Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 35.0 - 93.2 MPa | 5080 - 13500 psi | Average value: 67.7 MPa Grade Count:49 |
Overview of materials for Acrylonitrile Butadiene Styrene (ABS), 20% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), 20% Glass Fiber Filled". Specific grades with glass content betwe.. |
|||
Tensile Strength, Ultimate | 35.0 - 45.0 MPa | 5080 - 6530 psi | ASTM D638 |
Solvay Specialty Polymers Hylar® MP10 PVDF Polyvinylidene Fluoride
(discontinued **) Data provided by the manufacturer.Hylar® polymers have the characteristic stability of fluoropolymers combined with a unique polarity that influences its solubility and electrical properties. In a.. |
|||
Tensile Strength, Ultimate | 35.0 - 35.0 MPa @Temperature 32.0 - 32.0 °C |
5080 - 5080 psi @Temperature 89.6 - 89.6 °F |
Average value: 35.0 MPa Grade Count:1 |
Overview of materials for High Density Polyethylene (HDPE), Ultra High Molecular Weight This property data is a summary of similar materials in the MatWeb database for the category "High Density Polyethylene (HDPE), Ultra High Molecular Weight". Each property range of values reported i.. |
|||
Tensile Strength, Ultimate | 35.0 - 70.0 MPa @Temperature 60.0 - 150 °C |
5080 - 10200 psi @Temperature 140 - 302 °F |
Average value: 53.8 MPa Grade Count:1 |
Overview of materials for Nylon 66, 10% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 10% Glass Fiber Filled". Specific grades with glass content between 5% and 14% are included. .. |
|||
Tensile Strength, Ultimate | 35.0 - 235 MPa @Temperature -40.0 - 150 °C |
5080 - 34100 psi @Temperature -40.0 - 302 °F |
Average value: 88.6 MPa Grade Count:14 |
Overview of materials for Nylon 66, 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% are included. .. |
|||
Tensile Strength, Ultimate | 35.0 MPa | 5080 psi | 2 in/min, at max load; ASTM D638 |
A. Schulman POLYPUR™ FPU 1117 Thermoplastic Polyurethane Compound Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 35.0 MPa | 5080 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 131E Adhesive, Extrusion Grade DescriptionFormion® FI 131E is an adhesive grade extrusion product. It has been formulated to provide adhesion as a tie layer or resin modifier to bond Ionomer to polar and non polar substances, s.. |
|||
Tensile Strength, Ultimate | 35.0 MPa | 5080 psi | 2 in/min, at max load; ASTM D638 |
A. Schulman POLYPUR™ FPU 1117 Thermoplastic Polyurethane Compound Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 35.0 MPa | 5080 psi | 2 in/min, at max load; ASTM D638 |
A. Schulman POLYPUR™ FPU 1117 Thermoplastic Polyurethane Compound Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 35.0 MPa | 5080 psi | 2 in/min, at max load; ASTM D638 |
A. Schulman POLYPUR™ FPU 1117 Thermoplastic Polyurethane Compound Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 35.0 MPa | 5080 psi | at max load; ASTM D638 |
A. Schulman POLYPUR™ FPU 1376 Thermoplastic Polyurethane Compound Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 35.0 MPa | 5080 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 131E Adhesive, Extrusion Grade DescriptionFormion® FI 131E is an adhesive grade extrusion product. It has been formulated to provide adhesion as a tie layer or resin modifier to bond Ionomer to polar and non polar substances, s.. |
|||
Tensile Strength, Ultimate | 35.0 MPa | 5080 psi | ISO 37 |
Lubrizol ESTANE® GP80AB Ester Based Thermoplastic Polyurethane Type: Estane® GP 80AB is an aromatic polyester-based thermoplastic polyurethane (TPU).Appearance: Translucent spherical pelletsUses: Injection molding partsAvailable in EuropeInformation provided b.. |
|||
Tensile Strength, Ultimate | 35.0 MPa | 5080 psi | ISO 37 |
Lubrizol ESTANE® GP85AB Ester Based Thermoplastic Polyurethane Type: Estane® GP 85AB is an aromatic polyester-based thermoplastic polyurethane (TPU).Appearance: Translucent spherical pelletsUses: Injection molding partsInformation provided by Lubrizol. |
|||
Tensile Strength, Ultimate | 35.0 MPa | 5080 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 131E Adhesive, Extrusion Grade DescriptionFormion® FI 131E is an adhesive grade extrusion product. It has been formulated to provide adhesion as a tie layer or resin modifier to bond Ionomer to polar and non polar substances, s.. |
|||
Tensile Strength, Ultimate | 35.0 MPa | 5080 psi | butt tensile strength per ASTM D426 on brass |
Von Roll Isola IMI E-Solder® 3012 Electrically Conductive Adhesive Data provided by Von Roll Isola USA.E-SOLDER® epoxy based resin systems can be used at room temperature on heat sensitive materials, can bond dissimilar materials, and do not have flux or residue t.. |
|||
Tensile Strength, Ultimate | 35.0 MPa | 5080 psi | ISO 527-1 |
Chengdu Polyster H605 Thermoplastic Polyether-ester Elastomer (TPEE) Medium modulus molding and injection grade. Contains improved color- stable antioxidants. Excellent tear resistance. Molded and injected products for consumer use, such as airbag door covers, railwa.. |
|||
Tensile Strength, Ultimate | 35.0 MPa | 5080 psi | ASTM D638/D412 |
Covestro Bayflex® 180 Polyurethane Elastomeric RIM, 20% Mica Filled, MDI-based 2-Component Liquid System 0.150 in. thickness. RIM = Reaction Injection MoldingInformation provided by Bayer Corporation, Polyurethanes DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and .. |
|||
Tensile Strength, Ultimate | 35.0 MPa | 5080 psi | ASTM D638 |
Equate EMDA-6147 HDPE Blow Molding Resin EMDA-6147 is a high density polyethylene copolymer resin designed for blow molding of large size containers. Its high molecular weight and broad molecular weight distribution with a balanced density.. |
|||
Tensile Strength, Ultimate | 35.0 MPa | 5080 psi | ISO 527-1 |
Dow BETAMATE™ XW 1044-3 Epoxy BETAMATE™ XW 1044-3 is a one component, epoxy based adhesive especially developed for the body shop. The adhesive can be applied by robot systems and it shows high adhesion to metal and non-metal .. |
|||
Tensile Strength, Ultimate | 35.0 MPa | 5080 psi | ASTM D638 |
3D Systems DuraForm® AF Nylon for SLS® Systems Polyamide (nylon) material with metallic appearance for real-world physical testing and functional use. For use with all selective laser sintering SLS® systems.ApplicationsHousings and enclosuresCo.. |
|||
Tensile Strength, Ultimate | 35.0 MPa | 5080 psi | ASTM D638 |
Chem Polymer Durlex 709 IH PBT, Impact Modified A highly impact modified PBT exhibiting excellent toughness and processability.Data provided by the manufacturer, Chem Polymer. |
|||
Tensile Strength, Ultimate | 35.0 - 50.0 MPa | 5080 - 7250 psi | 50 mm/min; ASTM D638 |
Solvay Specialty Polymers Solef® 1009 PVDF Homopolymer
(discontinued **) Key features of this grade: Mean Viscosity, All Purpose, Injection/Extrusion, Virgin. Recommended processing is extrusion. Available as powder & granules.General information about SOLEF® PVDF: SO.. |
|||
Tensile Strength, Ultimate | 35.0 - 50.0 MPa | 5080 - 7250 psi | 50 mm/min; ASTM D638 |
Solvay Specialty Polymers Solef® 1012 PVDF Homopolymer
(discontinued **) Key features of this grade: High Viscosity, Virgin. Recommended processing is extrusion. Available as powder & granules.General information about SOLEF® PVDF: SOLEF® PVDF is a fluorinated semi-c.. |
|||
Tensile Strength, Ultimate | 35.0 MPa @Temperature 816 °C |
5080 psi @Temperature 1500 °F |
|
AK Steel 439 ULTRA FORM® Stainless Steel AK Steel 439 ULTRA FORM™ was developed for applications requiring oxidation and corrosion resistance superior to Type 409 as well as superior formability to AK Steel 439 Stainless Steel. As a resul.. |
|||
Tensile Strength, Ultimate | 35.0 MPa | 5080 psi | DIN 53504 |
Lubrizol ESTANE® 58214 Ether Based Thermoplastic Polyurethane (European Grade) Description: Estane® thermoplastic polyurethanes (TPUs) include elastomeric materials that bridge the gap between flexible rubber and rigid plastics. These materials offer toughness and durability .. |
|||
Tensile Strength, Ultimate | 35.0 - 100 MPa @Temperature -40.0 - 70.0 °C |
5080 - 14500 psi @Temperature -40.0 - 158 °F |
Average value: 67.5 MPa Grade Count:4 |
Overview of materials for Acrylic, Extruded This property data is a summary of similar materials in the MatWeb database for the category "Acrylic, Extruded". Each property range of values reported is minimum and maximum values of appropriate .. |
|||
Tensile Strength, Ultimate | 35.0 - 55.0 MPa @Temperature 60.0 - 120 °C |
5080 - 7980 psi @Temperature 140 - 248 °F |
Average value: 43.3 MPa Grade Count:1 |
Overview of materials for Polybutylene Terephthalate (PBT), Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Mineral Filled". Each property range of values reported is minimum and.. |
|||
Tensile Strength, Ultimate | 35.0 MPa | 5080 psi | ISO R527 |
Arkema Group Orgalloy® LT 5050 ES Polyamide Alloy Polyamide Alloy, Blow Molding of Technical PartsInformation provided by Arkema Group |