- Dow DOWLEX™ 2045.02AC Linear Low Density Polyethylene, Blown Film Grade
Dow DOWLEX™ 2045.02AC Linear Low Density Polyethylene, Blown Film Grade
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade |
| Manufacturer | Dow Chemical |
| Trade Name | DOWLEX™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Dow DOWLEX™ 2045.02AC Linear Low Density Polyethylene, Blown Film Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
DOWLEX® 2045.02AC Polyethylene resin is a high stability blown film extrusion resin that provides excellent tear strength and outstanding toughness. It contains high level of slip additive and medium level of antiblock additive. It complies with U.S. FDA regulation 21 CFR 177.1520 (c) 3.2 (a) for food contact applications, and has been approved by USDA for packaging meat and poultry products.Data provided by Dow Chemical.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in³ | |
| Melt Flow | 1.0 g/10 min @Load 2.16 kg |
1.0 g/10 min @Load 4.76 lb |
Melt flow ratio I10/I2 is 8. |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 26.2 MPa | 3800 psi | Molded property |
| Film Tensile Strength at Yield, MD | 10.3 MPa | 1490 psi | |
| Film Tensile Strength at Yield, TD | 11.0 MPa | 1600 psi | |
| Tensile Strength, Yield | 12.4 MPa | 1800 psi | Molded property |
| Film Elongation at Break, MD | 650 % | 650 % | |
| Film Elongation at Break, TD | 800 % | 800 % | |
| Elongation at Break | 1000 % | 1000 % | Molded value |
| Coefficient of Friction | 0.20 | 0.20 | |
| Elmendorf Tear Strength MD | 370 g | 370 g | Unspecified film thickness |
| Elmendorf Tear Strength TD | 800 g | 800 g | Unspecified film thickness |
| Dart Drop Test | 250 g | 0.551 lb | |
| Film Tensile Strength at Break, MD | 44.8 MPa | 6500 psi | |
| Film Tensile Strength at Break, TD | 35.2 MPa | 5110 psi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 106 °C | 223 °F |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 19 % | 19 % | |
| Gloss | 32 % | 32 % | 45° |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 232 °C | 450 °F | Film extrusion temperature |
Users viewing this material also viewed the following:
- Precision Polymer Engineering N40M Nitrile Rubber
- SABIC Innovative Plastics Cycolac® INP581 ABS
- Polykemi AB SCANAMID 66 A13^ Q2 EX8 Nylon 66, Mineral Reinforced
- Nilit FRIANYL A63 H-GV50 Nylon 6.6 for injection molding, 50% glass fiber reinforced
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 20 PHR Suprex Clay Filler
- Materion BrushCAST® 275CT Fine Grain Casting Alloy (Solution Annealed & Aged)
- Lehmann & Voss LUVOCOM® 1104/XCF/30 Polyether ketone, with carbon fiber, easy flowing
- Silberline Silvet® 330-20-E
- A. Schulman SCHULAMID® 66 GF50H 50% Glass Fiber Reinforced, Heat Stabilized 66
- Axiall 7181 Rigid PVC, Extrusion
Copyright © lookpolymers.com All Rights Reserved