Hexcel® Redux® 330K Epoxy film adhesives for the bonding and finishing of composites

Category	Polymer , Adhesive , Film , Thermoset , Epoxy , Epoxy Adhesive
Manufacturer	Hexcel
Trade Name
Port	Ningbo port,China
Trade Terms	EXW, FOB, CFR, CIF
Payment Terms	L/C, T/T, PayPal
Download PDF	Hexcel® Redux® 330K Epoxy film adhesives for the bonding and finishing of composites.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Redux 330 is a 350°F curing tough film adhesive which is ideally suited to structural bonding, composite to composite bonding, surface finishing, electromagnetic shielding and lightning strike applications. It is available with knitted nylon, matt nylon and metal foils, in a choice of weights to suit the wide range of applications. Redux 330 has excellent structural bonding performance and exceeds the requirements of BMS-8-245.Areal Weights: 0.35, 0.05, 0.08 psf.Features: Ideal for composite to composite bonding (no metallic fiber); Suitable for co-cure with 350°F prepreg systems; Good structural performance and service temperature to 270°F; Low volatile content (solventless production process); Excellent environmental resistance; High toughness; Light tack and good drapability; Contains carrier for glueline thickness control and for improved adhesive handling.Applications: Structural Composite Bonding

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	4.55 MPa <br>@Temperature 71.1 °C	660 psi <br>@Temperature 160 °F	Flatwise Tensile (Composite: Glass-Phenolic Core), Conditioning: 10 day Prebond Humidity + 14 Days at 160°F/100%RH
	5.79 MPa <br>@Temperature -55.0 °C	840 psi <br>@Temperature -67.0 °F	Flatwise Tensile (Composite: Glass-Phenolic Core), No conditioning
	6.41 MPa <br>@Temperature 71.1 °C	930 psi <br>@Temperature 160 °F	Flatwise Tensile (Composite: Glass-Phenolic Core), No conditioning
	6.62 MPa <br>@Temperature 21.1 °C	960 psi <br>@Temperature 70.0 °F	Flatwise Tensile (Composite: Glass-Phenolic Core), No conditioning
Shear Strength	3.65 MPa <br>@Temperature -55.0 °C	530 psi <br>@Temperature -67.0 °F	Beam Shear, No conditioning
	3.65 MPa <br>@Temperature 21.1 °C	530 psi <br>@Temperature 70.0 °F	Beam Shear, No conditioning
	3.65 MPa <br>@Temperature 71.1 °C	530 psi <br>@Temperature 160 °F	Beam Shear, No conditioning
	5.86 MPa <br>@Temperature -55.0 °C	850 psi <br>@Temperature -67.0 °F	Double Lap Shear (Composite/Composite), 0.05 psf, No conditioning
	6.41 MPa <br>@Temperature 149 °C	930 psi <br>@Temperature 300 °F	Double Lap Shear (Composite/Composite), 0.05 psf, No conditioning
	6.62 MPa <br>@Temperature 21.1 °C	960 psi <br>@Temperature 70.0 °F	Double Lap Shear (Composite/Composite), 0.05 psf, No conditioning
	13.8 MPa <br>@Temperature 149 °C	2000 psi <br>@Temperature 300 °F	Single Lap Shear (Metal/Metal), 0.05 psf, No conditioning
	41.4 MPa <br>@Temperature 21.1 °C	6000 psi <br>@Temperature 70.0 °F	Single Lap Shear (Metal/Metal), 0.05 psf, No conditioning
Peel Strength	5.43 kN/m <br>@Temperature 21.1 °C	31.0 pli <br>@Temperature 70.0 °F	Bell Peel, No conditioning

Processing Properties	Metric	English	Comments
Shelf Life	6.00 Month <br>@Temperature -17.8 °C	6.00 Month <br>@Temperature 0.000 °F

Descriptive Properties	Value	Comments
Carrier/Foil	Knitted nylon