- Industeel SIRIUS 800 Heat Resistant Alloy
Industeel SIRIUS 800 Heat Resistant Alloy
| Category | Metal , Superalloy , Iron Base |
| Manufacturer | Groupe Arcelor |
| Trade Name | SIRIUS |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Industeel SIRIUS 800 Heat Resistant Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: The SIRIUS® 800, H and H+ grades are three variants of a high chromium and nickel austenitic alloy which combines good corrosion and creep resistance. SIRIUS® 800 is employed at temperature below 600°C(1112°F) while SIRIUS® 800H and SIRIUS® 800H+ are used above 600°C (1112°F). CLI heats obtained by vacuum degassing process have a tight control of the chemical analysis including residual elements in order to improve the weldability and in-service properties.Information provided by manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 8.00 g/cc | 0.289 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | >= 520 MPa | >= 75400 psi | Minimum Guaranteed |
| Tensile Strength, Yield | >= 210 MPa @Strain 0.200 % |
>= 30500 psi @Strain 0.200 % |
|
| Elongation at Break | >= 35 % | >= 35 % | |
| Modulus of Elasticity | 196 GPa | 28400 ksi | |
| Poissons Ratio | 0.342 | 0.342 | Calculated |
| Shear Modulus | 73.0 GPa @Temperature 20.0 °C |
10600 ksi @Temperature 68.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 13.5 µm/m-°C @Temperature 0.000 - 100 °C |
7.50 µin/in-°F @Temperature 32.0 - 212 °F |
|
| 14.5 µm/m-°C @Temperature 0.000 - 100 °C |
8.06 µin/in-°F @Temperature 32.0 - 212 °F |
||
| 15.5 µm/m-°C @Temperature 0.000 - 400 °C |
8.61 µin/in-°F @Temperature 32.0 - 752 °F |
||
| 17.0 µm/m-°C @Temperature 0.000 - 600 °C |
9.44 µin/in-°F @Temperature 32.0 - 1110 °F |
||
| Specific Heat Capacity | 0.502 J/g-°C @Temperature 20.0 °C |
0.120 BTU/lb-°F @Temperature 68.0 °F |
|
| Thermal Conductivity | 13.0 W/m-K @Temperature 20.0 °C |
90.2 BTU-in/hr-ft²-°F @Temperature 68.0 °F |
|
| Annealing Point | 980 °C | 1800 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Aluminum, Al | 0.15 - 0.60 % | 0.15 - 0.60 % | |
| Carbon, C | <= 0.10 % | <= 0.10 % | |
| Chromium, Cr | 19 - 23 % | 19 - 23 % | |
| Copper, Cu | <= 0.75 % | <= 0.75 % | |
| Iron, Fe | 38.925 - 50.7 % | 38.925 - 50.7 % | As remainder |
| Nickel, Ni | 30 - 35 % | 30 - 35 % | |
| Phosphorous, P | <= 0.020 % | <= 0.020 % | |
| Silicon, Si | <= 1.0 % | <= 1.0 % | |
| Sulfur, S | <= 0.0050 % | <= 0.0050 % | |
| Titanium, Ti | 0.15 - 0.60 % | 0.15 - 0.60 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.000100 ohm-cm @Temperature 20.0 °C |
0.000100 ohm-cm @Temperature 68.0 °F |
Users viewing this material also viewed the following:
- Polykemi AB POLYfill PPH GF2020 PD2 Polypropylene Homopolymer, Glass Fibre-Reinforced, Chemically Coupled
- Arkema Group Oroglas® DRT Acrylic, Impact Grade (discontinued **)
- LATI Latistat 87/28-06 PC
- Techmer ES Plastiblend® PBT/ABS GF/M40 FR 40/40% Glass/Mineral Filled
- A. Schulman POLYFORT™ FPP 3716 Talc Filled Copolymer Polypropylene
- 3M 520 Sandblast Stencil
- BASF Palusol® 100 Silicate Panel
- ATI Allegheny Ludlum Stainless Steel Chromium-Nickel Type 302, 20% Cold Rolled (UNS S30200)
Copyright © lookpolymers.com All Rights Reserved