ-PBT alloy with excellent low temp..
Tensile Strength, Yield	49.0 MPa	7110 psi	Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics XYLEX X7300CL PC+POLYESTER (Europe-Africa-Middle East) PC+ POLYESTER unreinforced alloy developed for optical or lense market. Chemical resistance.
Tensile Strength, Yield	49.0 MPa	7110 psi	Type I, 50 mm/min; ASTM D 638
SABIC Innovative Plastics Xylex X7300OQ PC+POLYESTER (Asia Pacific) PC+ POLYESTER unreinforced alloy developed for optical or lense market. High flow with good impact and excellent optical quality.This data was supplied by SABIC-IP for the Asia Pacific region.
Tensile Strength, Yield	49.0 MPa	7110 psi	51 mm/min; ASTM D638
Styron MAGNUMâ„¢ 375 HH Acrylonitrile Butadiene Styrene (ABS) Resin Overview: High Heat, Low Gloss, Medium Impact ABS resin for injection moldingApplications: Automotive interior trim applications requiring low volatile organic compounds (VOC)Information provided by..
Tensile Strength, Yield	49.0 MPa	7110 psi	ISO 527-1/-2
Covestro Bayblend® T45 PG Polycarbonate + ABS General purpose injection molding gradeVicat/B 120 temperature = 112 °Cfor electroplating applicationsPreprocessingMax. Water content
Tensile Strength, Yield	49.0 MPa	7100 psi	ASTM D792
Clariant Renol PURSP0005 Polyurethane Elastomer, Glass Fiber Reinforced Data provided by Clariant Masterbatches
Tensile Strength, Yield	49.0 MPa	7110 psi	23°C, 50% RH; ASTM D638
Asahi Kasei Xyron® 240V Modified Polyphenylene Ether Flame RetardantInformation provided by Asahi Kasei
Tensile Strength, Yield	49.0 MPa @Thickness 3.20 mm	7110 psi @Thickness 0.126 in	Type I, 5 mm/min; ASTM D638
Bhansali Engineering Abstron TIM 200 MMA- ABS High Impact(Transparent ABS)Information provided by Bhansali
Tensile Strength, Yield	49.0 MPa	7100 psi	ASTM D-638
Axiall 3152 Rigid PVC, Extrusion Georgia Gulf 3152 is a twin screw powder blend NSF approved for the extrusion of potable water and drain waste and vent pipe application.Information provided by Georgia GulfGeorgia Gulf became Axial..
Tensile Strength, Yield	49.0 MPa	7110 psi	ASTM D638
Ashley Polymers Ashlene® L925 Nylon 12 A flexible Nylon 12 with exceptional toughness, excellent abrasion and chemical resistance, outstanding low temperature performance, dimensional stability and low moisture absorption. The natural c..
Tensile Strength, Yield	49.0 MPa	7100 psi	ASTM D638
Polymer Resources PPX-FR2 Modified PPO, UL 94 V-1 with HDT of 210 F (Unverified Data**) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.
Tensile Strength, Yield	49.0 - 227 MPa	7100 - 32900 psi	Average value: 137 MPa Grade Count:11
Overview of materials for Thermoplastic Polyurethane (TPUR), Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Thermoplastic Polyurethane (TPUR), Glass Fiber Reinforced". Each property range of values reported is mi..
Tensile Strength, Yield	49.0 MPa	7110 psi	50 mm/min; ISO 527
SABIC Innovative Plastics XYLEX FXY330DF PC+POLYESTER (Asia Pacific) Polyester+PC alloy. Diffusion Effect. Color package may affect performance.
Tensile Strength, Yield	49.0 MPa @Thickness 3.20 mm	7110 psi @Thickness 0.126 in	50 mm/min; ASTM D638
LG Chemical XG570 MABS, Anti-Scratch, High Impact, High Flow Feature: Injection Molding, Anti-Scratch, High Impact, High FlowApplication: LCD TV Stand Base, Audio/Video HousingCAS No. 9010-94-0Information provided by LG Chemical
Tensile Strength, Yield	49.0 MPa @Thickness 3.20 mm	7110 psi @Thickness 0.126 in	Type I, 5 mm/min; ASTM D638
Bhansali Engineering Abstron HI40H ABS Injection Molding Grade Automotive applications -Medium Impact, Super High Rigidity, PaintableInformation provided by Bhansali
Tensile Strength, Yield	49.0 MPa @Thickness 3.20 mm	7110 psi @Thickness 0.126 in	Type I, 5 mm/min; ASTM D638
Bhansali Engineering Abstron IPM3000 PMMA- ABS Alloy Super High Gloss, High scratch resistanceInformation provided by Bhansali