Asia International Enterprise (Hong Kong) ST6010 Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | Asia Int'l Enterprise (Hong Kong) Limited |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Asia International Enterprise (Hong Kong) ST6010 Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Asia International Enterprise (Hong Kong) Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.08 g/cc @Temperature 23.0 °C |
1.08 g/cc @Temperature 73.4 °F |
ASTM D792 |
| Filler Content | 0.00 % | 0.00 % | |
| Linear Mold Shrinkage | 0.010 - 0.018 cm/cm | 0.010 - 0.018 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 122 | 122 | ASTM D785 |
| Tensile Strength, Ultimate | 78.5 MPa | 11400 psi | 5mm/min; ASTM D638 |
| Elongation at Break | 120 % | 120 % | 5mm/min; ASTM D638 |
| Flexural Strength | 118 MPa | 17100 psi | 2.8mm/min; ASTM D790 |
| Flexural Modulus | 1.86 GPa | 270 ksi | 2.8mm/min; ASTM D790 |
| Izod Impact, Notched | 1.47 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
2.76 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | ASTM D648 |
| Flammability, UL94 | HB | HB |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 240 - 280 °C | 464 - 536 °F | Cylinder Temperature |
| Mold Temperature | 50.0 - 90.0 °C | 122 - 194 °F | |
| Drying Temperature | 80.0 - 90.0 °C | 176 - 194 °F | |
| Dry Time | 4 - 6 hour | 4 - 6 hour |
Users viewing this material also viewed the following:
- Osprey Metals 85/15 Cu Sn Powder (Grade 80% - 22)
- Pyrotek ISOMAG® 70 Structural Insulation
- Overview of materials for Polyetheretherketone, Unreinforced
- Micropol Microlink XL Crosslinkable Polyethylene
- Techmer ES Electrablend® PC 04008 FR BK Stainless Steel Filled
- A. Schulman PP 1407L-01 Polypropylene High-Impact Copolymer Polypropylene
- Ensinger DELRIN® 507 Black Acetal Homopolymer (POM)
Copyright © lookpolymers.com All Rights Reserved