Polymer Property : Flexural Modulus = 8.00 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Modulus	6.00 - 8.00 GPa	870 - 1160 ksi	Compression; ISO 178
Raschig Group AMPLA® 2000 melamine-modified polyester Halogen-free, organically and inorganically filled melamine-modified Polyester molding compound. Low post-shrinkage, very good electrical values, high heat resistance, very good sliding behavior, ve..
Flexural Modulus	6.00 - 8.00 GPa	870 - 1160 ksi	Injection; ISO 178
Raschig Group AMPLA® 2500 melamine-modified polyester Halogen-free, organically and inorganically filled melamine-modified Polyester molding compound. Excellent elasticity and shock resistance, low post-shrinkage, very good electrical values, high heat..
Flexural Modulus	7.00 - 8.00 GPa	1020 - 1160 ksi	Injection and Compression; ISO 178
Raschig Group AMPLA® 7250 melamine-modified polyester Cellulose reinforced melamine-modified Polyester molding compound. Very good electrical values, excellent heat resistance, excellent surface quality, low post shrinkage. This product meets the allow..
Flexural Modulus	6.00 - 8.00 GPa	870 - 1160 ksi	Injection and Compression; ISO 178
Raschig Group AMPLA® 7500 melamine-modified polyester Organically and inorganically filled melamine modified Polyester molding compound. Low post-shrinkage, very good electrical values, excellent heat resistance, very good sliding behavior and wear sta..
Flexural Modulus	6.00 - 8.00 GPa	870 - 1160 ksi	Injection; ISO 178
Raschig Group DECAL® 2061 Phenolic Wood flour reinforced phenolic molding compound. Good electrical properties, chemical resistance and mechanical properties. This product meets the allowed upper limits for heavy metals and PCAs and ..
Flexural Modulus	6.00 - 8.00 GPa	870 - 1160 ksi	Injection and Compression; ISO 178
Raschig Group DECAL® 5431 Phenolic Organically and inorganically filled phenolic molding compound. This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/..
Flexural Modulus	6.00 - 8.00 GPa	870 - 1160 ksi	Injection; ISO 178
Raschig Group MELOPAS® 6605 MP Melamine Cellulose reinforced Melamine molding compound. Very good electrical properties, excellent surface hardness, good mechanical strength and heat resistance, good wear and UV-stability, good gliding be..
Flexural Modulus	5.00 - 8.00 GPa	725 - 1160 ksi	Injection and Compression; ISO 178
Raschig Group MELOPLAS® 2500 MF Cellulose-reinforced MF molding compound in white and colored shades. Very good electrical properties, high surface hardness, good abrasion- and UV-stability, very good resistance to chemicals - al..
Flexural Modulus	1.29 - 8.00 GPa	186 - 1160 ksi	Average value: 5.61 GPa Grade Count:3
Overview of materials for PCT, 40% Glass Reinforced This property data is a summary of similar materials in the MatWeb database for the category "PCT, 40% Glass Reinforced". Specific grades with glass content between 35% and 44% are included. Each pr..
Flexural Modulus	2.00 - 8.00 GPa	290 - 1160 ksi	Average value: 5.22 GPa Grade Count:112
Overview of materials for Polycarbonate, 20% Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, 20% Glass Filled". Specific grades with glass content between 15% and 24% are included. E..
Flexural Modulus	0.800 - 8.00 GPa @Temperature -40.0 - 120 °C	116 - 1160 ksi @Temperature -40.0 - 248 °F	Average value: 2.65 GPa Grade Count:4
Overview of materials for Nylon 6, 30% Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 30% Mineral Filled". Specific grades with primary filler content between 25% and 34% are includ..
Flexural Modulus	3.45 - 8.00 GPa	500 - 1160 ksi	Average value: 4.59 GPa Grade Count:12
Overview of materials for Nylon 12, 20% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 12, 20% Glass Fiber Filled". Specific grades with glass content between 15% and 24% are included. ..
Flexural Modulus	6.50 - 8.00 GPa	943 - 1160 ksi	ISO 178
Vyncolit 2530 W Novolac Phenolic Mineral and organic filled phenolic molding compound with excellent thermal properties.USES: Lamp sockets, special lamp holders, pan handles and knobs.Information provided by Vyncolit, a Sumitomo Ba..
Flexural Modulus	6.00 - 8.00 GPa	870 - 1160 ksi	ISO 178
Vyncolit 2723 W Novolac Phenolic Mineral and organic filled phenolic molding compound with excellent mechanical, thermal and dielectric properties. I2/FO classified under NF F 16-101 (Fire & Smoke classification).USES: Circuit bre..
Flexural Modulus	6.00 - 8.00 GPa	870 - 1160 ksi	ISO 178
Vyncolit 2920 W Novolac Phenolic Mineral and organic filled molding compound with good dimensional stability and heat resistance.USES: Carburettor and intake manifold thermal insulator.Information provided by Vyncolit, a Sumitomo B..
Flexural Modulus	5.00 - 8.00 GPa	725 - 1160 ksi	ISO 178
Bulk Molding Compounds tetra-DUR F 4001 Bulk Molding Compound UL-Licensed, Abrasion resistance, free of fiber glass.Typical Applications - Requiring mechanical strength, abrasion resistance, dimensional stability, electrical insulation, electrostatic dissipati..
Flexural Modulus	1.70 - 8.00 GPa @Temperature -40.0 - 120 °C	247 - 1160 ksi @Temperature -40.0 - 248 °F	Average value: 3.83 GPa Grade Count:5
Overview of materials for Nylon 6, 20% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 20% Glass Fiber Filled".Specific grades with glass content between 15% and 24% are included. Ea..
Flexural Modulus	1.60 - 8.00 GPa	232 - 1160 ksi	Average value: 5.28 GPa Grade Count:278
Overview of materials for Polypropylene with 30% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 30% Glass Fiber Filler". Specific grades with glass content between 25% and 34% are i..