- A. Schulman POLYPUR™ FPU 1103F Thermoplastic Polyurethane Compound
A. Schulman POLYPUR™ FPU 1103F Thermoplastic Polyurethane Compound
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Molded , Polyurethane, TP |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman POLYPUR™ FPU 1103F Thermoplastic Polyurethane Compound.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.44 g/cc | 1.44 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm |
0.0010 - 0.0030 in/in @Thickness 0.126 in |
48 hr, at 80 and 121°C; ASTM D955 |
| 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm |
0.0010 - 0.0030 in/in @Thickness 0.126 in |
72 hr; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 55 | 55 | 15 sec delay; ASTM D2240 |
| Tensile Strength, Ultimate | 31.0 MPa | 4500 psi | at max load; ASTM D638 |
| Elongation at Break | 35 % | 35 % | ASTM D412 |
| Flexural Modulus | 0.759 GPa | 110 ksi | ASTM D790 |
| Izod Impact, Notched | 5.30 J/cm | 9.93 ft-lb/in | ASTM D256 |
| Falling Dart Impact | 7.00 J | 5.16 ft-lb | at -30°C; ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 180 µm/m-°C @Temperature -30.0 - 30.0 °C |
100 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM E831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 95.0 °C @Thickness 3.20 mm |
203 °F @Thickness 0.126 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C @Thickness 3.20 mm |
122 °F @Thickness 0.126 in |
ASTM D648 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® PC2200 PC (Europe-Africa-Middle East)
- Honeywell ACLAR® 11A (0.90 mil) CTFE Homopolymer, Barrier Film (discontinued **)
- Albis Plastics Cellulose Acetate Propionate CP808 (FDA), 8% Plasticizer (discontinued **)
- A. Schulman POLYBATCH™ House Red 50311U/4 Concentrate Based In LLDPE
- Loctite® 3566 Rapid Flow Low Profile Underfill
- Polyram PlusTek PA310G8BK10 Nylon 6.6 for injection Molding, 40% Glass Fiber Reinforced, Heat Stabilized
- 3M CN-3190 EMI Shielding Tape
- ATI Allvac® Nickelvac® C-263 Nickel Superalloy, Heat Treatment: 927°C (1700°F) Anneal
- BASF Ultradur® B 4300 GM42 20/10% Glass/Mineral Filled PBT
Copyright © lookpolymers.com All Rights Reserved