Adell BJ-33 Nylon 6, 15% Glass Reinforced; High Impact
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass Filled, Impact Grade |
| Manufacturer | Adell Plastics, Inc. |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Adell BJ-33 Nylon 6, 15% Glass Reinforced; High Impact.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Adell Plastics, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ASTM D792 |
| Water Absorption | 0.80 % | 0.80 % | 24 hour immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0075 cm/cm | 0.0075 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 76 | 76 | ASTM D785 |
| Hardness, Rockwell R | 112 | 112 | ASTM D785 |
| Tensile Strength, Ultimate | 86.2 MPa | 12500 psi | ASTM D638 |
| Elongation at Break | 3.5 % | 3.5 % | ASTM D638 |
| Flexural Strength | 108 MPa | 15700 psi | ASTM D790 |
| Flexural Modulus | 3.40 GPa | 493 ksi | ASTM D790 |
| Compressive Yield Strength | 103 MPa | 14900 psi | ASTM D695 |
| Izod Impact, Notched | 1.30 J/cm | 2.44 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 216 °C | 421 °F | ASTM D789 |
| Deflection Temperature at 0.46 MPa (66 psi) | 199 °C | 390 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 188 °C | 370 °F | ASTM D648 |
| Flammability, UL94 | HB | HB |
Users viewing this material also viewed the following:
- LG Chemical LI968W Co-Extrusion ASA
- Lanxess Durethan® BKV 325 Z H2.0 901510 Nylon 6, 25% Glass Fibers
- SABIC Innovative Plastics ULTEM 2110EPR PEI (Asia Pacific)
- Saint-Gobain Chemlam® SGC6-06 Copper Adhesive Tape
- Shin-Etsu Silicones KE-5551U High Strength Silicone Elastomer
- Schmolz + Bickenbach UGIMA® 630 Stainless Steel Bar
- A. Schulman SCHULAMID® 6 GF15H 15% Glass Bead Reinforced, Heat Stabilized Nylon 6
- Dow Corning SILASTIC® S-2 RTV SILICONE RUBBER BASE & CURING AGENT
- Arlon 0.008" (0.2032 mm) Flexible Heater Silicone with Fiberglass Substrate (44571R008)
- Abatron 85062 A/B Filled Potting Compound (discontinued **)
Copyright © lookpolymers.com All Rights Reserved