Guarniflon PTFE G415 Polytetrafluoroethylene 25% Soft Carbon
| Category | Polymer , Thermoplastic , Fluoropolymer , PTFE , Polytetrafluoroethylene (PTFE), Conductive Carbon Filled |
| Manufacturer | Guarniflon |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Guarniflon PTFE G415 Polytetrafluoroethylene 25% Soft Carbon.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PTFE G Standard Compound with carbon..Properties: Good thermal and electrical conductivity. Good resistance to deformation. Excellent resistance to load with low coefficient of friction and high wear strength. Enhanced chemical resistanceApplications: Bearings for high speed and when fast dissipation of electric charges is needed. Elastic bands for unlubricated compressors. Valve seats.Information provided by Guarniflon®
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.04 - 2.10 g/cc | 0.0737 - 0.0759 lb/in³ | extruded; ASTM D792 |
| 2.05 - 2.11 g/cc | 0.0741 - 0.0762 lb/in³ | molded; ASTM D792 | |
| Deformation | 2.5 - 4.0 % @Pressure 13.7 MPa, Time 86400 sec |
2.5 - 4.0 % @Pressure 1990 psi, Time 24.0 hour |
after 24hr relaxation; ASTM D621 |
| 4.5 - 6.5 % @Pressure 13.7 MPa, Time 86400 sec |
4.5 - 6.5 % @Pressure 1990 psi, Time 24.0 hour |
ASTM D621 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 60 - 65 | 60 - 65 | molded; ASTM D2240 |
| 60 - 65 | 60 - 65 | extruded; ASTM D2240 | |
| Tensile Strength | >= 14.0 MPa | >= 2030 psi | extruded; ASTM D4894, ASTM D4745 |
| 15.0 - 20.0 MPa | 2180 - 2900 psi | molded; ASTM D4894, ASTM D4745 | |
| Elongation at Break | >= 100 % | >= 100 % | extruded; ASTM D4745 |
| 150 - 200 % | 150 - 200 % | molded; ASTM D4894 | |
| Compressive Yield Strength | 7.00 - 9.00 MPa @Strain 1.00 % |
1020 - 1310 psi @Strain 1.00 % |
ASTM D695 |
| Coefficient of Friction, Dynamic | 0.13 | 0.13 | ASTM D1894 |
| K (wear) Factor | 20.0 - 30.0 x 10-8 mm³/N-M | 9.93 - 14.9 x 10-10 in³-min/ft-lb-hr | at PV 100; ASTM D3702 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 120 - 130 µm/m-°C | 66.7 - 72.2 µin/in-°F | ASTM D696 |
| Maximum Service Temperature, Air | 260 °C | 500 °F | |
| Minimum Service Temperature, Air | -200 °C | -328 °F |
Users viewing this material also viewed the following:
- Premix Premi-Glas® 1266 (Injection Compression Molded) Glass Reinforced TMC
- Polykemi AB SCANMID 6 B11^ FC Nylon 6
- SABIC Innovative Plastics Lexan® EXL1463T PC Copolymer (Asia Pacific)
- LG Chemical SEETEC ST508 Linear Low Density Polyethylene, Cast Film Grade
- Karina 651-48/1-B-IS-BZ Black PVC Compound
- Haynes Hastelloy® C-22® alloy, 20% cold worked sheet, aged 100 hours at 500°C
- Special Metals BRIGHTRAY® Alloy B Electrical Resistance Alloy
- Unipetrol PE HD LITEN® BB 75 HDPE
- ExxonMobil Exxsol™ DSP 75-95 Dearomatized Fluid
- Techmer ES HiFill FR® PA6/6 GF25 FR NAT005 25% Glass Filled
Copyright © lookpolymers.com All Rights Reserved