DuPont Performance Polymers Zytel® 77G43L NC010 Nylon 612  (Unverified Data**)

Category Polymer , Thermoplastic , Nylon , Nylon 612 , Nylon 612, Glass Fiber Filler
Manufacturer DuPont Performance Polymers
Trade Name Zytel®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® 77G43L NC010 Nylon 612  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
43% Glass Reinforced Polyamide 612Zytel 77G43L NC010 is a 43% glass fiber reinforced polyamide 612 resin for injection molding.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.42 g/cc
0.0513 lb/in³
DAM; ISO 1183
Water Absorption 1.7 %

@Thickness 2.00 mm
 1.7 %

@Thickness 0.0787 in
 DAM; Sim. to ISO 62
Moisture Absorption 0.700 %

@Thickness 2.00 mm
 0.700 %

@Thickness 0.0787 in
 DAM; Sim. to ISO 62
Viscosity Test 145 cm³/g
145 cm³/g
DAM; ISO 307 1157 1628
Linear Mold Shrinkage, Flow 0.0030 cm/cm
0.0030 in/in
DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.0080 cm/cm
0.0080 in/in
DAM; ISO 294-4 2577
Mechanical Properties Metric English Comments
Hardness, Rockwell R 118
118
DAM; ISO 2039-2
Tensile Strength at Break 165 MPa
23900 psi
50%RH; ISO 527-1/-2
200 MPa
29000 psi
DAM; ISO 527-1/-2
Tensile Stress 11.65 MPa

@Strain 0.230 %,
Temperature 150 °C
 1690 psi

@Strain 0.230 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
12.11 MPa

@Strain 0.220 %,
Temperature 150 °C
 1756 psi

@Strain 0.220 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
18.25 MPa

@Strain 0.220 %,
Temperature 90.0 °C
 2647 psi

@Strain 0.220 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
18.81 MPa

@Strain 0.240 %,
Temperature 90.0 °C
 2728 psi

@Strain 0.240 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
23.06 MPa

@Strain 0.220 %,
Temperature 40.0 °C
 3345 psi

@Strain 0.220 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
25.22 MPa

@Strain 0.230 %,
Temperature 40.0 °C
 3658 psi

@Strain 0.230 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
28.59 MPa

@Strain 0.670 %,
Temperature 150 °C
 4147 psi

@Strain 0.670 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
33.27 MPa

@Strain 0.230 %,
Temperature 23.0 °C
 4825 psi

@Strain 0.230 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
34.16 MPa

@Strain 0.230 %,
Temperature 0.000 °C
 4954 psi

@Strain 0.230 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
38.37 MPa

@Strain 0.910 %,
Temperature 150 °C
 5565 psi

@Strain 0.910 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
38.78 MPa

@Strain 0.540 %,
Temperature 90.0 °C
 5625 psi

@Strain 0.540 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
40.89 MPa

@Strain 0.410 %,
Temperature 40.0 °C
 5931 psi

@Strain 0.410 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
41.15 MPa

@Strain 0.340 %,
Temperature 23.0 °C
 5968 psi

@Strain 0.340 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
42.43 MPa

@Strain 1.26 %,
Temperature 150 °C
 6154 psi

@Strain 1.26 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
44.21 MPa

@Strain 0.330 %,
Temperature 0.000 °C
 6412 psi

@Strain 0.330 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
45.35 MPa

@Strain 0.640 %,
Temperature 90.0 °C
 6577 psi

@Strain 0.640 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
53.67 MPa

@Strain 2.05 %,
Temperature 150 °C
 7784 psi

@Strain 2.05 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
59.11 MPa

@Strain 1.98 %,
Temperature 150 °C
 8573 psi

@Strain 1.98 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
59.5 MPa

@Strain 0.960 %,
Temperature 90.0 °C
 8630 psi

@Strain 0.960 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
59.61 MPa

@Strain 0.580 %,
Temperature 40.0 °C
 8646 psi

@Strain 0.580 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
66.9 MPa

@Strain 0.420 %,
Temperature -40.0 °C
 9700 psi

@Strain 0.420 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
71.96 MPa

@Strain 0.820 %,
Temperature 40.0 °C
 10440 psi

@Strain 0.820 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
72.96 MPa

@Strain 0.660 %,
Temperature 23.0 °C
 10580 psi

@Strain 0.660 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
73.4 MPa

@Strain 3.36 %,
Temperature 150 °C
 10600 psi

@Strain 3.36 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
74.39 MPa

@Strain 0.560 %,
Temperature 23.0 °C
 10790 psi

@Strain 0.560 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
76.78 MPa

@Strain 0.550 %,
Temperature 0.000 °C
 11140 psi

@Strain 0.550 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
77.36 MPa

@Strain 1.35 %,
Temperature 90.0 °C
 11220 psi

@Strain 1.35 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
79.92 MPa

@Strain 0.630 %,
Temperature 0.000 °C
 11590 psi

@Strain 0.630 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
80.08 MPa

@Strain 1.55 %,
Temperature 90.0 °C
 11610 psi

@Strain 1.55 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
100.88 MPa

@Strain 1.16 %,
Temperature 40.0 °C
 14631 psi

@Strain 1.16 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
101.31 MPa

@Strain 1.34 %,
Temperature 40.0 °C
 14694 psi

@Strain 1.34 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
101.76 MPa

@Strain 2.22 %,
Temperature 90.0 °C
 14759 psi

@Strain 2.22 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
102.71 MPa

@Strain 0.730 %,
Temperature -40.0 °C
 14897 psi

@Strain 0.730 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
103.38 MPa

@Strain 1.03 %,
Temperature 23.0 °C
 14994 psi

@Strain 1.03 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
115.95 MPa

@Strain 0.970 %,
Temperature 0.000 °C
 16817 psi

@Strain 0.970 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
122.2 MPa

@Strain 1.02 %,
Temperature 23.0 °C
 17720 psi

@Strain 1.02 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
126 MPa

@Strain 0.990 %,
Temperature 0.000 °C
 18300 psi

@Strain 0.990 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
129.98 MPa

@Strain 1.47 %,
Temperature 23.0 °C
 18852 psi

@Strain 1.47 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
130.54 MPa

@Strain 0.870 %,
Temperature -40.0 °C
 18933 psi

@Strain 0.870 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
135.21 MPa

@Strain 1.83 %,
Temperature 40.0 °C
 19611 psi

@Strain 1.83 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
141.03 MPa

@Strain 1.05 %,
Temperature -40.0 °C
 20455 psi

@Strain 1.05 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
149.29 MPa

@Strain 1.35 %,
Temperature 0.000 °C
 21653 psi

@Strain 1.35 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
161.61 MPa

@Strain 1.55 %,
Temperature 23.0 °C
 23440 psi

@Strain 1.55 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
174.83 MPa

@Strain 1.52 %,
Temperature 0.000 °C
 25357 psi

@Strain 1.52 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
175.37 MPa

@Strain 1.39 %,
Temperature -40.0 °C
 25435 psi

@Strain 1.39 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
183.58 MPa

@Strain 1.34 %,
Temperature -40.0 °C
 26626 psi

@Strain 1.34 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
234.23 MPa

@Strain 1.92 %,
Temperature -40.0 °C
 33972 psi

@Strain 1.92 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
10.0 MPa

@Strain 0.107 %,
Time 3600 sec
 1450 psi

@Strain 0.107 %,
Time 1.00 hour
 50%RH; isochronous; ISO 11403-1 -2
10.0 MPa

@Strain 0.119 %,
Time 360000 sec
 1450 psi

@Strain 0.119 %,
Time 100 hour
 50%RH; isochronous; ISO 11403-1 -2
10.0 MPa

@Strain 0.133 %,
Time 3.60e+6 sec
 1450 psi

@Strain 0.133 %,
Time 1000 hour
 50%RH; isochronous; ISO 11403-1 -2
10.0 MPa

@Time 360 sec,
Strain 0.102 %
 1450 psi

@Time 0.100 hour,
Strain 0.102 %
 50%RH; isochronous; ISO 11403-1 -2
Elongation at Break 3.0 %
3.0 %
DAM; ISO 527-1/-2
5.0 %
5.0 %
50%RH; ISO 527-1/-2
Tensile Modulus 11.5 GPa
1670 ksi
50%RH; ISO 527-1/-2
12.5 GPa
1810 ksi
DAM; ISO 527-1/-2
Flexural Modulus 11.0 GPa
1600 ksi
DAM; ISO 178
Secant Modulus 2.22 GPa

@Strain 5.39 %,
Temperature 100 °C
 322 ksi

@Strain 5.39 %,
Temperature 212 °F
 DAM; ISO 11403-1 -2
Users viewing this material also viewed the following: