- A. Schulman POLYFORT™ PP 2173HU Toyota High Impact Copolymer Polypropylene
A. Schulman POLYFORT™ PP 2173HU Toyota High Impact Copolymer Polypropylene
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Impact Modified; Molded/Extruded |
| Manufacturer | A. Schulman, Inc. |
| Trade Name | POLYFORT™ |
| Port | Ningbo port,China |
| Trade Terms | EXW, FOB, CFR, CIF |
| Payment Terms | L/C, T/T, PayPal |
| Download PDF | A. Schulman POLYFORT™ PP 2173HU Toyota High Impact Copolymer Polypropylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
DescriptionPolyfort® PP 2173HU Toyota is a high flow, UV stabilized, high impact copolymer polypropylene.Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.905 g/cc | 0.905 g/cc | ASTM D792 |
| Melt Flow | 20 g/10 min <br>@Temperature 230 °C |
20 g/10 min <br>@Temperature 446 °F |
Condition L; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 18.0 MPa | 2610 psi | ASTM D638 |
| Elongation at Yield | 37 % | 37 % | |
| Flexural Strength | 18.0 MPa | 2610 psi | |
| Flexural Modulus | 0.760 GPa | 110 ksi | ASTM D790 |
| Izod Impact, Notched | 6.00 J/cm | 11.2 ft-lb/in | ASTM D256 |
| Falling Dart Impact | 5.10 J <br>@Thickness 1.78 mm,<br> Temperature -30.0 °C |
3.76 ft-lb <br>@Thickness 0.0701 in,<br> Temperature -22.0 °F |
Pass |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ASTM D648 |
Users viewing this material also viewed the following:
- Network Polymers MS 110 Styrene Methyl Methacrylate Terpolymer
- Polymer Resources ABS-FR Flame Retardant ABS
- Karina 837-35/1-E-ERYB Ivory PVC Compound
- SABIC Innovative Plastics LNP LUBRICOMP JFL36 PES (Asia Pacific)
- SABIC Innovative Plastics LNP Thermocomp UC008S PPA (Asia Pacific)
- Ensinger Tecapeek® XP-90 Compression Molded PEEK Compound, 25% Fiberglass
- ExxonMobil 2 Mobilith AW Series
- MV Labs RH470 [(C6H5)3P]2Rh(CO)Cl Carbonylchlorobis(triphenylphosphine) rhodium(I)
- Kuraray HYBRAR® BF1 Three Layer Blown Film
Copyright © lookpolymers.com All Rights Reserved