Imerys KT-Cast/Rogersâ„¢ Kaolin
| Category | Ceramic , Oxide , Aluminum Oxide , Silicon Oxide |
| Manufacturer | Imerys (Kentucky-Tennessee Clay Co.) |
| Trade Name | KT-Cast/Rogers™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Imerys KT-Cast/Rogersâ„¢ Kaolin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Imerys
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Particle Size | 0.50 µm | 0.50 µm | 30% finer than |
| 1.0 µm | 1.0 µm | 48% finer than | |
| 2.0 µm | 2.0 µm | 62% finer than | |
| 5.0 µm | 5.0 µm | 81% finer than | |
| 10 µm | 10 µm | 91% finer than | |
| 20 µm | 20 µm | 97% finer than | |
| pH | 5.5 | 5.5 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Rupture | 0.00276 GPa | 0.400 ksi |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | 38.1 % | 38.1 % | |
| CaO | 0.20 % | 0.20 % | |
| Carbon, C | 0.050 % | 0.050 % | |
| Fe2O3 | 0.50 % | 0.50 % | |
| K2O | 0.20 % | 0.20 % | |
| Loss on Ignition(%) | 13.6 % | 13.6 % | |
| MgO | 0.10 % | 0.10 % | |
| Na2O | 0.10 % | 0.10 % | |
| SiO2 | 45.1 % | 45.1 % | |
| Sulfur, S | 0.060 % | 0.060 % | |
| TiO2 | 1.6 % | 1.6 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| M.B.I. (meq/100g) | 4.5 |
Users viewing this material also viewed the following:
- Ineos Nova 602 Crystal Polystyrene GP Grade (discontinued **)
- PolyOne Geon™ Vinyl Flexible C5D01 Polyvinyl Chloride, Flexible (PVC, Flexible)
- LG Chemical LUMID GP1300A(W) PA6, High Viscosity
- Kolon NOPLA® KE531 PEN-PET Copolyester
- Cossa Polimeri ESTABLEND 4501 V0/D Flame Retardant PC - ABS
- Chosun Refractories HAPT-80S Plastic Refractory
- 3M Scotchcal™ ElectroCut™ 407 Graphic Film
- A. Schulman ComAlloy Hiloy® 464 Glass Fiber/Bead Reinforced, PET Alloy
- Pyrotek Pyrocast ALF3 Low Cement Refractory Castable
Copyright © lookpolymers.com All Rights Reserved