DuPont Performance Polymers Zytel® HTN FE8200 NC010 Polyphthalamide (PPA)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyphthalamide (PPA)
Manufacturer DuPont Performance Polymers
Trade Name Zytel® HTN
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® HTN FE8200 NC010 Polyphthalamide (PPA)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Unreinforced Toughened PPA High Performance Polyamide Zytel HTNFE8200 NC010 is an unreinforced toughened heat stabilized lubricated high performance polyamide resin for injection molding. It is also a PPA resin.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.13 g/cc
0.0408 lb/in³
DAM; ISO 1183
Water Absorption 6.3 %

@Thickness 2.00 mm
 6.3 %

@Thickness 0.0787 in
 DAM; Sim. to ISO 62
Moisture Absorption 1.90 %

@Thickness 2.00 mm
 1.90 %

@Thickness 0.0787 in
 DAM; Sim. to ISO 62
Linear Mold Shrinkage, Flow 0.0080 cm/cm
0.0080 in/in
DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.0090 cm/cm
0.0090 in/in
DAM; ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Stress 0.400 MPa

@Strain 0.160 %,
Temperature 150 °C
 58.0 psi

@Strain 0.160 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
0.500 MPa

@Strain 0.150 %,
Temperature 150 °C
 72.5 psi

@Strain 0.150 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
1.34 MPa

@Strain 0.0700 %,
Temperature -40.0 °C
 194 psi

@Strain 0.0700 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
1.37 MPa

@Strain 0.0500 %,
Temperature -20.0 °C
 199 psi

@Strain 0.0500 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
1.39 MPa

@Strain 0.120 %,
Temperature 90.0 °C
 202 psi

@Strain 0.120 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
1.83 MPa

@Strain 0.0700 %,
Temperature -20.0 °C
 265 psi

@Strain 0.0700 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
1.83 MPa

@Strain 0.0600 %,
Temperature -40.0 °C
 265 psi

@Strain 0.0600 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
2.08 MPa

@Strain 0.0900 %,
Temperature 90.0 °C
 302 psi

@Strain 0.0900 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
2.22 MPa

@Strain 0.100 %,
Temperature 23.0 °C
 322 psi

@Strain 0.100 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
2.28 MPa

@Strain 0.100 %,
Temperature 40.0 °C
 331 psi

@Strain 0.100 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
2.41 MPa

@Strain 0.110 %,
Temperature 40.0 °C
 350 psi

@Strain 0.110 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
2.66 MPa

@Strain 0.120 %,
Temperature 0.000 °C
 386 psi

@Strain 0.120 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
2.68 MPa

@Strain 0.110 %,
Temperature 0.000 °C
 389 psi

@Strain 0.110 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
2.73 MPa

@Strain 0.110 %,
Temperature 23.0 °C
 396 psi

@Strain 0.110 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
4.42 MPa

@Strain 1.96 %,
Temperature 150 °C
 641 psi

@Strain 1.96 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
4.75 MPa

@Strain 1.95 %,
Temperature 150 °C
 689 psi

@Strain 1.95 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
5.55 MPa

@Strain 0.230 %,
Temperature -20.0 °C
 805 psi

@Strain 0.230 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
5.78 MPa

@Strain 0.250 %,
Temperature -40.0 °C
 838 psi

@Strain 0.250 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
6.49 MPa

@Strain 0.230 %,
Temperature -40.0 °C
 941 psi

@Strain 0.230 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
7.55 MPa

@Strain 4.24 %,
Temperature 150 °C
 1100 psi

@Strain 4.24 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
7.58 MPa

@Strain 4.35 %,
Temperature 150 °C
 1100 psi

@Strain 4.35 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
8.42 MPa

@Strain 0.310 %,
Temperature -20.0 °C
 1220 psi

@Strain 0.310 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
8.87 MPa

@Strain 6.72 %,
Temperature 150 °C
 1290 psi

@Strain 6.72 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
9.36 MPa

@Strain 6.86 %,
Temperature 150 °C
 1360 psi

@Strain 6.86 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
10.1 MPa

@Strain 14.98 %,
Temperature 150 °C
 1460 psi

@Strain 14.98 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
10.39 MPa

@Strain 20.0 %,
Temperature 150 °C
 1507 psi

@Strain 20.0 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
11.69 MPa

@Strain 15.03 %,
Temperature 150 °C
 1695 psi

@Strain 15.03 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
12.24 MPa

@Strain 20.01 %,
Temperature 150 °C
 1775 psi

@Strain 20.01 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
13.78 MPa

@Strain 1.43 %,
Temperature 90.0 °C
 1999 psi

@Strain 1.43 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
16.03 MPa

@Strain 0.870 %,
Temperature 90.0 °C
 2325 psi

@Strain 0.870 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
17.91 MPa

@Strain 20.01 %,
Temperature 90.0 °C
 2598 psi

@Strain 20.01 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
18.15 MPa

@Strain 14.9 %,
Temperature 90.0 °C
 2632 psi

@Strain 14.9 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
18.39 MPa

@Strain 0.790 %,
Temperature 40.0 °C
 2667 psi

@Strain 0.790 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
19.35 MPa

@Strain 0.950 %,
Temperature 40.0 °C
 2806 psi

@Strain 0.950 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
19.36 MPa

@Strain 6.09 %,
Temperature 90.0 °C
 2808 psi

@Strain 6.09 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
19.55 MPa

@Strain 3.53 %,
Temperature 90.0 °C
 2835 psi

@Strain 3.53 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
20.71 MPa

@Strain 0.860 %,
Temperature 23.0 °C
 3004 psi

@Strain 0.860 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
21.82 MPa

@Strain 1.00 %,
Temperature 23.0 °C
 3165 psi

@Strain 1.00 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
22.45 MPa

@Strain 0.940 %,
Temperature -20.0 °C
 3256 psi

@Strain 0.940 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
24.69 MPa

@Strain 1.00 %,
Temperature 0.000 °C
 3581 psi

@Strain 1.00 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
24.79 MPa

@Strain 0.870 %,
Temperature -40.0 °C
 3595 psi

@Strain 0.870 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
25.47 MPa

@Strain 1.02 %,
Temperature -40.0 °C
 3694 psi

@Strain 1.02 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
27.96 MPa

@Strain 1.24 %,
Temperature 0.000 °C
 4055 psi

@Strain 1.24 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
32.77 MPa

@Strain 1.28 %,
Temperature -20.0 °C
 4753 psi

@Strain 1.28 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
34.82 MPa

@Strain 2.10 %,
Temperature 90.0 °C
 5050 psi

@Strain 2.10 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
37.5 MPa

@Strain 20.0 %,
Temperature 90.0 °C
 5440 psi

@Strain 20.0 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
38.82 MPa

@Strain 13.99 %,
Temperature 90.0 °C
 5630 psi

@Strain 13.99 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
39.05 MPa

@Strain 1.77 %,
Temperature -20.0 °C
 5664 psi

@Strain 1.77 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
40.67 MPa

@Strain 2.14 %,
Temperature 40.0 °C
 5899 psi

@Strain 2.14 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
41.81 MPa

@Strain 1.81 %,
Temperature -40.0 °C
 6064 psi

@Strain 1.81 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
42.04 MPa

@Strain 2.00 %,
Temperature 40.0 °C
 6097 psi

@Strain 2.00 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
43.42 MPa

@Strain 1.63 %,
Temperature -40.0 °C
 6298 psi

@Strain 1.63 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
44.67 MPa

@Strain 2.24 %,
Temperature 23.0 °C
 6479 psi

@Strain 2.24 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
45.11 MPa

@Strain 3.74 %,
Temperature 90.0 °C
 6543 psi

@Strain 3.74 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
46.09 MPa

@Strain 20.01 %,
Temperature 40.0 °C
 6685 psi

@Strain 20.01 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
46.67 MPa

@Strain 2.14 %,
Temperature 23.0 °C
 6769 psi

@Strain 2.14 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
47.8 MPa

@Strain 13.94 %,
Temperature 40.0 °C
 6930 psi

@Strain 13.94 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
50.13 MPa

@Strain 2.13 %,
Temperature -20.0 °C
 7271 psi

@Strain 2.13 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
51.19 MPa

@Strain 2.28 %,
Temperature 0.000 °C
 7424 psi

@Strain 2.28 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2