A. Schulman POLYPUR™ FPU 1376 Thermoplastic Polyurethane Compound

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Molded , Polyurethane, TP
Manufacturer A. Schulman, Inc.
Trade Name POLYPUR™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF A. Schulman POLYPUR™ FPU 1376 Thermoplastic Polyurethane Compound.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by A. Schulman.
Physical Properties Metric English Comments
Specific Gravity 1.29 g/cc
1.29 g/cc
ASTM D792
Linear Mold Shrinkage 0.0010 - 0.0030 cm/cm

@Thickness 3.20 mm
0.0010 - 0.0030 in/in

@Thickness 0.126 in
48 hr, at 80 and 121°C; ASTM D955
0.0010 - 0.0030 cm/cm

@Thickness 3.20 mm
0.0010 - 0.0030 in/in

@Thickness 0.126 in
72 hr; ASTM D955
0.0020 - 0.0040 cm/cm

@Thickness 3.20 mm
0.0020 - 0.0040 in/in

@Thickness 0.126 in
48 hr at 121°C; ASTM D955
Mechanical Properties Metric English Comments
Hardness, Shore D 65
65
15 sec delay; ASTM D2240
Tensile Strength, Ultimate 35.0 MPa
5080 psi
at max load; ASTM D638
Elongation at Break 30 %
30 %
ASTM D412
Flexural Modulus 0.900 GPa
131 ksi
at 70°C, tangent
1.40 GPa
203 ksi
tangent; ASTM D790
Izod Impact, Notched 2.00 J/cm
3.75 ft-lb/in
ASTM D256
Falling Dart Impact 6.01 J
4.43 ft-lb
at -30°C; ASTM D3029
Tear Strength 110 kN/m
628 pli
ASTM D624
Thermal Properties Metric English Comments
CTE, linear 27.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
15.0 µin/in-°F

@Temperature -22.0 - 86.0 °F
2.7 mm/mm; ASTM D696
Melting Point 220 °C
428 °F
by DSC, 10°C per 220 minutes
Deflection Temperature at 0.46 MPa (66 psi) 90.0 °C

@Thickness 3.20 mm
194 °F

@Thickness 0.126 in
ASTM D648
Descriptive Properties Value Comments
Heat Sag 15 mm
ASTM D3769, 1 hr, at 121°C