Polymer Property : Flexural Strength = 18.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Flexural Strength 18.0 MPa
2610 psi
Plastcom SLOVALEN PQ 81 T 10 PP, 10% mineral filling
FeaturesModified PP for injection moulding with the content of 10% mineral filling. Increased rigidity, strength and thermal use up to 130°C depending on the talc content. Decreased shrinkage. Gene..
Flexural Strength 18.0 MPa
2610 psi
Pyrotek NAD-250 Structural Insulation Board
NAD-250 is a general purpose cement board. It is suitable for low-voltage electrical insulation in dry conditions.ApplicationsOven shelves Platen insulators Coil boxes Foundry core plates Heat guar..
Flexural Strength 18.0 MPa
2610 psi
Quadrant EPP Fluorosint® HPV PTFE + additives, bearing grade, compression moulded (ISO Data)
FDA compliant Fluorosint HPV is a high performance Fluorosint bearing grade, optimized for high pressure-velocity capabilities and very low wear. Fluorosint HPV was developed for bearing application..
Flexural Strength 18.0 MPa
2610 psi
Quadrant EPP TIVAR® 1000 antistatic PE-UHMW + carbon black (ISO Data)
By incorporating an effective carbon black grade, TIVAR 1000 antistatic offers the electrostatic dissipative properties often required for PE-UHMW components operating at high line speeds and convey..
Flexural Strength 18.0 MPa
2610 psi
Quadrant EPP TIVAR® Burnguard PE-UHMW + flame retardant + other additives (ISO Data)
TIVAR Burnguard is a PE-UHMW grade containing a very effective non-halogenated flame retardant. Specifically developed to improve the poor flammability behaviour of straight forward virgin polyethyl..
Flexural Strength 18.0 MPa
2610 psi
Quadrant EPP TIVAR® ECO PE-UHMW reprocessed (ISO Data)
This grade, partially composed of reprocessed PE-UHMW material, has an overall lower property level than the virgin TIVAR 1000 and a lower cost. Compared with virgin PE 500, however, it has a much b..
Flexural Strength 18.0 MPa
2610 psi
Quadrant EPP TIVAR® MD PE-UHMW + metal detectable additive (ISO Data)
This PE-UHMW grade with extremely high degree of polymerisation contains a metal detectable additive which does hardly affect the inherent PE-UHMW key properties. TIVAR MD presents excellent toughne..
Flexural Strength 18.0 MPa
2610 psi
50N; ASTM D790
Ravago Manufacturing Americas Echo® RPPC 20/10 BK Recycled Polypropylene
Copolymer Polypropylene, Unreinforced, 20 MFI, 10 Izod, BlackEntecs proprietary products include a full range of compounds in the Nylon 6/6, Nylon 6, ABS, PBT, Polycarbonate, PC/ABS, PC/ASA, PC/PBT,..
Flexural Strength 18.0 MPa

@Temperature 150 °C
2610 psi

@Temperature 302 °F
ISO 178
Solvay Specialty Polymers Amodel® AP-9240 NL Polyphthalamide (PPA) Resin, 40% Mineral Filled, Dry as Molded  (
AMODEL AP-9240 NL resin is a 40% mineral-filled, impact-modified polyphthalamide (PPA). It was designed to provide a smooth molded surface suitable for many decorative applications. This resin offer..
Flexural Strength >= 18.0 MPa
>= 2610 psi
MarkeTech Repton 837 Zirconia + 4.4 mol% Calcia
Brand 837 features: Good spalling characteristics.REPTON setter tiles, kiln furniture, and special fixtures are lightweight, ridge, and high strength ceramics that resist distortion and spalling, ev..
Flexural Strength 18.0 MPa
2610 psi
ISO 178
MRC Polymers MAXTELâ„¢ 600T15IMUV TPO, 15% Talc Filled
• For automotive exterior applications• Excellent process ability and dimensional stability• Can be UV Stabilized• Internal and external lubricants can be addedInformation pr..
Flexural Strength 18.0 MPa
2610 psi
2 mm/min; ISO 178
SABIC Innovative Plastics ULTEM SILTEM-STM1500 PEI (Europe-Africa-Middle East)
SILTEM STM1500 is a flexible siloxane-polyetherimide copolymer for cable and wire coatings. RoHS compliant.
Flexural Strength 18.0 MPa
2610 psi
ISO Data
Styrolution Styrolux 3G55 SBC
Styrolux 3G55 is a thermoplastic styrene-butadiene block copolymer which is suitable for film and sheet extrusion, and thermoforming. It offers and outstanding combination of crystal clarity and ex..
Flexural Strength 18.0 MPa
2610 psi
ISO 178
Styrolution Styrolux BX6400 SBC
Styrolux BX6400 is a developmental styrene butadiene copolymer (SBC) of high clarity and ultimate toughness used mainly in sheet and film extrusion and thermoforming applications. It is specifically..
Flexural Strength 18.0 MPa
2610 psi
ISO 178
SABIC Innovative Plastics LNP THERMOCOMP TH0300B PU
LNP* Thermocomp* Th0300B is a compound based on Polyurethane containing proprietary fillers. Characteristics of this grade are High Specific Gravity.
Flexural Strength 18.0 MPa
2610 psi
ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP TH0450A PUR
LNP THERMOCOMP* TH0450A is a compound based on Polyurethane resin. Added features of this material include: High Specific Gravity.
Flexural Strength 18.0 MPa
2610 psi
ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP TH0450A PUR (Asia Pacific)
LNP THERMOCOMP* TH0450A is a compound based on Polyurethane resin. Added features of this material include: High Specific Gravity.
Flexural Strength 18.0 MPa
2610 psi
ISO 178
SABIC Innovative Plastics LNP THERMOCOMP TH0600A PUR
LNP THERMOCOMP* TH0600A is a compound based on Polyurethane resin. Added features of this material include: High Specific Gravity.
Flexural Strength 18.0 MPa
2610 psi
ISO 178
SABIC Innovative Plastics LNP THERMOCOMP TH0600A PUR (Asia Pacific)
LNP THERMOCOMP* TH0600A is a compound based on Polyurethane resin. Added features of this material include: High Specific Gravity.
Flexural Strength 18.0 MPa
2610 psi
A. Schulman POLYFORT™ PP 2173HU Toyota High Impact Copolymer Polypropylene
DescriptionPolyfort® PP 2173HU Toyota is a high flow, UV stabilized, high impact copolymer polypropylene.Information provided by A. Schulman.
Flexural Strength 18.0 MPa
2610 psi
A. Schulman POLYFORT™ PP 2173HU Toyota High Impact Copolymer Polypropylene
DescriptionPolyfort® PP 2173HU Toyota is a high flow, UV stabilized, high impact copolymer polypropylene.Information provided by A. Schulman.
Flexural Strength 18.0 MPa
2610 psi
A. Schulman POLYFORT™ PP 2173HU Toyota High Impact Copolymer Polypropylene
DescriptionPolyfort® PP 2173HU Toyota is a high flow, UV stabilized, high impact copolymer polypropylene.Information provided by A. Schulman.
Flexural Strength 18.0 MPa
2610 psi
A. Schulman POLYFORT™ PP 2173HU Toyota High Impact Copolymer Polypropylene
DescriptionPolyfort® PP 2173HU Toyota is a high flow, UV stabilized, high impact copolymer polypropylene.Information provided by A. Schulman.
Flexural Strength 18.0 MPa
2610 psi
A. Schulman POLYFORT™ PP 2173HU Toyota High Impact Copolymer Polypropylene
DescriptionPolyfort® PP 2173HU Toyota is a high flow, UV stabilized, high impact copolymer polypropylene.Information provided by A. Schulman.
Flexural Strength 18.0 MPa
2610 psi
A. Schulman POLYFORT™ PP 2173HU Toyota High Impact Copolymer Polypropylene
DescriptionPolyfort® PP 2173HU Toyota is a high flow, UV stabilized, high impact copolymer polypropylene.Information provided by A. Schulman.
Flexural Strength >= 18.0 MPa
>= 2610 psi
high temp bending
China-Yixing Longly Refractories ASM-120 Cordierite-Mullite
Featured mullite, cordierite as the main raw material, the use of advanced production technology, professionally manufacturing the kiln furniture of ceramic and powder metallurgy with load bearing b..
Flexural Strength 18.0 MPa
2610 psi
After conditioning at 23°C and 50% RH; ISO 178
Arkema Group Orgalloy® LE 60LMXV Polyamide 6 Alloy
Polyamide Alloy, Semi-Flexible grade, Nylon 6 basedTubes / Mandrels / Profiles / CablesInformation provided by Arkema Group
Flexural Strength 18.0 MPa
2610 psi
Biomer P209 PHB Biodegradable Polymer
PHB is a isotactic, absolutely linear, thermoplastic homopolyester built of 3-hydroxy butyric acid. The formula of the subunit is -[O-CH(CH3)-CH2-CO]-. PHB is free from even traces of catalysts. P..
Flexural Strength 18.0 MPa
2610 psi
Plastcom SLOVALEN PQ 83 T 10 PP, 10% mineral filling
FeaturesModified PP + EPDM for injection moulding with the content of 10% mineral filler. Increased rigidity, strength and thermal. Decreased shrinkage. Application in automotive, covers of car chas..
Flexural Strength 18.0 MPa
2610 psi
ASTM D790
Polyram RamOfin PPC370B73 Polypropylene, 73% Mineral Filled
73% mineral filled polypropylene for heavy density injection molding applicationsInformation provided by Polyram Ram On Ind.