Daelim H&L Plavis G15 Aromatic Polyimide, 15% Graphite Filled, Machined Parts
| Category | Polymer , Thermoset , Polyimide, TS |
| Manufacturer | Daelim H&L Super Engineering Plastics |
| Trade Name | Plavis |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Daelim H&L Plavis G15 Aromatic Polyimide, 15% Graphite Filled, Machined Parts.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High abrasion resistance, very low friction coefficient property, suitable for being applied to spin component of spin apparatusInformation provided by Daelim H&L
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.49 g/cc | 1.49 g/cc | ASTM D792 |
| Moisture Absorption at Equilibrium | 0.90 % | 0.90 % | 50% RH; ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 80 - 92 | 80 - 92 | ASTM D785 |
| Tensile Strength, Ultimate | 47.1 MPa @Temperature 260 °C |
6830 psi @Temperature 500 °F |
ASTM D1708 |
| 78.7 MPa @Temperature 23.0 °C |
11400 psi @Temperature 73.4 °F |
ASTM D1708 | |
| Tensile Strength, Yield | 58.9 MPa @Strain 1.00 % |
8550 psi @Strain 1.00 % |
ASTM D95 |
| 138.5 MPa @Strain 10.0 % |
20080 psi @Strain 10.0 % |
ASTM D95 | |
| Elongation at Break | 7.4 % @Temperature 260 °C |
7.4 % @Temperature 500 °F |
ASTM D1708 |
| 11.2 % @Temperature 23.0 °C |
11.2 % @Temperature 73.4 °F |
ASTM D1708 | |
| Flexural Strength | 64.7 MPa @Temperature 260 °C |
9380 psi @Temperature 500 °F |
ASTM D790 |
| 118.5 MPa @Temperature 23.0 °C |
17190 psi @Temperature 73.4 °F |
ASTM D790 | |
| Flexural Modulus | 2.60 GPa @Temperature 260 °C |
377 ksi @Temperature 500 °F |
ASTM D790 |
| 3.81 GPa @Temperature 23.0 °C |
553 ksi @Temperature 73.4 °F |
ASTM D790 | |
| Compressive Modulus | 2.9234 GPa @Temperature 23.0 °C |
424.00 ksi @Temperature 73.4 °F |
ASTM D695 |
| Izod Impact, Notched (ISO) | 4.7088 kJ/m² | 2.2410 ft-lb/in² | ASTM D256 |
| Coefficient of Friction | 0.20 | 0.20 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 4.70 µm/m-°C @Temperature 23.0 - 260 °C |
2.61 µin/in-°F @Temperature 73.4 - 500 °F |
ASTM D696 |
| Decomposition Temperature | 616 °C | 1140 °F | |
| Oxygen Index | 54.15 % | 54.15 % | ASTM D2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 - 1.00e+15 ohm-cm @Temperature 23.0 °C |
1.00e+14 - 1.00e+15 ohm-cm @Temperature 73.4 °F |
ASTM D257 |
| Dissipation Factor | 0.0104 @Frequency 1.00e+6 Hz, Temperature 23.0 °C |
0.0104 @Frequency 1.00e+6 Hz, Temperature 73.4 °F |
ASTM D150 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| 50% Weight Reduction Time (Minutes) | 240 |
Users viewing this material also viewed the following:
- Osprey Metals Ni40Cu Binary Alloy Powder (Grade 90% - 16)
- DuPont Performance Polymers Crastin® CE15330 NC010 PBT (Unverified Data**)
- Ineos Nova S-5100 High Impact Compact Polystyrene (discontinued **)
- Mallard Creek Polymers Rovene® 6201 Styrene-Acrylic Resin
- Sumitomo Bakelite North America 52-40-40-P Long-Glass Reinforced Diallyl Phthalate
- UBE 5021T Nylon 6/66 Monofilament (Drawing Ratio=4.5)
- EMS-Grivory Grivory® L 25 W 20 Y PA12-I
- 3M OFM0802 Outdoor UL Recognized Brite Silver Polyester Label Products
- Schott DUROBAX® clear Neutral Glass Tubing
Copyright © lookpolymers.com All Rights Reserved