Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 167 °F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	60.0 - 75.0 °C	140 - 167 °F	ASTM D648
Arkema Group Kynar Flex® 2900 PVDF Copolymer (discontinued **) Copolymer Series, Kynar® components are used extensively in the high purity semiconductor market, the pulp and paper industry, nuclear waste processing, and the general chemical processing industry..
Deflection Temperature at 0.46 MPa (66 psi)	70.0 - 75.0 °C	158 - 167 °F
C.O.I.M. EXTER S® S 109 E Orthophthalic Resin Description: The Exter S product line contains a large number of unsaturated polyester resin products with an array of properties and applications.Specific Notes for ESTER S® S 109 E: General purpo..
Deflection Temperature at 0.46 MPa (66 psi)	60.0 - 75.0 °C	140 - 167 °F	ASTM D648
Arkema Group KYNAR FLEX® 2800-00 Polyvinylidene Fluoride Copolymer - Extrusion Characteristics: Natural resin - translucent, off-white hemispheres. Flexible. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechanical strength, low..
Deflection Temperature at 0.46 MPa (66 psi)	60.0 - 75.0 °C	140 - 167 °F	ASTM D648
Arkema Group KYNAR FLEX® 2800-01 Polyvinylidene Fluoride Copolymer - Extrusion Characteristics: Natural resin - translucent, off-white hemispheres. Flexible, lubricated. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechanical s..
Deflection Temperature at 0.46 MPa (66 psi)	60.0 - 75.0 °C	140 - 167 °F	ASTM D648
Arkema Group KYNAR FLEX® 2850 Black Polyvinylidene Fluoride Copolymer - Extrusion & Molding Characteristics: Natural resin - translucent, off-white hemispheres. 150°C Temperature rating, pigmented. High stability in harsh thermal, chemical and ultraviolet environments. High toughness ..
Deflection Temperature at 0.46 MPa (66 psi)	60.0 - 75.0 °C	140 - 167 °F	ASTM D648
Arkema Group KYNAR FLEX® 2850-02 Polyvinylidene Fluoride Copolymer - Extrusion Characteristics: Natural resin - translucent, off-white hemispheres. 150°C Temperature rating. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechani..
Deflection Temperature at 0.46 MPa (66 psi)	60.0 - 75.0 °C	140 - 167 °F	ASTM D648
Arkema Group KYNAR FLEX® 2850-04 Polyvinylidene Fluoride Copolymer - Extrusion & Molding Characteristics: Natural resin - translucent, off-white hemispheres. 150°C Temperature rating. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechani..
Deflection Temperature at 0.46 MPa (66 psi)	60.0 - 75.0 °C	140 - 167 °F	ASTM D648
Arkema Group KYNAR FLEX® 2900-04 Polyvinylidene Fluoride Copolymer - Extrusion & Molding Characteristics: Natural resin - translucent, off-white hemispheres. Flexible, flame and smoke suppressant. High stability in harsh thermal, chemical and ultraviolet environments. High toughness..
Deflection Temperature at 0.46 MPa (66 psi)	60.0 - 75.0 °C	140 - 167 °F	ASTM D648
Arkema Group KYNAR FLEX® 2800-20 Polyvinylidene Fluoride Copolymer - Extrusion & Molding Characteristics: Natural resin - translucent, off-white hemispheres. Flexible. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechanical strength, low..
Deflection Temperature at 0.46 MPa (66 psi)	60.0 - 75.0 °C	140 - 167 °F	ASTM D648
Arkema Group KYNAR FLEX® 2850-00 Polyvinylidene Fluoride Copolymer - Extrusion & Molding Characteristics: Natural resin - translucent, off-white hemispheres. 150°C Temperature rating. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechani..
Deflection Temperature at 0.46 MPa (66 psi)	60.0 - 75.0 °C	140 - 167 °F	ASTM D648
Arkema Group KYNAR FLEX® 2850-07 Polyvinylidene Fluoride Copolymer - Extrusion & Molding Characteristics: Natural resin - translucent, off-white hemispheres. 150°C Temperature rating. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechani..