ExxonMobil LLDPE LL 1001.32 Linear Low Density Polyethylene Resin
| Category | Polymer , Thermoplastic , Polyethylene (PE) , LLDPE |
| Manufacturer | Exxon Chemical |
| Trade Name | LLDPE |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil LLDPE LL 1001.32 Linear Low Density Polyethylene Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: LL 1001.32 is a butane LLDPE resin. Films made from LL 1001.32 have very good tensile and toughness properties.Availability: Latin America, North America and South America Additive: Antiblock: NoSlip: NoProcessing Aid: NoThermal Stabilizer: YesApplications: Cast FilmCast Stretch FilmIndustrial LinersLinersProduce BagsRefuse BagsTrash BagsInformation provided by ExxonMobil
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | ExxonMobil method |
| Melt Flow | 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 8.27 MPa | 1200 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 7.58 MPa | 1100 psi | ASTM D882 |
| Film Elongation at Break, MD | 350 % | 350 % | ASTM D882 |
| Film Elongation at Break, TD | 810 % | 810 % | ASTM D882 |
| Puncture Energy | 2.82 J | 2.08 ft-lb | ExxonMobil Method |
| Elmendorf Tear Strength MD | 20 g | 20 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 460 g | 460 g | ASTM D1922 |
| Dart Drop Test | 60.0 g | 0.132 lb | ASTM D1709A |
| Film Tensile Strength at Break, MD | 66.2 MPa | 9600 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 28.3 MPa | 4100 psi | ASTM D882 |
| 1% Secant Modulus, MD | 110 MPa | 16000 psi | ASTM D882 |
| 1% Secant Modulus, TD | 131 MPa | 19000 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | <= 250 °C | <= 482 °F | Peak Melting Point; ExxonMobil method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 1.7 % | 1.7 % | ASTM D1003 |
| Gloss | 90 % | 90 % | 45°; ASTM D2457 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Puncture Force | 9 lbf | ExxonMobil Method |
Users viewing this material also viewed the following:
- S&E Specialty Polymers TufPrene™ 2000-40 SEBS
- Hong Kun Group N-(3-Chloropropyl)morpholine Pharmaceutical Intermediate
- MBA Polymers PP 2126 Post-consumer recycled general purpose polypropylene impact copolymer
- Gouda Vuurvast FLUCON 160 K Dense Self Flowing Refractory Castable
- HP Alloys Alloy 718, 15% Cold Worked, Aged
- Stir SpA RH I P (PVC)
- Solvay TECHNYL® 2912GMH7-P PA66, 63% glass fiber, DRY
- ThyssenKrupp 51CrV4 Saw Steel, Hot-Rolled Strip
- BASF Palatinol® 11-9P-I High Molecular Weight Linear Phthalate
Copyright © lookpolymers.com All Rights Reserved